Abstract: In recent years asymmetric cross section aluminum
alloy stock has been finding increasing use in various industrial manufacturing areas such as general structures and automotive
components. In these areas, components are generally required to have
complex curved configuration and, as such, a bending process is required during manufacture. Undesirable deformation in bending
processes such as flattening or wrinkling can easily occur when thin-walled sections are bent. Hence, a thorough understanding of the
bending behavior of such sections is needed to prevent these undesirable deformations. In this study, the bending behavior of
asymmetric channel section was examined using finite element analysis (FEA). Typical methods of preventing undesirable
deformation, such as asymmetric laminated elastic mandrels were included in FEA model of draw bending. Additionally, axial tension
was applied to prevent wrinkling. By utilizing the FE simulations effect of restriction dies and axial tension on undesirable deformation during the process was clarified.
Abstract: Aluminum alloy sheets have several advantages such
as the lightweight, high-specific strength and recycling efficiency.
Therefore, aluminum alloy sheets in sheet forming have been used in various areas as automotive components and so forth. During the
process of sheet forming, wrinkling which is caused by compression stress might occur and the formability of sheets was affected by
occurrence of wrinkling. A few studies of uniaxial compressive test by
using square tubes, pipes and sheets were carried out to clarify the each wrinkling behavior. However, on uniaxial compressive test,
deformation behavior of the sheets hasn-t be cleared. Then, it is necessary to clarify the relationship between the buckling behavior
and the forming conditions. In this study, the effect of dimension of the sheet in the buckling behavior on compression test of aluminum alloy sheet was cleared by experiment and FEA. As the results, the buckling
deformation was classified by three modes in terms of the distribution of equivalent plastic strain.