Abstract: Sulfur dioxide (SO2) is a very toxic air pollutant gas and it causes the greenhouse effect, photochemical smog, and acid rain, which threaten human health severely. Thus, the capture of SO2 gas is very important for the environment. Graphene which is two-dimensional material has excellent mechanical, chemical, thermal properties, and many application areas such as energy storage devices, gas adsorption, sensing devices, and optical electronics. Further, graphene oxide (GO) is examined as a good adsorbent because of its important features such as functional groups (epoxy, carboxyl and hydroxyl) on the surface and layered structure. The SO2 adsorption properties of the fibers are usually investigated on carbon fibers. In this study, potential adsorption capacity of GO fibers was researched. GO dispersion was first obtained with Hummers’ method from graphite, and then GO fibers were obtained via wet spinning process. These fibers were converted into a disc shape, dried, and then subjected to SO2 gas adsorption test. The SO2 gas adsorption capacity of GO fiber discs was investigated in the fields of utilization of different coagulation baths and reduction by hydrazine hydrate. As coagulation baths, single and triple baths were used. In single bath, only ethanol and CaCl2 (calcium chloride) salt were added. In triple bath, each bath has a different concentration of water/ethanol and CaCl2 salt, and the disc obtained from triple bath has been called as reference disk. The fibers which were produced with single bath were flexible and rough, and the analyses show that they had higher SO2 adsorption capacity than triple bath fibers (reference disk). However, the reduction process did not increase the adsorption capacity, because the SEM images showed that the layers and uniform structure in the fiber form were damaged, and reduction decreased the functional groups which SO2 will be attached. Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD) analyzes were performed on the fibers and discs, and the effects on the results were interpreted. In the future applications of the study, it is aimed that subjects such as pH and additives will be examined.
Abstract: This paper investigates the application of metallic
coatings on high fiber volume fraction carbon/epoxy polymer matrix
composites. For the grip of the metallic layer, a method of modifying
the surface of the composite by introducing a mixture of copper and
steel powder (filler powders) which can reduce the impact of thermal
spray particles. The powder was introduced to the surface at the time
of the forming. Arc spray was used to project the zinc coating layer.
The substrate was grit blasted to avoid poor adherence. The porosity, microstructure, and morphology of layers are
characterized by optical microscopy, SEM and image analysis. The
samples were studied also in terms of hardness and erosion resistance.
This investigation did not reveal any visible evidence damage to the
substrates. The hardness of zinc layer was about 25.94 MPa and the
porosity was around (∼6.70%). The erosion test showed that the zinc
coating improves the resistance to erosion. Based on the results
obtained, we can conclude that thermal spraying allows the production
of protective coating on PMC. Zinc coating has been identified as a
compatible material with the substrate. The filler powders layer
protects the substrate from the impact of hot particles and allows
avoiding the rupture of brittle carbon fibers.
Abstract: Novel wind-lens turbine designs can augment power
output. Vacuum-Assisted Resin Transfer Molding (VARTM) is used
to form large and complex structures from a Carbon Fiber Reinforced
Polymer (CFRP) composite. Typically, wind-lens turbine structures
are fabricated in segments, and then bonded to form the final structure.
This paper introduces five new adhesive joints, divided into two
groups: one is constructed between dry carbon and CFRP fabrics, and
the other is constructed with two dry carbon fibers. All joints and
CFRP fabrics were made in our laboratory using VARTM
manufacturing techniques. Specimens were prepared for tensile testing
to measure joint performance. The results showed that the second
group of joints achieved a higher tensile strength than the first group.
On the other hand, the tensile fracture behavior of the two groups
showed the same pattern of crack originating near the joint ends
followed by crack propagation until fracture.
Abstract: We constructed an atomic structure model for a PAN-based carbon fiber containing amorphous structures using molecular dynamics methods. It was found that basic physical properties such as crystallinity, Young’s modulus, and thermal conductivity of our model were nearly identical to those of real carbon fibers. We then obtained the tensile strength of a carbon fiber, which has no macro defects. We finally determined that the limitation of the tensile strength was 19 GPa.
Abstract: Carbon fibers are fabricated from different materials,
such as special polyacrylonitrile (PAN) fibers, rayon fibers and pitch.
Among these three groups of materials, PAN fibers are the most
widely used precursor for the manufacture of carbon fibers. The
process of fabrication carbon fibers from special PAN fibers includes
two steps; oxidative stabilization at low temperature and
carbonization at high temperatures in an inert atmosphere. Due to the
high price of raw materials (special PAN fibers), carbon fibers are
still expensive.
In the present work the main goal is making carbon fibers from
low price commercial PAN fibers with modified chemical
compositions. The results show that in case of conducting completes
stabilization process, it is possible to produce carbon fibers with
desirable tensile strength from this type of PAN fibers. To this
matter, thermal characteristics of commercial PAN fibers were
investigated and based upon the obtained results, with some changes
in conventional procedure of stabilization in terms of temperature
and time variables; the desirable conditions of complete stabilization
is achieved.