Abstract: Friction stir welding (FSW) is an advantageous method in the thermal joining processes, featuring the welding of various dissimilar and similar material combinations, joining temperatures below the melting point which prevents irregularities such as pores and hot cracks as well as high strengths mechanical joints near the base material. The FSW process consists of a rotating tool which is made of a shoulder and a probe. The welding process is based on a rotating tool which plunges in the workpiece under axial pressure. As a result, the material is plasticized by frictional heat which leads to a decrease in the flow stress. During the welding procedure, the material is continuously displaced by the tool, creating a firmly bonded weld seam behind the tool. However, the mechanical properties of the weld seam are affected by the design and geometry of the tool. These include in particular microstructural and surface properties which can favor crack initiation. Following investigation compares the dynamic properties of FSW weld seams with conventional and stationary shoulder geometry based on load increase test (LIT). Compared to classical Woehler tests, it is possible to determine the fatigue strength of the specimens after a short amount of time. The investigations were carried out on a robotized welding setup on 2 mm thick EN AW 5754 aluminum alloy sheets. It was shown that an increased tensile and fatigue strength can be achieved by using the stationary shoulder concept. Furthermore, it could be demonstrated that the LIT is a valid method to describe the fatigue behavior of FSW weld seams.
Abstract: The main objective of this study is to investigate basic properties of different natural clays, by two methods. The first method is a gas phase conversion of methylbutynol (MBOH). The second method is the application of Pyrrole-tpd. Based on the product distribution from the first method, the acidic, basic and coordinately unsaturated sites were differentiated. It was shown that both the conversion and the selectivity for basic products did not change with reaction time. Nevertheless, a deviation from the stoichiometric ratio R of formed acetylene to acetone was observed (R=0.8…0.97). The conversion normalized to the surface area was used for establishing the activity sequence: White kaolinite > red kaolinite > bentonite > zeolite > diatomite. In addition, the results were compared with synthetic amorphous alumosilicates and typical basic materials like MgO and ZnO. The basic properties were characterized using the Pyrrole-tpd. The Pyrrole-tpd results showed the same basicity sequence as the MBOH gas phase reaction.
Abstract: Protective textiles get soiled, stained and even worn during their use, which may not be usable after a certain period due to the loss of protective performance. They need regular cleaning and maintenance, which helps to extend the durability of the clothing, retains their useful properties and ensures that fresh clothing is ready to wear when needed. Generally, the cleaning processes used for various protective clothing include dry-cleaning (using solvents) or wet cleaning (using water). These cleaning processes can alter the fabric surface properties, dimensions, and physical, mechanical and performance properties. The technology of laundering and dry-cleaning has undergone several changes. Sustainable methods and products are available for faster, safer and improved cleaning of protective textiles. We performed a comprehensive and systematic review of green technologies and eco-friendly products for sustainable cleaning of protective textiles. Special emphasis is given on the care and maintenance procedures of protective textiles for protection from fire, bullets, chemical and other types of protective clothing.
Abstract: Nitrogen implantation in aluminum and its alloys is acquainted for the difficulties in obtaining modified layers deeper than 200 nm. The present work addresses a new method to overcome such a problem; although, the coating with nitrogen and oxygen obtained by plasma immersion ion implantation (PIII) into a 7075 aluminum alloy surface was too shallow. This alloy is commonly used for structural parts in aerospace applications. Such a layer was characterized by secondary ion mass spectroscopy, electron microscopy, and nanoindentation experiments reciprocating wear tests. From the results, one can assume that the wear of this aluminum alloy starts presenting severe abrasive wear followed by an additional adhesive mechanism. PIII produced a slight difference, as shown in all characterizations carried out in this work. The results shown here can be used as the scientific basis for further nitrogen PIII experiments in aluminum alloys which have the goal to produce thicker modified layers or to improve their surface properties.
