Abstract: This study aimed to investigate the effect of aggressive environment on the flexural properties of halloysite nanotubes-polyester nanocomposites. Results showed that the addition of halloysite nanotubes into polyester matrix was found to improve flexural properties of the nanocomposites in dry condition and after water-methanol exposure. Significant increase in surface roughness was also observed and measured by Alicona Infinite Focus optical microscope.
Abstract: The effect of extraction solvent upon properties
of carrageenan from Eucheuma cottonii was studied. The
distilled water and KOH solution (concentration 0.1- 0.5N) were
used as the solvent. Extraction process was carried out in water
bath equipped by stirrer with constant speed of 275 rpm with a
constant ratio of seaweed weight to solvent volume ( 1:50 g/mL)
at 86oC for 45 minutes. The extract was then precipitated in 3
volume of 90% ethanol, oven dried at 60oC. Based on
experimental data, alkali significantly influenced yield and
properties of extracted carrageenan. The extracted carrageenan
was found to have essentially identical FTIR spectra to the
reference samples of kappa-carrageenan. Increasing the KOH
concentration led to carrageenan containing less sulfate content
and intrinsic viscosity. The gel strength increased along with the
increasing of KOH concentration. The decreasing of intrinsic
viscosity value indicates that a polymer degradation occurs
during alkali extraction.