Abstract: This paper presents the findings of an
experimental investigation to study the effect of alkali content
in geopolymer mortar specimens exposed to sulphuric acid.
Geopolymer mortar specimens were manufactured from Class F fly
ash by activation with a mixture of sodium hydroxide and sodium
silicate solution containing 5% to 8% Na2O. Durability of specimens
were assessed by immersing them in 10% sulphuric acid solution and
periodically monitoring surface deterioration and depth of
dealkalization, changes in weight and residual compressive strength
over a period of 24 weeks. Microstructural changes in the specimens
were studied with Scanning electron microscopy (SEM) and EDAX.
Alkali content in the activator solution significantly affects the
durability of fly ash based geopolymer mortars in sulphuric acid.
Specimens manufactured with higher alkali content performed better
than those manufactured with lower alkali content. After 24 weeks in
sulphuric acid, specimen with 8% alkali still recorded a residual
strength as high as 55%.
Abstract: The research investigates the effects of super plasticizer and molarity of sodium hydroxide alkaline solution on the workability, microstructure and compressive strength of self compacting geopolymer concrete (SCGC). SCGC is an improved way of concreting execution that does not require compaction and is made by complete elimination of ordinary Portland cement content. The parameters studied were superplasticizer (SP) dosage and molarity of NaOH solution. SCGC were synthesized from low calcium fly ash, activated by combinations of sodium hydroxide and sodium silicate solutions, and by incorporation of superplasticizer for self compactability. The workability properties such as filling ability, passing ability and resistance to segregation were assessed using slump flow, T-50, V-funnel, L-Box and J-ring test methods. It was found that the essential workability requirements for self compactability according to EFNARC were satisfied. Results showed that the workability and compressive strength improved with the increase in superplasticizer dosage. An increase in strength and a decrease in workability of these concrete samples were observed with the increase in molarity of NaOH solution from 8M to 14M. Improvement of interfacial transition zone (ITZ) and micro structure with the increase of SP and increase of concentration from 8M to 12M were also identified.
Abstract: The aim of this study is to compare the effect of the ultrasonic pre treatment on the removal of heavy metals (Iron, Zinc and Copper) from Acid Mine Drainage (AMD) by Denver Cell flotation. Synthetic AMD and individual metal solutions are used in the initial experiments to optimise the process conditions for real AMD. Three different process methods, ultrasound treatment followed by Denver flotation cell, Denver flotation cell alone and ultrasonic treatments run simultaneously with the Denver flotation cell were tested for every sample. Precipitation of the metal solutions by using sodium hydroxide (NaOH) and application of the optimum frother dosage followed by flotation significantly reduced the metal content of the AMD.
Abstract: The present paper reports results of an experimental
program conducted to study performance of fly ash based
geopolymer pastes at elevated temperature. Three series of
geopolymer pastes differing in Na2O content (8.5%, 10% and 11.5%)
were manufactured by activating low calcium fly ash with a mixture
of sodium hydroxide and sodium silicate solution. The paste
specimens were subjected to temperatures as high as 900oC and the
behaviour at elevated temperatures were investigated on the basis of
physical appearance, weight losses, residual strength, shrinkage
measurements and sorptivity tests at different temperatures. Scanning
electron microscopy along with EDX and XRD tests were also
conducted to examine microstructure and mineralogical changes
during the thermal exposure. Specimens which were initially grey
turned reddish accompanied by appearance of small cracks as the
temperature increased to 900oC. Loss of weight was more in
specimens manufactured with highest Na2O content. Geopolymer
paste specimen containing minimum Na2O performed better than
those with higher Na2O content in terms of residual compressive
strength.