Abstract: Emphasis on the advancement of new materials and technology has been there for the past few decades. The global development towards using cheap and durable materials from renewable resources contributes to sustainable development. An experimental investigation of mechanical behaviour of sisal fibre-reinforced concrete is reported for making a suitable building material in terms of reinforcement. Fibre reinforced Composite is one such material, which has reformed the concept of high strength. Sisal fibres are abundantly available in the hot areas. Sisal fibre has emerged as a reinforcing material for concretes, used in civil structures. In this work, properties such as hardness and tensile strength of sisal fibre reinforced cement composites with 6, 12, 18 and 24% by weight of sisal fibres were assessed. Sisal fibre reinforced cement composite slabs with long sisal fibres were manufactured using a cast hand lay up technique. Mechanical response was measured under tension. The high energy absorption capacity of the developed composite system was reflected in high toughness values under tension respectively.
Abstract: This paper in essence presents comparative
experimental data on the mechanical performance of steel and
synthetic fibre-reinforced concrete under compression, tensile split
and flexure. URW1050 steel fibre and HPP45 synthetic fibre, both
with the same concrete design mix, have been used to make cube
specimens for a compression test, cylinders for a tensile split test and
beam specimens for a flexural test. The experimental data
demonstrated steel fibre reinforced concrete to be stronger in flexure
at early stages, whilst both fibre reinforced concrete types displayed
comparatively the same performance in compression, tensile splitting
and 28-day flexural strength. In terms of post-crack controlHPP45
was preferable.
Abstract: Experimental study on the influence of fibre content
on crack behaviour and propagation in synthetic-fibre reinforced
beams has been reported in this paper. The tensile behaviour of
metallic fibre concrete is evaluated in terms of residual flexural
tensile strength values determined from the load-crack mouth
opening displacement curve or load-deflection curve obtained by
applying a centre-point load on a simply supported notched prism.
The results achieved demonstrate that an increase in fibre content has
an almost negligible effect on compressive and tensile splitting
properties, causes a marginal increment in flexural tensile strength
and increasesthe Re3 value.