Abstract: Poly(lactic acid) (PLA) is a biodegradable polymer
which has good mechanical properties, however, its brittleness limits
its usage especially in packaging materials. Therefore, in this work,
PLA based polyurethane films were prepared by synthesizing with
different types of isocyanates; methylene diisocyanate (MDI) and
hexamethylene diisocyanates (HDI). For this purpose, PLA based
polyurethane must have good strength and flexibility. Therefore,
polycaprolactone which has better flexibility were prepared with
PLA. An effective way to endow polylactic acid with toughness is
through chain-extension reaction of the polylactic acid pre-polymer
with polycaprolactone used as chain extender. Polyurethane prepared
from MDI showed brittle behaviour, while, polyurethane prepared
from HDI showed flexibility at same concentrations.
Abstract: Polyurethane foam is functionalized with Sulfonic acid groups to remove lead ions (Pb2+) from drinking water through a cation exchange process. The synthesis is based on addition polymerization of the -NCO groups of an isocyanate with the –OH groups of a polyol to form the urethane. Toluene-diisocyanateis reacted with Polypropylene glycol to form a linear pre-polymer, which is further polymerized using a chain extender, N, N-bis(2-hydorxyethyl)-2-aminoethane-sulfonic acid (BES). BES acts as a functional group site to exchange Pb2+ ions. A set of experiments was designed to study the effect of various processing parameters on the performance of the synthesized foam. The maximum Pb2+ ion exchange capacity of the foam was found to be 47ppb/g from a 100ppb Pb2+ solution over a period of 60 minutes. A multistage batch filtration process increased the lead removal to 50-54ppb/3g of foam over a period of 90 minutes.
Abstract: Polyurethane foams (PUF) has been prepared from
vegetable; soybean based polyols. They were characterized into
flexible and semi rigid polyurethane foam. This work is directed to
production of flexible polyurethane foams by a process involving the
reaction of mixture of 2,4- and 2,6-Toluene di Isocyanate isomers,
with portion of to blends of soy polyols with petroleum polyol in the
presence of other ingredients such as blowing agents, silicone
surfactants and accelerating agents. Additon of chain extender
improves the property then further decreases the properties on further
addition of the same. The objective of this work was to study the
effect of chain extender and role of phosphoric acid catalyst to the
final properties and correlate the morphology image with mechanical
properties of these foams.