Abstract: In order to supplement the brittle property of concrete,
fibers are added into concrete mixtures. Compared to general concrete,
various characteristics such as tensile strength, bending strength,
bending toughness, and resistance to crack are superior, and even
when cracks occur, improvements on toughness as well as resistance
to shock are excellent due to the growth of fracture energy. Increased
function of steel fiber reinforced concrete can be differentiated
depending on the fiber dispersion, and sand percentage can be an
important influence on the fiber dispersion. Therefore, in this research,
experiments were planned on sand percentage in order to apprehend
the influence of sand percentage on the bending properties and direct
tension of SFRC and basic experiments were conducted on bending
and direct tension in order to recognize the properties of bending
properties and direct tension following the size of the aggregates and
sand percentage.
Abstract: Despite of the preponderant role played by cement among the construction materials, it is today considered as a material destructing the environment due to the large quantities of carbon dioxide exhausted during its manufacture. Besides, global warming is now recognized worldwide as the new threat to the humankind against which advanced countries are investigating measures to reduce the current amount of exhausted gases to the half by 2050. Accordingly, efforts to reduce green gases are exerted in all industrial fields. Especially, the cement industry strives to reduce the consumption of cement through the development of alkali-activated geopolymer mortars using industrial byproducts like bottom ash. This study intends to gather basic data on the flowability and strength development characteristics of alkali-activated geopolymer mortar by examining its FT-IT features with respect to the effects and strength of the alkali-activator in order to develop bottom ash-based alkali-activated geopolymer mortar. The results show that the 35:65 mass ratio of sodium hydroxide to sodium silicate is appropriate and that a molarity of 9M for sodium hydroxide is advantageous. The ratio of the alkali-activators to bottom ash is seen to have poor effect on the strength. Moreover, the FT-IR analysis reveals that larger improvement of the strength shifts the peak from 1060 cm–1 (T-O, T=Si or Al) toward shorter wavenumber.