Abstract: Titanium and its alloys have been used extensively over the past 25 years as biomedical materials in orthopedic and dental applications because of their good mechanical properties, corrosion resistance, and biocompatibility. It is known that the surface properties of titanium implants can enhance the cellular response and play an important role in Osseo integration. The rate and quality of Osseo integration in titanium implants are related to their surface properties. The purpose of this investigation was to evaluate the effect of sandblasting and acid etching on surface morphology, roughness, the wettability of titanium. The surface properties will be characterized by scanning electron microscopy and contact angle and roughness measurements. The results show that surface morphology, roughness, and wettability were changed and enhanced by these treatments.
Abstract: Recently, copper and manganese-containing systems are recognized as active and selective catalysts in many oxidation reactions. The main idea of this study is to obtain more information about γ-Al2O3 supported Cu-La catalysts and to evaluate their activity to simultaneous oxidation of CO, CH3OH and dimethyl ether (DME). The catalysts were synthesized by impregnation of support with a mixed aqueous solution of nitrates of copper, manganese and lanthanum under different conditions. XRD, HRTEM/EDS, TPR and thermal analysis were performed to investigate catalysts’ bulk and surface properties. The texture characteristics were determined by Quantachrome Instruments NOVA 1200e specific surface area and pore analyzer. The catalytic measurements of single compounds oxidation were carried out on continuous flow equipment with a four-channel isothermal stainless steel reactor in a wide temperature range. On the basis of XRD analysis and HRTEM/EDS, it was concluded that the active component of the mixed Cu-Mn-La/γ–alumina catalysts strongly depends on the Cu/Mn molar ratio and consisted of at least four compounds – CuO, La2O3, MnO2 and Cu1.5Mn1.5O4. A homogeneous distribution of the active component on the carrier surface was found. The chemical composition strongly influenced catalytic properties. This influence was quite variable with regards to the different processes.
Abstract: The mineral bioflotation represents a viable
alternative for the evaluation of new processes benefit alternative.
The adsorption bacteria on minerals surfaces will depend mainly on
the type of the microorganism as well as of the studied mineral
surface. In the current study, adhesion of S. carnosus on coal was
studied. Several methods were used as: DRX, Fourier Transform
Infra-Red (FTIR) adhesion isotherms and kinetic. The main goal is to
recovery of organic matter by the microflotation process on coal
particles with biological reagent (S. carnosus). Adhesion tests
revealed that adhesion took place after of 8 h at pH 9. The results
suggest that the adhesion of bacteria to solid substrates can be
considered an abiotic physicochemical process that is consequently
governed by bacterial surface properties such as their specific surface
area, hydrophobicity and surface functionalities. The greatest coal
fine flotability was of 75%, after 5 min of flotation.
Abstract: Ultrasonic shot peening (USP) on AALY12 sheet was studied. Several parameters (arc heights, surface roughness, surface topography and micro hardness) with different USP process parameters were measured. The research proposes that radius of curvature of shot peened sheet increases with time and electric current decreasing, while increases with pin diameter increasing, and radius of curvature reaches a saturation level after a specific processing time and electric current. An empirical model of the relationship between radius of curvature and pin diameter, electric current, time was also obtained. The research shows that the increment of surface and vertical micro hardness of material is more obvious with longer time and higher value of electric current, which can be up to 20% and 28% respectively.
Abstract: The surface properties of many materials can be readily and predictably modified by the controlled deposition of thin layers containing appropriate functional groups and this research area is now a subject of widespread interest. The layer-by-layer (lbl) method involves depositing oppositely charged layers of polyelectrolytes onto the substrate material which are stabilized due to strong electrostatic forces between adjacent layers. This type of modification affords products that combine the properties of the original material with the superficial parameters of the new external layers. Through an appropriate selection of the deposited layers, the surface properties can be precisely controlled and readily adjusted in order to meet the requirements of the intended application. In the presented paper a variety of anionic (poly(acrylic acid)) and cationic (linear poly(ethylene imine), polymers were successfully deposited onto the polypropylene nonwoven using the lbl technique. The chemical structure of the surface before and after modification was confirmed by reflectance FTIR spectroscopy, volumetric analysis and selective dyeing tests. As a direct result of this work, new materials with greatly improved properties have been produced. For example, following a modification process significant changes in the electrostatic activity of a range of novel nanocomposite materials were observed. The deposition of polyelectrolyte nanolayers was found to strongly accelerate the loss of electrostatically generated charges and to increase considerably the thermal resistance properties of the modified fabric (the difference in T50% is over 20oC). From our results, a clear relationship between the type of polyelectrolyte layer deposited onto the flat fabric surface and the properties of the modified fabric was identified.
