Abstract: Coatings based on polyaniline (PANI) can improve the resistance of steel against corrosion. In this work, the preparation of stable suspensions of colloidal PANI-SiO2 particles, suitable for obtaining of composite anticorrosive coating on steel, is described. Electrokinetic data as a function of pH are presented, showing that the zeta potentials of the PANI-SiO2 particles are governed primarily by the charged groups at the silica oxide surface. Electrosteric stabilization of the PANI-SiO2 particles’ suspension against aggregation is realized at pH>5.5 (EB form of PANI) by adsorption of positively charged polyelectrolyte molecules onto negatively charged PANI-SiO2 particles. The PANI-SiO2 particles are incorporated by electrodeposition into the metal matrix of zinc in order to obtain composite (hybrid) coatings. The latter are aimed to ensure sacrificial protection of steel mainly in aggressive media leading to local corrosion damages. The surface morphology of the composite zinc coatings is investigated with SEM. The influence of PANI-SiO2 particles on the cathodic and anodic processes occurring in the starting electrolyte for obtaining of the coatings is followed with cyclic voltammetry. The electrochemical and corrosion behavior is evaluated with potentiodynamic polarization curves and polarization resistance measurements. The beneficial effect of the stabilized PANI-SiO2 particles for the increased protective ability of the composites is commented and discussed.
Abstract: Polymer-like organic thin films were deposited on both
aluminum alloy type 6061 and glass substrates at room temperature by
Plasma Enhanced Chemical Vapor Deposition (PECVD) methodusing
benzene and hexamethyldisiloxane (HMDSO) as precursor materials.
The surface and physical properties of plasma-polymerized organic
thin films were investigated at different r.f. powers. The effects of
benzene/argon ratio on the properties of plasma polymerized benzene
films were also investigated. It is found that using benzene alone
results in a non-coherent and non-adherent powdery deposited
material. The chemical structure and surface properties of the asgrown
plasma polymerized thin films were analyzed on glass
substrates with FTIR and contact angle measurements. FTIR spectra
of benzene deposited film indicated that the benzene rings are
preserved when increasing benzene ratio and/or decreasing r.f.
powers. FTIR spectra of HMDSO deposited films indicated an
increase of the hydrogen concentration and a decrease of the oxygen
concentration with the increase of r.f. power. The contact angle (θ) of
the films prepared from benzene was found to increase by about 43%
as benzene ratio increases from 10% to 20%. θ was then found to
decrease to the original value (51°) when the benzene ratio increases
to 100%. The contact angle, θ, for both benzene and HMDSO
deposited films were found to increase with r.f. power. This signifies
that the plasma polymerized organic films have substantially low
surface energy as the r.f power increases. The corrosion resistance of
aluminum alloy substrate both bare and covered with plasma
polymerized thin films was carried out by potentiodynamic
polarization measurements in standard 3.5 wt. % NaCl solution at
room temperature. The results indicate that the benzene and HMDSO
deposited films are suitable for protection of the aluminum substrate
against corrosion. The changes in the processing parameters seem to
have a strong influence on the film protective ability. Surface
roughness of films deposited on aluminum alloy substrate was
investigated using scanning electron microscopy (SEM). The SEM
images indicate that the surface roughness of benzene deposited films
increase with decreasing the benzene ratio. SEM images of benzene
and HMDSO deposited films indicate that the surface roughness
decreases with increasing r.f. power. Studying the above parameters
indicate that the films produced are suitable for specific practical
applications.