Abstract: Metal cutting is a severe plastic deformation process
involving large strains, high strain rates, and high temperatures.
Conventional analysis of the chip formation process is based on bulk
material deformation disregarding the inhomogeneous nature of the
material microstructure. A series of orthogonal cutting tests of AISI
1045 and 1144 steel were conducted which yielded similar process
characteristics and chip formations. With similar shear angles and cut
chip thicknesses, shear strains for both chips were found to range
from 2.0 up to 2.8. The manganese-sulfide (MnS) precipitate in the
1144 steel has a very distinct and uniform shape which allows for
comparison before and after chip formation. From close observations
of MnS precipitates in the cut chips it is shown that the conventional
approach underestimates plastic strains in metal cutting.
Experimental findings revealed local shear strains around a value of
6. These findings and their implications are presented and discussed.