Abstract: Electrospinning is a broadly used technology to obtain
polymeric nanofibers ranging from several micrometers down to
several hundred nanometers for a wide range of applications. It offers
unique capabilities to produce nanofibers with controllable porous
structure. With smaller pores and higher surface area than regular
fibers, electrospun fibers have been successfully applied in various
fields, such as, nanocatalysis, tissue engineering scaffolds, protective
clothing, filtration, biomedical, pharmaceutical, optical electronics,
healthcare, biotechnology, defense and security, and environmental
engineering. In this study, polyurethane nanofibers were obtained
under different electrospinning parameters. Fiber morphology and
diameter distribution were investigated in order to understand them
as a function of process parameters.
Abstract: The nanofiber sheet of Multiwall Cabon Nanotube
(MWCNTs)/Polyacylonitile (PAN) composites was fabricated from
electrospun nanofiber. Firstly the surface of MWCNTs was
chemically modified, comparing two different techniques consisting
of admicellar polymerization and functionalization to improve the
dispersion and prevent the aggregation in the PAN matrix. The
modified MWCNTs were characterized by the dispersion in
dimethylformamide (DMF) solvent, Laser particle size, and FTRaman.
Lastly, DSC, SEM and mechanical properties of the
nanofiber sheet were examined. The results show that the mechanical
properties of the nanofiber sheet prepared from admicellar
polymerization-modified MWCNTs were higher than those of the
others.
Abstract: In this study, single nozzle method used for
electrospinning technique which composite polymer solution with
cellulose nanowiskers (CNW) was treated by ultrasonic sonificator
have been compared with coaxial (double) nozzle method, in terms of
mechanical, thermal and morphological properties of composite
nanofiber. The effect of water content in composite polymer solution
on properties of nanofiber has also been examined. It has been seen
that single nozzle method which polymer solution does not contain
water has better results than that of coaxial method, in terms of
mechanical, thermal and morphological properties of nanofiber.
However, it is necessary to make an optimization study on setting
condition of ultrasonic treatment to get better dispersion of CNW in
composite nanofiber and to get better mechanical and thermal
properties
Abstract: Aligned and random nanofibrous scaffolds of PVA/PCL/nHA were fabricated by electrospinning method. The composite nanofibrous scaffolds were subjected to detailed analysis. Morphological investigations revealed that the prepared nanofibers have uniform morphology and the average fiber diameters of aligned and random scaffolds were 135.5 and 290 nm, respectively. The obtained scaffolds have a porous structure with porosity of 88 and 76% for random and aligned nanofibers, respectively. Furthermore, FTIR analysis demonstrated that there were strong intramolecular interactions between the molecules of PVA/PCL/nHA. On the other hand, mechanical characterizations show that aligning the nanofibers, could significantly improve the rigidity of the resultant biocomposite nanofibrous scaffolds.