Abstract: This work deals with the synthesis and the determination of some surface properties of a new anionic surfactant belonging to sulfonamide derivatives. The interest in this new surfactant is that its behavior in aqueous solution is interesting both from a fundamental and a practice point of view. Indeed, it is well known that this kind of surfactant leads to the formation of bilayer structures, and the microstructures obtained have applications in various fields, ranging from cosmetics to detergents, to biological systems such as cell membranes and bioreactors. The surfactant synthesized from pure n-alkane by photosulfochlorination and derivatized using N-ethanol amine is a mixture of position isomers. These compounds have been analyzed by Gas Chromatography coupled to Mass Spectrometry by Electron Impact mode (GC -MS/IE), and IR. The surface tension measurements were carried out, leading to the determination of the critical micelle concentration (CMC), surface excess and the area occupied per molecule at the interface. The foaming power has also been determined by Bartsch method, and the results have been compared to those of commercial surfactants. The stability of the foam formed has also been evaluated. These compounds show good foaming power characterized in most cases by dry foam.
Abstract: This work deals with problems of tool axis inclination angles in ball-end milling. Tool axis inclination angle contributes to improvement of functional surface properties (surface integrity - surface roughness, residual stress, micro hardness, etc.), decreasing cutting forces and improving production. By milling with ball-end milling tool, using standard way of cutting, when work piece and cutting tool contain right angle, we have zero cutting speed on edge. At this point cutting tool only pushes material into the work piece. Here we can observe the following undesirable effects - chip contraction, increasing of cutting temperature, increasing vibrations or creation of built-up edge. These effects have negative results – low quality of surface and decreasing of tool life (in the worse case even it is pinching out). These effects can be eliminated with the tilt of cutting tool or tilt of work piece.
Abstract: Polymer-like organic thin films were deposited on both
aluminum alloy type 6061 and glass substrates at room temperature by
Plasma Enhanced Chemical Vapor Deposition (PECVD) methodusing
benzene and hexamethyldisiloxane (HMDSO) as precursor materials.
The surface and physical properties of plasma-polymerized organic
thin films were investigated at different r.f. powers. The effects of
benzene/argon ratio on the properties of plasma polymerized benzene
films were also investigated. It is found that using benzene alone
results in a non-coherent and non-adherent powdery deposited
material. The chemical structure and surface properties of the asgrown
plasma polymerized thin films were analyzed on glass
substrates with FTIR and contact angle measurements. FTIR spectra
of benzene deposited film indicated that the benzene rings are
preserved when increasing benzene ratio and/or decreasing r.f.
powers. FTIR spectra of HMDSO deposited films indicated an
increase of the hydrogen concentration and a decrease of the oxygen
concentration with the increase of r.f. power. The contact angle (θ) of
the films prepared from benzene was found to increase by about 43%
as benzene ratio increases from 10% to 20%. θ was then found to
decrease to the original value (51°) when the benzene ratio increases
to 100%. The contact angle, θ, for both benzene and HMDSO
deposited films were found to increase with r.f. power. This signifies
that the plasma polymerized organic films have substantially low
surface energy as the r.f power increases. The corrosion resistance of
aluminum alloy substrate both bare and covered with plasma
polymerized thin films was carried out by potentiodynamic
polarization measurements in standard 3.5 wt. % NaCl solution at
room temperature. The results indicate that the benzene and HMDSO
deposited films are suitable for protection of the aluminum substrate
against corrosion. The changes in the processing parameters seem to
have a strong influence on the film protective ability. Surface
roughness of films deposited on aluminum alloy substrate was
investigated using scanning electron microscopy (SEM). The SEM
images indicate that the surface roughness of benzene deposited films
increase with decreasing the benzene ratio. SEM images of benzene
and HMDSO deposited films indicate that the surface roughness
decreases with increasing r.f. power. Studying the above parameters
indicate that the films produced are suitable for specific practical
applications.
