The Preparation of Silicon and Aluminum Extracts from Tuncbilek and Orhaneli Fly Ashes by Alkali Fusion

Coal fly ash is formed as a solid waste product from the combustion of coal in coal fired power stations. Huge amounts of fly ash are produced globally every year and are predicted to increase. Nowadays, less than half of the fly ash is used as a raw material for cement manufacturing, construction and the rest of it is disposed as a waste causing yet another environmental concern. For this reason, the recycling of this kind of slurries into useful materials is quite important in terms of economical and environmental aspects. The purpose of this study is to evaluate the Orhaneli and Tuncbilek coal fly ashes for utilization in some industrial applications. Therefore the mineralogical and chemical compositions of these fly ashes were analyzed by X-ray fluorescence spectroscopy, ourier-transform infrared spectrometer, and X-ray diffraction. The silicon (Si) and aluminum (Al) in the fly ashes were activated by alkali fusion technique with sodium hydroxide. The obtained extracts were analyzed for Si and Al content by inductively coupled plasma optical emission spectrometry.

Authors:

• M. Sari Yilmaz
• N. Karamahmut Mermer

Keywords:

• Extraction
• Fly ash
• Fusion
• XRD.

References:

[1] OECD, “Electricity generation”, OECD Factbook 2011-2012:
Economic, Environmental and Social Statistics, OECD Publishing,
2011, pp. 132-133.
[2] V. M. Malhotra, “Making concrete, “Greener” with fly ash,” ACI
Concrete International, vol. 21, no. 5, pp. 61–66, 1999.
[3] G. Gorhan, E. Kahraman, M. S. Baspınar and I. Demir, “Uçucu kül
bölüm I: olusumu, sınıflandırılması ve kullanımı”, Yapı Teknolojileri
Elektronik Dergisi, vol. 2, pp. 85 -94, 2008 (In Turkish).
[4] J. G. S. Van Jaarsveld, J.S.J. Van Deventer, G.C. Lukey, “The
characterisation of source materials in fly ash-based geopolymers”,
Mater. Lett., vol.57, pp. 1272–1280, 2003.
[5] I. Majchrzak-Kucęba, W. Nowak, “Thermal analysis of fly ash-based
zeolites. J. Therm. Anal. Calorim. vol.77, pp. 125–131, 2004.
[6] N. F. Gao, S. Kume, K. Watari,. “Zeolite–carbon composites prepared
from industrial wastes: (I) effects of processing parameters”, Mater. Sci.
Eng., A, vol.399, pp. 216–221, 2005.
[7] M. Halina, S. Ramesh, M. A. Yarmo, R. A. Kamarudin, “Nonhydrothermal
synthesis of mesoporous materials using sodium silicate
from coal fly ash,” Mater. Chem. Phys., vol. 101, no. 2-3, pp. 344–351,
2007.
[8] C. Belviso, F. Cavalcante, S. Fiore, “Synthesis of zeolite from Italian
coal fly ash: differences in crystallization temperature using seawater
instead of distilled water”, Waste Manag. vol.30, pp. 839–847, 2010.
[9] G. Chandrasekar, K. S. You, J. W. Ahn, W. S. Ahn, “Synthesis of
hexagonal and cubic mesoporous silica using power plant bottom ash,”
Micropor. Mesopor. Mater., vol. 111, no. 1–3, pp. 455–462, 2008.
[10] Fei Shi, Jing-Xiao Liu, Kai Song, Zhen-Yu Wang, “Cost-effective
synthesis of silica aerogels from fly ash via ambient pressure drying”, J
Non-Cryst. Solids, vol.356, pp. 2241–2246, 2010.
[11] I. Majchrzak-Kucęba, W. Nowak, “Characterization of MCM-41
mesoporous materials derived from polish fly ashes”, Int. J. Miner.
Process., vol.101, pp. 100–111, 2011.
[12] X. Querol, N. Moreno, J.C. Umana, A. Alastuey, E. Hernandez, A.
Lopez-Soler, F. Plana, “Synthesis of zeolites from coal fly ash: an
overview”, Int. J. Coal Geol., vol. 50, no. 1, pp. 413-423, 2002.
[13] N. Shigemoto, H. Hayashi and K. Miyaura “Selective formation of Na-X
zeolite from coal fly ash by fusion with sodium hydroxide prior to
hydrothermal reaction”, J. Mater. Sci., vol.28, no. 17, pp. 4781-4786,
1993.
[14] O. Celik, E. Damcı, S. Piskin, “Characterization of fly ash and it effects
on the compressive strength properties of Portland cement”, Indian J.
Eng. Mater. Sci., vol.15, no. 5, pp. 433-440, 2008.