Abstract: In this paper, the effect of bolt clamping force on the fatigue behavior of bolted single lap joints of aluminum alloy 2024- T3 have been studied using numerical finite element method. To do so, a three dimensional model according to the bolted single lap joint has been created and numerical analysis has been carried out using finite element based package. Then the stress distribution and also the slip amplitudes have been calculated in the critical regions and the outcome have been compared with the available experimental fatigue tests results. The numerical results show that in low applied clamping force, the fatigue failure of the specimens occur around the stress concentration location (the bolted hole edge) due to the tensile stresses and thus fatigue crack propagation, but with increase of the clamping force, the fatigue life increases and the cracks nucleate and propagate far from the hole edge because of fretting fatigue. In other words, with the further increase of clamping force value of the joint, the fatigue life reduces due to occurrence of the fretting fatigue in the critical location where the slip amplitude is within its critical occurs earlier.
Abstract: Friction stir welding is a solid state joining process. High strength aluminum alloys are widely used in aircraft and marine industries. Generally, the mechanical properties of fusion welded aluminum joints are poor. As friction stir welding occurs in solid state, no solidification structures are created thereby eliminating the brittle and eutectic phases common in fusion welding of high strength aluminum alloys. In this review the process parameters, microstructural evolution, and effect of friction stir welding on the properties of weld specific to aluminum alloys have been discussed.
Abstract: Recycling of aluminum alloys often decrease fluidity,
consequently influence the castability of the alloy. In this study, the
fluidity of Al-Zn alloys, such as the standard A713 alloy with and
without scrap addition has been investigated. The scrap added was
comprised of contaminated alloy turning chips. Fluidity
measurements were performed with double spiral fluidity test
consisting of gravity casting of double spirals in green sand moulds
with good reproducibility. The influence of recycled alloy on fluidity
has been compared with that of the virgin alloy and the results
showed that the fluidity decreased with the increase in recycled alloy
at minimum pouring temperatures. Interestingly, an appreciable
improvement in the fluidity was observed at maximum pouring
temperature, especially for coated spirals.
Abstract: Magnesium alloys have gained increased attention in recent years in automotive, electronics, and medical industry. This because of magnesium alloys have better properties than aluminum alloys and steels in respects of their low density and high strength to weight ratio. However, the main problems of magnesium alloy welding are the crack formation and the appearance of porosity during the solidification. This paper proposes a unique technique to weld two thin sheets of AZ31B magnesium alloy using a paste containing Ag nanoparticles. The paste containing Ag nanoparticles of 5 nm in average diameter and an organic solvent was used to coat the surface of AZ31B thin sheet. The coated sheet was heated at 100 °C for 60 s to evaporate the solvent. The dried sheet was set as a lower AZ31B sheet on the jig, and then lap fillet welding was carried out by using a pulsed Nd:YAG laser in a closed box filled with argon gas. The characteristics of the microstructure and the corrosion behavior of the joints were analyzed by opticalmicroscopy (OM), energy dispersive spectrometry (EDS), electron probe micro-analyzer (EPMA), scanning electron microscopy (SEM), and immersion corrosion test. The experimental results show that the wrought AZ31B magnesium alloy can be joined successfully using Ag nanoparticles. Ag nanoparticles insert promote grain refinement, narrower the HAZ width and wider bond width compared to weld without and insert. Corrosion rate of welded AZ31B with Ag nanoparticles reduced up to 44 % compared to base metal. The improvement of corrosion resistance of welded AZ31B with Ag nanoparticles due to finer grains and large grain boundaries area which consist of high Al content. β-phase Mg17Al12 could serve as effective barrier and suppressed further propagation of corrosion. Furthermore, Ag distribution in fusion zone provide much more finer grains and may stabilize the magnesium solid solution making it less soluble or less anodic in aqueous
Abstract: A lot of research made during these last 15 years
showed that the quantification of the springback has a significant role
in the industry of sheet metal forming. These studies were made with
the objective of finding techniques and methods to minimize or
completely avoid this permanent physical variation. Moreover, the
use of steel and aluminum alloys in the car industry and aviation
poses every day the problem of the springback. The determination in
advance of the quantity of the springback allows consequently the
design and manufacture of the tool. The aim of this paper is to study
experimentally the influence of the blank holder force BHF and the
radius of curvature of the die on the springback and their influence on
the strain in various zone of specimen.
The original of our purpose consist on tests which are ensured by
adapting a U-type stretching-bending device on a tensile testing
machine, where we studied and quantified the variation of the
springback according to displacement.