Abstract: In the present study, M2 high speed steels were
fabricated by using electro-slag rapid remelting process. Carbide
structure was analysed and the fracture toughness and hardness were
also measured after austenitization treatment at 1190 and 1210oC
followed by tempering treatment at 535oC for billets with various
diameters from 16 to 60 mm. Electro-slag rapid remelting (ESRR)
process is an advanced ESR process combined by continuous casting
and successfully employed in this study to fabricate a sound M2 high
speed ingot. Three other kinds of commercial M2 high speed steels,
produced by traditional method, were also analysed for comparison.
Distribution and structure of eutectic carbides of the ESRR billet were
found to be comparable to those of commercial alloy and so was the
fracture toughness.