Abstract: Targeted drug delivery is a method of delivering
medication to a patient in a manner that increases the concentration
of the medication in some parts of the body relative to others.
Targeted drug delivery seeks to concentrate the medication in the
tissues of interest while reducing the relative concentration of the
medication in the remaining tissues. This improves efficacy of the
while reducing side effects. In the present work, we investigate the
effect of magnetic field, flow rate and particle concentration on the
capturing of magnetic particles transported in a stent implanted
fluidic channel. Iron oxide magnetic nanoparticles (Fe3O4)
nanoparticles were synthesized via co-precipitation method. The
synthesized Fe3O4 nanoparticles were added in the de-ionized (DI)
water to prepare the Fe3O4 magnetic particle suspended fluid. This
fluid is transported in a cylindrical tube of diameter 8 mm with help
of a peristaltic pump at different flow rate (25-40 ml/min). A
ferromagnetic coil of SS 430 has been implanted inside the
cylindrical tube to enhance the capturing of magnetic nanoparticles
under magnetic field. The capturing of magnetic nanoparticles was
observed at different magnetic magnetic field, flow rate and particle
concentration. It is observed that capture efficiency increases from
47-67% at magnetic field 2-5kG, respectively at particle
concentration 0.6mg/ml and at flow rate 30 ml/min. However, the
capture efficiency decreases from 65 to 44% by increasing the flow
rate from 25 to 40 ml/min, respectively. Furthermore, it is observed
that capture efficiency increases from 51 to 67% by increasing the
particle concentration from 0.3 to 0.6 mg/ml, respectively.
Abstract: In the present study, we have synthesized Cr and Fe
doped zinc oxide (ZnO) nanostructures (Zn1-δCraFebO; where δ = a +
b = 20%, a = 5, 6, 8 & 10% and b = 15, 14, 12 & 10%) via sol-gel
method at different doping concentrations. The synthesized samples
were characterized for structural properties by X-ray diffractrometer
and field emission scanning electron microscope and the optical
properties were carried out through photoluminescence and UVvisible
spectroscopy. The particle size calculated through field
emission scanning electron microscope varies from 41 to 96 nm for
the samples synthesized at different doping concentrations. The
optical band gaps calculated through UV-visible spectroscopy are
found to be decreasing from 3.27 to 3.02 eV as the doping
concentration of Cr increases and Fe decreases.
Abstract: In this work, we have synthesized BaTiO3 via sol gel method by sintering at different temperatures (600, 700, 800, 900, 10000C) and studied their structural, optical and ferroelectric properties through X-ray diffraction (XRD), UV-Vis spectrophotometer and PE Loop Tracer. X-ray diffraction patterns of barium titanate samples show that the peaks of the diffractogram are successfully indexed with the tetragonal and cubic structure of BaTiO3. The Optical band gap calculated through UV Visible spectrophotometer varies from 4.37 to 3.80 eV for the samples sintered at 600 to 10000C, respectively. The particle size calculated through transmission electron microscopy varies from 20 to 40 nm for the samples sintered at 600 to 10000C, respectively. Moreover, it has been observed that the ferroelectricity increases as we increase the sintering temperature.