Abstract: Phase equilibria of AZ91D Mg alloys for
nonflammable use, containing Ca and Y, were carried out by using
FactSage® and FTLite database, which revealed that solid solution
treatment could be performed at temperatures from 400 to 450oC.
Solid solution treatment of AZ91D Mg alloy without Ca and Y was
successfully conducted at 420oC and supersaturated microstructure
with all beta phase resolved into matrix was obtained. In the case of
AZ91D Mg alloy with some Ca and Y; however, a little amount of
intermetallic particles were observed after solid solution treatment.
After solid solution treatment, each alloy was annealed at temperatures
of 180 and 200oC for time intervals from 1 min to 48 hrs and hardness
of each condition was measured by micro-Vickers method. Peak aging
conditions were deduced as at the temperature of 200oC for 10 hrs.