Abstract: In this study, the adhesion of ice to solid substrates
with different surface properties is compared. Clear ice, similar to
atmospheric in-flight icing encounters, is accreted on the different
substrates under controlled conditions. The ice adhesion behavior is
investigated by means of a dynamic vibration testing technique with
an electromagnetic shaker initiating ice de-bonding in the interface
between the substrate and the ice. The results of the experiments
reveal that the affinity for ice accretion is significantly influenced by
the water contact angle of the respective sample.
Abstract: This study uses natural water and the surface properties of powdered activated carbon to acclimatize organics, forming biofilms on the surface of powdered activated carbon. To investigate the influence of different hydraulic retention times on the removal efficacy of trace organics in raw water, and to determine the optimal hydraulic retention time of a biological powdered activated carbon system, this study selects ozone-treated water processed by Feng-shan Advanced Water Purification Plant in southern Taiwan for the experiment. The evaluation indicators include assimilable organic carbon, dissolved organic carbon, and total organic carbon. The results of this study can improve the quality of drinking water treated using advanced water purification procedures.
Abstract: Biomimicry has many potential benefits as many
technologies found in nature are superior to their man-made
counterparts. As technological device components approach the micro
and nanoscale, surface properties such as surface adhesion and friction
may need to be taken into account. Lowering surface adhesion by
manipulating chemistry alone might no longer be sufficient for such
components and thus physical manipulation may be required.
Adhesion reduction is only one of the many surface functions
displayed by micro/nano-structured cuticles of insects. Here, we
present a mini review of our understanding of insect cuticle structures
and the relationship between the structure dimensions and the
corresponding functional mechanisms. It may be possible to introduce
additional properties to material surfaces (indeed multi-functional
properties) based on the design of natural surfaces.
Abstract: Magnesium is used implant material potentially for
non-toxicity to the human body. Due to the excellent
bio-compatibility, Mg alloys is applied to implants avoiding removal
second surgery. However, it is found commercial magnesium alloys
including aluminum has low corrosion resistance, resulting
subcutaneous gas bubbles and consequently the approach as
permanent bio-materials. Generally, Aluminum is known to pollution
substance, and it raises toxicity to nervous system. Therefore
especially Mg-35Zn-3Ca alloy is prepared for new biodegradable
materials in this study. And the pulsed power is used in
constant-current mode of DC power kinds of anodization. Based on
the aforementioned study, it examines corrosion resistance and
biocompatibility by effect of current and frequency variation. The
surface properties and thickness were compared using scanning
electronic microscopy. Corrosion resistance was assessed via
potentiodynamic polarization and the effect of oxide layer on the body
was assessed cell viability. Anodized Mg-35Zn-3Ca alloy has good
biocompatibility in vitro by current and frequency variation.
Abstract: The nature of adsorbed species on catalytic surface
over an industrial precipitated iron-based high temperature catalyst
during FTS was investigated by in-situ DRIFTS and chemical
trapping. The formulation of the mechanism of oxygenates formation
and key intermediates were also discussed. Numerous oxygenated
precursors and crucial intermediates were found by in-situ DRIFTS,
such as surface acetate, acetyl and methoxide. The results showed that
adsorbed molecules on surface such as methanol or acetaldehyde
could react with basic sites such as lattice oxygen or free surface
hydroxyls. Adsorbed molecules also had reactivity of oxidizing.
Moreover, acetyl as a key intermediate for oxygenates was observed
by investigation of CH3OH + CO and CH3I + CO + H2. Based on the
nature of surface properties, the mechanism of oxygenates formation
on precipitated iron-based high temperature catalyst was discussed.