Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: Atmospheric carbon dioxide emissions are considered
as the greatest environmental challenge the world is facing today.
The tasks to control the emissions include the recovery of CO2 from
flue gas. This concern has been improved due to recent advances in
materials process engineering resulting in the development of
inorganic gas separation membranes with excellent thermal and
mechanical stability required for most gas separations. This paper,
therefore, evaluates the performance of a highly selective inorganic
membrane for CO2 recovery applications. Analysis of results
obtained is in agreement with experimental literature data. Further
results show the prediction performance of the membranes for gas
separation and the future direction of research. The materials
selection and the membrane preparation techniques are discussed.
Method of improving the interface defects in the membrane and its
effect on the separation performance has also been reviewed and in
addition advances to totally exploit the potential usage of this
innovative membrane.
Abstract: Chitosan functionalized Fe3O4-Au core shell
nanoparticles have been prepared using a two-step wet chemical
approach using NaBH4 as reducing agent for formation of Au in
ethylene glycol. X-ray diffraction studies shows individual phases of
Fe3O4 and Au in the as prepared samples with crystallite size of 5.9
and 11.4 nm respectively. The functionalization of the core-shell
nanostructure with Chitosan has been confirmed using Fourier
transform infrared spectroscopy along with signatures of octahedral
and tetrahedral sites of Fe3O4 below 600cm-1. Mössbauer
spectroscopy shows decrease in particle-particle interaction in
presence of Au shell (72% sextet) than pure oleic coated Fe3O4
nanoparticles (88% sextet) at room temperature. At 80K, oleic acid
coated Fe3O4 shows only sextets whereas the Chitosan functionalized
Fe3O4 and Chitosan functionalized Fe3O4@Au core shell show
presence of 5 and 11% doublet, respectively.