Abstract: Three alumina-supported Pt-Sn catalysts have been
prepared by means of co-impregnation and characterized by XRD and
N2 adsorption. The influence of catalyst composition and reaction
conditions on the conversion and selectivity were investigated in the
hydrogenation of acetic acid in an isothermal integral fixed bed
reactor. The experiments were performed on the temperature interval
468-548 K, liquid hourly space velocity (LHSV) of 0.3-0.7h-1,
pressures between 1.0 and 5.0Mpa. A good compromise of
0.75%Pt-1.5%Sn can act as an optimized acetic acid hydrogenation
catalyst, and the conversion and selectivity can be tuned through the
variation of reaction conditions.
Abstract: To reduce the carbon dioxide emission into the
atmosphere, adsorption is believed to be one of the most attractive
methods for post-combustion treatment of flue gas. In this work,
activated carbon (AC) was modified by polyethylenimine (PEI) via
impregnation in order to enhance CO2 adsorption capacity. The
adsorbents were produced at 0.04, 0.16, 0.22, 0.25, and 0.28 wt%
PEI/AC. The adsorption was carried out at a temperature range from
30 °C to 75 °C and five different gas pressures up to 1 atm. TG-DTA,
FT-IR, UV-visible spectrometer, and BET were used to characterize
the adsorbents. Effects of PEI loading on the AC for the CO2
adsorption were investigated. Effectiveness of the adsorbents on the
CO2 adsorption including CO2 adsorption capacity and adsorption
temperature was also investigated. Adsorption capacities of CO2 were
enhanced with the increase in the amount of PEI from 0.04 to 0.22
wt% PEI before the capacities decreased onwards from0.25 wt% PEI
at 30 °C. The 0.22 wt% PEI/AC showed higher adsorption capacity
than the AC for adsorption at 50 °C to 75 °C.
Abstract: Characteristics and sonocatalytic activity of zeolite
Y catalysts loaded with TiO2 using impregnation and ion exchange
methods for the degradation of amaranth dye were investigated.
The Ion-exchange method was used to encapsulate the TiO2 into
the internal pores of the zeolite while the incorporation of TiO2
mostly on the external surface of zeolite was carried out using the
impregnation method. Different characterization techniques were
used to elucidate the physicochemical properties of the produced
catalysts. The framework of zeolite Y remained virtually
unchanged after the encapsulation of TiO2 while the crystallinity of
zeolite decreased significantly after the incorporation of 15 wt% of
TiO2. The sonocatalytic activity was enhanced by TiO2
incorporation with maximum degradation efficiencies of 50% and
68% for the encapsulated titanium and titanium loaded onto the
zeolite, respectively after 120min of reaction. Catalysts
characteristics and sonocatalytic behaviors were significantly
affected by the preparation method and the location of TiO2
introduced with zeolite structure. Behaviors in the sonocatalytic
process were successfully correlated with the characteristics of the
catalysts used.