Abstract: Martensitic texture-phase transition in Selective Laser Melting (SLM) Ti-6Al-4V (ELI) alloys was found. Electron Backscatter Diffraction (EBSD) analysis showed the initial cubic beta < 100 > (001) BCC texture. Such kind of texture is observed in BCC metals with flat rolling texture when axis is in the direction of rolling and the texture plane coincides with the plane of rolling. It was found that the texture of the parent BCC beta-phase determined the texture of low-temperature HCP alpha-phase limited the choice of its orientation variants. The {10-12} < -1011 > twinning system in titanium alloys after SLM was determined. Analysis of the oxygen contamination in SLM alloys was done. Comparison of the obtained results with the conventional titanium alloys is also provided.
Abstract: Selective laser melting (SLM), a promising additive manufacturing (AM) technology, has a huge potential in the fabrication of Ti-6Al-4V near-net shape components. However, poor surface finish of the components fabricated from this technology requires secondary machining to achieve the desired accuracy and tolerance. Therefore, a systematic understanding of the machinability of SLM fabricated Ti-6Al-4V components is paramount to improve the productivity and product quality. Considering the significance of machining in SLM fabricated Ti-6Al-4V components, this research aim is to study the influence of build orientation on machinability characteristics by performing low speed orthogonal cutting tests. In addition, the machinability of SLM fabricated Ti-6Al-4V is compared with conventionally produced wrought Ti-6Al-4V to understand the influence of SLM technology on machining. This paper is an attempt to provide evidence to the hypothesis associated that build orientation influences cutting forces, chip formation and surface integrity during orthogonal cutting of SLM Ti-6Al-4V samples. Results obtained from the low speed orthogonal cutting tests highlight the practical importance of microstructure and build orientation on machinability of SLM Ti-6Al-4V.
Abstract: The commercially available titanium alloy, Ti-6Al-4V, was oxynitrided in the deoxygenated nitrogen gas at high temperatures followed by cooling in oxygen-containing nitrogen in order to analyze the influence of oxynitriding parameters on the phase modification, hardness, and the microstructural evolution of the oxynitrided coating. The surface microhardness of the oxynitrided alloy increased due to the strengthening effect of the formed titanium oxynitrides, TiNxOy. The maximum microhardness was obtained, when TiNxOy had near equiatomic composition of nitrogen and oxygen. It could be attained under the optimum oxygen partial pressure and temperature-time condition.
Abstract: Due to reduced stiffness, research on second
generation titanium alloys for implant applications, like the
metastable β-titanium alloy Ti-15Mo, become more and more
important in the recent years. The machinability of these alloys is
generally poor leading to problems during implant production and
comparably large production costs. Therefore, in the present study,
Ti-15Mo was alloyed with 0.8 wt.-% of the rare earth metals
lanthanum (Ti-15Mo+0.8La) and neodymium (Ti-15Mo+0.8Nd) to
improve its machinability. Their microstructure consisted of a
titanium matrix and micrometer-size particles of the rare earth metals
and two of their oxides. The particles stabilized the microstructure as
grain growth was minimized. As especially the ductility might be
affected by the precipitates, the behavior of Ti-15Mo+0.8La and Ti-
15Mo+0.8Nd was investigated during static and dynamic
deformation at elevated temperature to develop a processing route.
The resulting mechanical properties (static strength and ductility)
were similar in all investigated alloys.
Abstract: Biometallic materials are the most important materials for use in biomedical applications especially in manufacturing a variety of biological artificial replacements in a modern worlds, e.g. hip, knee or shoulder joints, due to their advanced characteristics. Titanium (Ti) and its alloys are used extensively in biomedical applications based on their high specific strength and excellent corrosion resistance. Beta-Ti alloys containing completely biocompatible elements are exceptionally prospective materials for manufacturing of bioimplants. They have superior mechanical, chemical and electrochemical properties for use as biomaterials. These biomaterials have the ability to introduce the most important property of biochemical compatibility which is low elastic modulus. This review examines current information on the recent developments in alloying elements leading to improvements of beta Ti alloys for use as biomaterials. Moreover, this paper focuses mainly on the evolution, evaluation and development of the modulus of elasticity as an effective factor on the performance of beta alloys.
