Abstract: This research focuses on the use of the Taguchi method to reduce the surface roughness and improve dimensional accuracy of parts machined by Wire Electrical Discharge Machining (EDM) with S7 heat treated steel material. Due to its high impact toughness, the material is a candidate for a wide variety of tooling applications which require high precision in dimension and desired surface roughness. This paper demonstrates that Taguchi Parameter Design methodology is able to optimize both dimensioning and surface roughness successfully by investigating seven wire-EDM controllable parameters: pulse on time (ON), pulse off time (OFF), servo voltage (SV), voltage (V), servo feed (SF), wire tension (WT), and wire speed (WS). The temperature of the water in the Wire EDM process is investigated as the noise factor in this research. Experimental design and analysis based on L18 Taguchi orthogonal arrays are conducted. This paper demonstrates that the Taguchi-based system enables the wire EDM process to produce (1) high precision parts with an average of 0.6601 inches dimension, while the desired dimension is 0.6600 inches; and (2) surface roughness of 1.7322 microns which is significantly improved from 2.8160 microns.
Abstract: Wire Electric Discharge Machining (WEDM) is
thermal machining process capable of machining very hard
electrically conductive material irrespective of their hardness.
WEDM is being widely used to machine micro scale parts with the
high dimensional accuracy and surface finish. The objective of this
paper is to optimize the process parameters of wire EDM to fabricate
the micro channels and to calculate the surface finish and material
removal rate of micro channels fabricated using wire EDM. The
material used is aluminum 6061 alloy. The experiments were
performed using CNC wire cut electric discharge machine. The effect
of various parameters of WEDM like pulse on time (TON) with the
levels (100, 150, 200), pulse off time (TOFF) with the levels (25, 35,
45) and current (IP) with the levels (105, 110, 115) were investigated
to study the effect on output parameter i.e. Surface Roughness and
Material Removal Rate (MRR). Each experiment was conducted
under different conditions of pulse on time, pulse off time and peak
current. For material removal rate, TON and Ip
were the most significant process parameter. MRR increases with the increase in
TON and Ip and decreases with the increase in TOFF. For surface
roughness, TON and Ip have the maximum effect and TOFF was found
out to be less effective.