Abstract: Asymmetric incremental sheet forming (AISF) could significantly reduce costs incurred by the fabrication of complex industrial components with a minimal environmental impact. The AISF experiments were carried out on commercially pure titanium (Ti-Gr2), Timetal (15-3-3-3) alloy, and Ti-6Al-4V (Ti-Gr5) alloy. A special testing geometry was used to characterize the titanium alloys properties from the point of view of the forming zone and titanium structure effect. The structure and properties of the materials were assessed by means of metallographic analyses and microhardness measurements.The highest differences in the parameters assessed as a function of the sampling zone were observed in the case of alpha-phase Ti-Gr2at the expense of the most substantial sheet thinning occurrence. A springback causes a smaller stored deformation in Timetal (β alloy) resulting in less pronounced microstructure refinement and microhardness increase. Ti-6Al-4V alloy exhibited early failure due to its poor formability at ambient temperature.
Abstract: Shear spinning is closely related to the asymmetric incremental sheet forming (AISF) that could significantly reduce costs incurred by the fabrication of complex aeronautical components with a minimal environmental impact. The spinning experiments were carried out on commercially pure titanium (Ti-Gr2) and Ti-6Al-4V (Ti-Gr5) alloy. Three forming modes were used to characterize the titanium alloys properties from the point of view of different spinning parameters. The structure and properties of the materials were assessed by means of metallographic analyses and microhardness measurements. The highest value wall angle failure limit was achieved using spinning parameters mode for both materials. The feed rate effect was observed only in the samples from the Ti-Gr2 material, when a refinement of the grain microstructure with lower feed rate and higher tangential speed occurred. Ti-Gr5 alloy exhibited a decrease of the microhardness at higher straining due to recovery processes.
Abstract: Ti-6Al-4V alloy has demonstrated a high strength to
weight ratio as well as good properties at high temperature. The
successful application of the alloy in some important areas depends
on suitable joining techniques. Friction welding has many
advantageous features to be chosen for joining Titanium alloys. The
present work investigates the feasibility of producing similar metal
joints of this Titanium alloy by rotary friction welding method. The
joints are produced at three different speeds and the performances of
the welded joints are evaluated by conducting microstructure studies,
Vickers Hardness and tensile tests at the joints. It is found that the
weld joints produced are sound and the ductile fractures in the tensile
weld specimens occur at locations away from the welded joints. It is
also found that a rotational speed of 1500 RPM can produce a very
good weld, with other parameters kept constant.