Abstract: We report the microstructural and magnetic properties
of Ni50Mn39Sn11 and Ni50Mn36Sn14 ribbon Heusler alloys.
Experimental results were obtained by differential scanning
calorymetry, X-ray diffraction and vibrating sample magnetometry
techniques. The Ni-Mn-Sn system undergoes a martensitic structural
transformation in a wide temperature range. For example, for
Ni50Mn39Sn11 the start and finish temperatures of the martensitic and
austenite phase transformation for ribbon alloy were Ms=336K,
Mf=328K, As=335K and Af=343K whereas no structural
transformation is observed for Ni50Mn36Sn14 alloys. Magnetic
measurements show the typical ferromagnetic behavior with Curie
temperature 207 K at low applied field of 50 Oe. The complex
behavior exhibited by these Heusler alloys should be ascribed to the
strong coupling between magnetism and structure, being their
magnetic behavior determined by the distance between Mn atoms.