Abstract: Asymmetric incremental sheet forming (AISF) could significantly reduce costs incurred by the fabrication of complex industrial components with a minimal environmental impact. The AISF experiments were carried out on commercially pure titanium (Ti-Gr2), Timetal (15-3-3-3) alloy, and Ti-6Al-4V (Ti-Gr5) alloy. A special testing geometry was used to characterize the titanium alloys properties from the point of view of the forming zone and titanium structure effect. The structure and properties of the materials were assessed by means of metallographic analyses and microhardness measurements.The highest differences in the parameters assessed as a function of the sampling zone were observed in the case of alpha-phase Ti-Gr2at the expense of the most substantial sheet thinning occurrence. A springback causes a smaller stored deformation in Timetal (β alloy) resulting in less pronounced microstructure refinement and microhardness increase. Ti-6Al-4V alloy exhibited early failure due to its poor formability at ambient temperature.
Abstract: Shear spinning is closely related to the asymmetric incremental sheet forming (AISF) that could significantly reduce costs incurred by the fabrication of complex aeronautical components with a minimal environmental impact. The spinning experiments were carried out on commercially pure titanium (Ti-Gr2) and Ti-6Al-4V (Ti-Gr5) alloy. Three forming modes were used to characterize the titanium alloys properties from the point of view of different spinning parameters. The structure and properties of the materials were assessed by means of metallographic analyses and microhardness measurements. The highest value wall angle failure limit was achieved using spinning parameters mode for both materials. The feed rate effect was observed only in the samples from the Ti-Gr2 material, when a refinement of the grain microstructure with lower feed rate and higher tangential speed occurred. Ti-Gr5 alloy exhibited a decrease of the microhardness at higher straining due to recovery processes.
Abstract: Titanium alloys like Ti-6Al-2Sn-4Zr-6Mo (Ti-
6246) are widely used in aerospace applications. Component
manufacturing, however, is difficult and expensive as their
machinability is extremely poor. A thorough understanding of the
chip formation process is needed to improve related metal cutting
operations.In the current study, orthogonal cutting experiments have
been performed and theresulting chips were analyzed by optical
microscopy and scanning electron microscopy.Chips from aTi-
6246ingot were produced at different cutting speeds and cutting
depths. During the experiments, depending of the cutting conditions,
continuous or segmented chips were formed. Narrow, highly
deformed and grain oriented zones, the so-called shear zone,
separated individual segments. Different material properties have
been measured in the shear zones and the segments.
Abstract: Ti-6Al-4V alloy has demonstrated a high strength to
weight ratio as well as good properties at high temperature. The
successful application of the alloy in some important areas depends
on suitable joining techniques. Friction welding has many
advantageous features to be chosen for joining Titanium alloys. The
present work investigates the feasibility of producing similar metal
joints of this Titanium alloy by rotary friction welding method. The
joints are produced at three different speeds and the performances of
the welded joints are evaluated by conducting microstructure studies,
Vickers Hardness and tensile tests at the joints. It is found that the
weld joints produced are sound and the ductile fractures in the tensile
weld specimens occur at locations away from the welded joints. It is
also found that a rotational speed of 1500 RPM can produce a very
good weld, with other parameters kept constant.
Abstract: Greenhouse gases (GHG) emissions impose major
threat to global warming potential (GWP). Unfortunately
manufacturing sector is one of the major sources that contribute
towards the rapid increase in greenhouse gases (GHG) emissions. In
manufacturing sector electric power consumption is the major driver
that influences CO2 emission. Titanium alloys are widely utilized in
aerospace, automotive and petrochemical sectors because of their
high strength to weight ratio and corrosion resistance. Titanium
alloys are termed as difficult to cut materials because of their poor
machinability rating. The present study analyzes energy consumption
during cutting with reference to material removal rate (MRR).
Surface roughness was also measured in order to optimize energy
consumption.
Abstract: Titanium alloys like the modern alloy Ti 6Al 2Sn 4Zr 6Mo (Ti-6246) combine excellent specific mechanical properties and corrosion resistance. On the other hand,due to their material characteristics, machining of these alloys is difficult to perform. The aim of the current study is the analyses of wear mechanisms of coated cemented carbide tools applied in orthogonal cutting experiments of Ti-6246 alloy. Round bars were machined with standard coated tools in dry conditions on a CNC latheusing a wide range of cutting speeds and cutting depths. Tool wear mechanisms were afterwards investigated by means of stereo microscopy, optical microscopy, confocal microscopy and scanning electron microscopy. Wear mechanisms included fracture of the tool tip (total failure) and abrasion. Specific wear features like crater wear, micro cracks and built-up edgeformation appeared depending of the mechanical and thermal conditions generated in the workpiece surface by the cutting action.