Abstract: Commercially SA 516 Grade 70 is frequently used for the manufacturing of pressure vessels, boilers and storage tanks etc. in fabrication industry. Heat input is the major parameter during welding that may bring significant changes in the microstructure as well as the mechanical properties. Different welding technique has different heat input rate per unit surface area. Materials with large thickness are dealt with different combination of welding techniques to achieve required mechanical properties. In the present research two schemes: Scheme 1: SMAW (Shielded Metal Arc Welding) & GTAW (Gas Tungsten Arc Welding) and Scheme 2: SMAW & SAW (Submerged Arc Welding) of hybrid welding techniques have been studied. The purpose of these schemes was to study hybrid welding effect on the microstructure and mechanical properties of the weldment, heat affected zone and base metal area. It is significant to note that the thickness of base plate was 12 mm, also welding conditions and parameters were set according to ASME Section IX. It was observed that two different hybrid welding techniques performed on two different plates demonstrated that the mechanical properties of both schemes are more or less similar. It means that the heat input, welding techniques and varying welding operating conditions & temperatures did not make any detrimental effect on the mechanical properties. Hence, the hybrid welding techniques mentioned in the present study are favorable to implicate for the industry using the plate thickness around 12 mm thick.
Abstract: This research paper portrays a comparative analysis of
thermomechanical behaviour of Shielded Metal Arc Welding
(SMAW) and Gas Tungsten Arc Welding (GTAW) of low carbon
steel of AISI 1020 grade butt joints. The thermal history has been
obtained by experimental work. We have focused on temperature
dependent cooling rate as depicted by Adam’s two-dimensional
model. The effect of moving point heat source of SMAW and GTAW
on mechanical properties has been judged by optical and scanning
electron micrographs of different regions in weld joints. The
microhardness study has been carried to visualize the joint strength
due to formation of different phases.