Abstract: Fe-based amorphous feedstock powders are used as the matrix into which various ratios of hard B4C nanoparticles (0, 5, 10, 15, 20 vol.%) as reinforcing agents were prepared using a planetary high-energy mechanical milling. The ball-milled nanocomposite feedstock powders were also sprayed by means of high-velocity oxygen fuel (HVOF) technique. The characteristics of the powder particles and the prepared coating depending on their microstructures and nanohardness were examined in detail using nanoindentation tester. The results showed that the formation of the Fe-based amorphous phase was noticed over the course of high-energy ball milling. It is interesting to note that the nanocomposite coating is divided into two regions, namely, a full amorphous phase region and homogeneous dispersion of B4C nanoparticles with a scale of 10–50 nm in a residual amorphous matrix. As the B4C content increases, the nanohardness of the composite coatings increases, but the fracture toughness begins to decrease at the B4C content higher than 20 vol.%. The optimal mechanical properties are obtained with 15 vol.% B4C due to the suitable content and uniform distribution of nanoparticles. Consequently, the changes in mechanical properties of the coatings were attributed to the changes in the brittle to ductile transition by adding B4C nanoparticles.
Abstract: Zn alloy and composite coatings are widely used in
buildings and structures, automobile and fasteners industries to
protect steel component from corrosion. In this paper, Zn-Ni-Al2O3
nanocomposite coatings were electrodeposited on mild steel using a
novel sol enhanced electroplating method. In this method, transparent
Al2O3 sol was added into the acidic Zn-Ni bath to produced Zn-Ni-
Al2O3 nanocomposite coatings. The effect of alumina sol on the
electrodeposition process, and coating properties was investigated
using cyclic voltammetry, XRD, ESEM and Tafel test. Results from
XRD tests showed that the structure of all coatings was single γ-
Ni5Zn21 phase. Cyclic voltammetry results showed that the
electrodeposition overpotential was lower in the presence of alumina
sol in the bath, and caused the reduction potential of Zn-Ni to shift to
more positive values. Zn-Ni-Al2O3 nanocomposite coatings produced
more uniform and compact deposits, with fine grained microstructure
when compared to Zn-Ni coatings. The corrosion resistance of Zn-Ni
coatings was improved significantly by incorporation of alumina
nanoparticles into the coatings.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: We investigate the ZnO role in the inherent protection
of old manuscripts to protect them against environmental damaging
effect of ultraviolet radiation, pollutant gasses, mold and bacteria. In
this study a cellulosic nanocomposite of ZnO were used as protective
coating on the surface of paper fibers. This layered nanocomposite
can act as a consolidate materials too. Furthermore, to determine how
well paper works screen objects from the damaging effects, two
accelerated aging mechanisms due to light and heat are discussed.
Results show good stability of papers with nanocomposite coating.
Also, a good light stability was shown in the colored paper that
treated with this nanocomposite. Furthermore, to demonstrate the
degree of antifungal and antibacterial properties of coated papers,
papers was treated with four common molds and bacteria and the
good preventive effects of coated paper against molds and bacteria
are described.