Abstract: Biodiesel production from vegetable oil will produce
glycerol as by-product about 10% of the biodiesel production. The
amount of glycerol that was produced needed alternative way to
handling immediately so as to not become the waste that polluted
environment. One of the solutions was to process glycerol to
polyglycidyl nitrate (PGN). PGN is synthesized from glycerol by
three-step reactions i.e. nitration of glycerol, cyclization of 13-
dinitroglycerine and polymerization of glycosyl nitrate. Optimum
condition of nitration of glycerol with nitric acid has not been known.
Thermodynamic feasibility should be done before run experiments in
the laboratory. The aim of this study was to determine the parameters
those affect nitration of glycerol and nitric acid and chose the
operation condition. Many parameters were simulated to verify its
possibility to experiment under conditions which would get the
highest conversion of 1, 3-dinitroglycerine and which was the ideal
condition to get it. The parameters that need to be studied to obtain
the highest conversion of 1, 3-dinitroglycerine were mol ratio of
nitric acid/glycerol, reaction temperature, mol ratio of
glycerol/dichloromethane and pressure. The highest conversion was
obtained in the range of mol ratio of nitric acid /glycerol between 2/1
– 5/1, reaction temperature of 5-25oC and pressure of 1 atm. The
parameters that need to be studied further to obtain the highest
conversion of 1.3 DNG are mol ratio of nitric acid/glycerol and
reaction temperature.
Abstract: Coal fly ash (CFA) generated by coal-based thermal
power plants is mainly composed of some oxides having high
crystallinity, like quartz and mullite. In this study, the effect of CFA
crystallinity toward lead adsorption capacity was investigated. To get
solid with various crystallinity, the solution of sodium hydroxide
(NaOH) of 1-7 M was used to treat CFA at various temperature and
reflux time. Furthermore, to evaluate the effect of NaOH-treated CFA
with respect to adsorption capacity, the treated CFA were examine as
adsorbent for removing lead in the solution. The result shows that
using NaOH to treat CFA causes crystallinity of quartz and mullite
decrease. At higher NaOH concentration (>3M), in addition the
damage of quartz and mullite crystallinity is followed by crystal
formation called hydroxysodalite. The lower crystalllinity, the higher
adsorption capacity.
Abstract: Coal fly ash (CFA) generated by coal-based thermal
power plants is mainly composed of quartz, mullite, and unburned
carbon. In this study, the effect of unburned carbon on CFA toward
its adsorption capacity was investigated. CFA with various carbon
content was obtained by refluxing it with sulfuric acid having various
concentration at various temperature and reflux time, by heating at
400-800°C, and by sieving into 100-mesh in particle size. To
evaluate the effect of unburned carbon on CFA toward its adsorption
capacity, adsorption of methyl violet solution with treated CFA was
carried out. The research shows that unburned carbon leads to
adsorption capacity decrease. The highest adsorption capacity of
treated CFA was found 5.73 x 10-4mol.g-1.