Combination of Tensile Strength and Elongation of Reverse Rolled TaNbHfZrTi Refractory High Entropy Alloy

The refractory high entropy alloys are potential materials for high-temperature applications because of their ability to retain high strength up to 1600°C. However, their practical applications were limited due to poor elongation at room temperature. Therefore, decreasing the average valence electron concentrations (VEC) is an effective design strategy to improve the intrinsic ductility of refractory high entropy alloys. In this work, the high-entropy alloy TaNbHfZrTi was processed at room temperature by each step reverse rolling up to a 90% reduction in thickness. Subsequently, the reverse rolled 90% samples were utilized for annealing treatment at 800°C and 1000°C for 1 h to understand phase stability, microstructure, texture, and mechanical properties. The reverse rolled 90% condition contains body-centered cubic (BCC) single-phase; upon annealing at 800 °C, the formation of secondary phase BCC-2 prevailed. The partial recrystallization and complete recrystallization microstructures were developed for annealed at 800°C and 1000°C, respectively. The reverse rolled condition and 1000°C annealed temperature exhibit extraordinary room temperature tensile properties with high ultimate tensile strength (UTS) without compromising loss of ductility called “strength-ductility” trade-off. The reverse-rolled 90% and annealing treatment carried out at temperature about 1000°C for 1 h consist of UTS 1430 MPa and 1556 MPa with an appreciable amount of 21% and 20% elongation, respectively. The development of hierarchical microstructure prevailed for the annealed 1000°C which led to the simultaneous increase in tensile strength and elongation.

• M. Veerasham

• refractory high entropy alloys
• reverse rolling
• recrystallization
• microstructure
• tensile properties

[1] Miracle, D. B., & Senkov, O. N. (2017). A critical review of high entropy alloys and related concepts. Acta Materialia, 122, 448-511.
[2] Murty, B. S., Yeh, J. W., Ranganathan, S., & Bhattacharjee, P. P. (2019). High-entropy alloys. Elsevier.
[3] Veeresham, M. Development of Impressive Tensile Properties of Hybrid Rolled Ta0.5Nb0.5Hf0.5ZrTi1.5 Refractory High Entropy Alloy. International Journal of Mechanical and Materials Engineering 15.6 (2021): 267-271.
[4] Tsai, K. Y., Tsai, M. H., & Yeh, J. W. (2013). Sluggish diffusion in Co–Cr–Fe–Mn–Ni high-entropy alloys. Acta Materialia, 61(13), 4887-4897.
[5] Senkov, O. N., Wilks, G. B., Miracle, D. B., Chuang, C. P., & Liaw, P. K. (2010). Refractory high-entropy alloys. Intermetallics, 18(9), 1758-1765.
[6] Senkov, O. N., Wilks, G. B., Scott, J. M., & Miracle, D. B. (2011). Mechanical properties of Nb25Mo25Ta25W25 and V20Nb20Mo20Ta20W20 refractory high entropy alloys. Intermetallics, 19(5), 698-706.
[7] Senkov, O. N., Miracle, D. B., Chaput, K. J., & Couzinie, J. P. (2018). Development and exploration of refractory high entropy alloys—A review. Journal of materials research, 33(19), 3092-3128.
[8] Senkov, O. N., Senkova, S. V., & Woodward, C. (2014). Effect of aluminum on the microstructure and properties of two refractory high-entropy alloys. Acta Materialia, 68, 214-228.
[9] Juan, C. C., Tsai, M. H., Tsai, C. W., Lin, C. M., Wang, W. R., Yang, C. C., ... & Yeh, J. W. (2015). Enhanced mechanical properties of HfMoTaTiZr and HfMoNbTaTiZr refractory high-entropy alloys. Intermetallics, 62, 76-83.
[10] Sheikh, S., Shafeie, S., Hu, Q., Ahlström, J., Persson, C., Veselý, J., ... & Guo, S. (2016). Alloy design for intrinsically ductile refractory high-entropy alloys. Journal of applied physics, 120(16), 164902.
[11] Wei, Y., Li, Y., Zhu, L., Liu, Y., Lei, X., Wang, G., ... & Gao, H. (2014). Evading the strength–ductility trade-off dilemma in steel through gradient hierarchical nanotwins. Nature communications, 5(1), 1-8.
[12] Verlinden, B., Driver, J., Samajdar, I., & Doherty, R. D. (2007). Thermo-mechanical processing of metallic materials. Elsevier.
[13] Hughes, D. A., & Hansen, N. (1997). High angle boundaries formed by grain subdivision mechanisms. Acta materialia, 45(9), 3871-3886.
[14] Humphreys, F. J., & Hatherly, M. (2012). Recrystallization and related annealing phenomena. Elsevier.
[15] Holscher, M., Raabe, D., & Lucke, K. (1991). Rolling and recrystallization textures of bcc steels. Steel Research-Dusseldorf 62(12), 567-575.
[16] Li, Z., Pradeep, K. G., Deng, Y., Raabe, D., & Tasan, C. C. (2016). Metastable high-entropy dual-phase alloys overcome the strength–ductility trade-off. Nature, 534(7606), 227-230.
[17] Wei, Y., Li, Y., Zhu, L., Liu, Y., Lei, X., Wang, G., ... & Gao, H. (2014). Evading the strength–ductility trade-off dilemma in steel through gradient hierarchical nanotwins. Nature communications, 5(1), 1-8.
[18] Liu, L., Ding, Q., Zhong, Y., Zou, J., Wu, J., Chiu, Y. L., ... & Shen, Z. (2018). Dislocation network in additive manufactured steel breaks strength–ductility trade-off. Materials Today, 21(4), 354-361.
[19] Ming, K., Bi, X., & Wang, J. (2019). Strength and ductility of CrFeCoNiMo alloy with hierarchical microstructures. International Journal of Plasticity, 113, 255-268.