Abstract: Catalysts play an important role in producing valuable fuel products in petroleum refining; but, due to feedstock’s impurities catalyst gets deactivated with carbon and metal deposition. The disposal of spent catalyst falls under the category of hazardous industrial waste that requires strict agreement with environmental regulations. The spent hydroprocessing catalyst contains Mo, V and Ni at high concentrations that have been found to be economically significant for recovery. Metal recovery process includes deoiling, decoking, grinding, dissolving and treatment with complexing leaching agent such as ethylene diamine tetra acetic acid (EDTA). The process conditions have been optimized as a function of time, temperature and EDTA concentration in presence of ultrasonic agitation. The results indicated that optimum condition established through this approach could recover 97%, 94% and 95% of the extracted Mo, V and Ni, respectively, while 95% EDTA was recovered after acid treatment.
Abstract: The present investigation deals with bioleaching of spent petroleum catalyst using At. ferrooxidans and At. thiooxidans. The spent catalyst used in the present study was pretreated with acetone to remove the oily hydrocarbons. FESEM and XPS analysis indicated the presence of metals in sulfide and oxide forms in spent catalyst. Both At. ferrooxidans and At. thiooxidans were found to be highly effective in producing the acid. Bioleaching with At. ferrooxidans and At. thiooxidans led to higher recovery of metals compare to control. During bioleaching similar recoveries of metals were obtained using At. ferrooxidans and At. thiooxidans. This might be due to the presence of metals as soluble oxides and sulphides in the spent catalyst. At the end of bioleaching, about 87-90% Ni, 34% Al, 65-73% Mo and 92-97% V were leached using above bacteria. It is elucidated that bioleaching with At. thiooxidans is comparatively more advantageous due to lower cost of sulphur.
Abstract: Bioleaching of spent catalyst using moderate thermophilic chemolithotrophic acidophiles in growth medium without Fe source was investigated with two different pulp densities and three different size fractions. All the experiments were conducted on shake flasks at a temperature of 65 °C. The leaching yield of Ni and Al was found to be promising with very high leaching yield of 92-96% followed by Al as 41-76%, which means both Ni and Al leaching were favored by the moderate thermophilic bioleaching compared to the mesophilic bioleaching. The acid consumption was comparatively higher for the 10% pulp density experiments. Comparatively minimal difference in the leaching yield with different size fractions and different pulp densities show no requirement of grinding and using low pulp density less than 10%. This process would rather be economical as well as eco-friendly process for future optimization of the recovery of metal values from spent catalyst.
Abstract: The recovery of metal values and safe disposal of
spent catalyst is gaining interest due to both its hazardous nature and
increased regulation associated with disposal methods. Prior to the
recovery of the valuable metals, removal of entrained deposits limit
the diffusion of lixiviate resulting in low recovery of metals must be
taken into consideration. Therefore, petroleum refinery spent catalyst
was subjected to acetone washing and roasting at 500oC. The treated
samples were investigated for metals bioleaching using
Acidithiobacillus ferrooxidans in batch reactors and the leaching
efficiencies were compared. It was found out that acetone washed
spent catalysts results in better metal recovery compare to roasted
spent. About 83% Ni, 20% Al, 50% Mo and 73% V were leached
using the acetone washed spent catalyst. In both the cases, Ni, V and
Mo was high compared to Al.
Abstract: Spent petroleum catalyst from Korean petrochemical
industry contains trace amount of metals such as Ni, V and Mo.
Therefore an attempt was made to recover those trace metal using
bioleaching process. Different leaching parameters such as Fe(II)
concentration, pulp density, pH, temperature and particle size of
spent catalyst particle were studied to evaluate their effects on the
leaching efficiency. All the three metal ions like Ni, V and Mo
followed dual kinetics, i.e., initial faster followed by slower rate. The
percentage of leaching efficiency of Ni and V were higher than Mo.
The leaching process followed a diffusion controlled model and the
product layer was observed to be impervious due to formation of
ammonium jarosite (NH4)Fe3(SO4)2(OH)6. In addition, the lower
leaching efficiency of Mo was observed due to a hydrophobic coating
of elemental sulfur over Mo matrix in the spent catalyst.