Abstract: In this study, epoxy composite specimens reinforced
with multi-walled carbon nanotube filler were fabricated using shear
mixer and ultra-sonication processor. The mechanical and thermal
properties of the fabricated specimens were measured and evaluated.
From the electron microscope images and the results from the
measurements of tensile strengths, the specimens having 0.6 wt%
nanotube content show better dispersion and higher strength than those
of the other specimens. The Young’s moduli of the specimens
increased as the contents of the nanotube filler in the matrix were
increased. The specimen having a 0.6 wt% nanotube filler content
showed higher thermal conductivity than that of the other specimens.
While, in the measurement of thermal expansion, specimens having
0.4 and 0.6 wt% filler contents showed a lower value of thermal
expansion than that of the other specimens. On the basis of the
measured and evaluated properties of the composites, we believe that
the simple and time-saving fabrication process used in this study was
sufficient to obtain improved properties of the specimens.
Abstract: PVC foam-fly ash composites (PVC-FA) are
characterized for their structural, morphological, mechanical and
thermal properties. The tensile strength of the composites increased
modestly with higher fly ash loading, while there was a significant
increase in the elastic modulus for the same composites. On the other
hand, a decrease in elongation at UTS was observed upon increasing
fly ash content due to increased rigidity of the composites. Similarly,
the flexural modulus increased as the fly ash loading increased,
where the composites containing 25 phr fly ash showed the highest
flexural strength. Thermal properties of PVC-fly ash composites were
determined by Thermo Gravimetric Analysis (TGA). The
microstructural properties were studied by Scanning Electron
Microscopy (SEM). SEM results confirm that fly ash particles were
mechanically interlocked in PVC matrix with good interfacial
interaction with the matrix. Particle agglomeration and debonding
was observed in samples containing higher amounts of fly ash.
Abstract: Two types of glass fibers having different lengths
(1/16" and 1/32") were added into rigid PVC foams to enhance the
dimensional stability of extruded rigid Polyvinyl Chloride (PVC)
foam at different concentrations (0-20 phr) using a single screw
profile extruder. PVC foam-glass fiber composites (PVC-GF) were
characterized for their dimensional stability, structural, thermal, and
mechanical properties. Experimental results show that the
dimensional stability, heat resistance, and storage modulus were
enhanced without compromising the tensile and flexural strengths of
the composites. Overall, foam composites which were prepared with
longer glass fibers exhibit better mechanical and thermal properties
than those prepared with shorter glass fibers due to higher
interlocking between the fibers and the foam cells, which result in
better load distribution in the matrix.
Abstract: In this study, microcrystalline cellulose (MCC) was
extracted from oil palm empty fruit bunch (EFB) cellulose which was
earlier isolated from oil palm EFB fibre. In order to isolate the
cellulose, the chlorination method was carried out. Then, the MCC
was prepared by simultaneous ultrasonic and alkali treatment from
the isolated α-cellulose. Based on mass balance calculation, the yields
for MCC obtained from EFB was 44%. For fiber characterization, it
is observed that the chemical composition of the hemicellulose and
lignin for all samples decreased while composition for cellulose
increased. The structural property of the MCC was studied by X-ray
diffraction (XRD) method and the result shows that the MCC
produced is a cellulose-I polymorph, with 73% crystallinity.
Abstract: The present study was conducted to evaluate the
potential applicability of biological trickling filter system for the
treatment of simulated textile wastewater containing reactive azo
dyes with bacterial consortium under non-sterile conditions. The
percentage decolorization for the treatment of wastewater containing
structurally different dyes was found to be higher than 95% in all
trials. The stable bacterial count of the biofilm on stone media of the
trickling filter during the treatment confirmed the presence,
proliferation, dominance and involvement of the added microbial
consortium in the treatment of textile wastewater. Results of
physicochemical parameters revealed the reduction in chemical
oxygen demand (58.5-75.1%), sulphates (18.9-36.5%), and
phosphates (63.6-73.0%). UV-Visible and FTIR spectroscopy
confirmed decolorization of dye containing wastewater was ultimate
consequence of biodegradation. Toxicological studies revealed the
nontoxic nature of degradative metabolites.