Volume:8, Issue: 8, 2014 Page No: 785 - 787
ISSN: 2415-6620
Polymer composite nano-fibers including (1, 3 wt %)
silver nano-particles have been produced by electrospinning method.
Polyacrylonitrile/N,N-dimethylformamide (PAN/DMF) solution have
been prepared and the amount of silver nitrate have been adjusted to
PAN weight. Silver nano-particles were obtained from reduction of
silver ions into silver nano-particles by chemical reduction by
hydrazine hydroxide (N2H5OH). The different amount of silver salt
was loaded into polymer matrix to obtain polyacrylonitrile composite
nano-fiber containing silver nano-particles. The effect of the amount
of silver nano-particles on the properties of composite nano-fiber web
was investigated. Electrical conductivity, mechanical properties,
thermal properties were examined by Microtest LCR Meter 6370
(0.01 mΩ-100 MΩ), Tensile tester, Differential scanning calorimeter
DSC (Q10) and SEM respectively. Also antimicrobial efficiency test
(ASTM E2149-10) was done against to Staphylococcus aureus
bacteria. It has been seen that breaking strength, conductivity,
antimicrobial effect, enthalpy during cyclization increase by use of
silver nano-particles while the diameter of nano-fiber decreases.