Abstract: Magnetic spinel ferrites are materials that possess size, magnetic properties and heating ability adequate for their potential use in biomedical applications. The Mn0.5Ga0.5Fe2O4 magnetic nanoparticles (MNPs) were synthesized by sol-gel method using citric acid as chelating agent of metallic precursors. The synthesized samples were identified by X-Ray Diffraction (XRD) as an inverse spinel structure with no secondary phases. Saturation magnetization (Ms) of crystalline powders was 45.9 emu/g, which was higher than those corresponding to GaFe2O4 (14.2 emu/g) and MnFe2O4 (40.2 emu/g) synthesized under similar conditions, while the coercivity field (Hc) was 27.9 Oe. The average particle size was 18 ± 7 nm. The heating ability of the MNPs was enough to increase the surrounding temperature up to 43.5 °C in 7 min when a quantity of 4.5 mg of MNPs per mL of liquid medium was tested. Cytotoxic effect (hemolysis assay) of MNPs was determined and the results showed hemolytic values below 1% in all tested cases. According to the results obtained, these synthesized nanoparticles can be potentially used as thermoseeds for hyperthermia therapy.
Abstract: We investigated magneto-optical Kerr effect in transparent region of implanted ferrite-garnet films for the (YBiCa)3(FeGe)5O12. The implantation process was carried out at room temperature by Ne+ ions with energy of 100 KeV and with various doses (0.5-2.5) 1014 ion/cm2. We discovered that slight deviation of the plane of external alternating magnetic field from plane of sample leads to appearance intensive magneto-optical maximum in transparent region of garnet films ħω=0.5-2.0 eV. In the proceeding, we have also found that the deviation of polarization plane from P- component of incident light leads to the appearance of the similar magneto-optical effects in this region. The research of magnetization processes in transparent region of garnet films showed that the formation of magneto-optical effects in region ħω=0.5-2.3 eV has a rather complex character.
Abstract: Among the different cancer treatments that are currently used, hyperthermia has a promising potential due to the multiple benefits that are obtained by this technique. In general terms, hyperthermia is a method that takes advantage of the sensitivity of cancer cells to heat, in order to damage or destroy them. Within the different ways of supplying heat to cancer cells and achieve their destruction or damage, the use of magnetic nanoparticles has attracted attention due to the capability of these particles to generate heat under the influence of an external magnetic field. In addition, these nanoparticles have a high surface area and sizes similar or even lower than biological entities, which allow their approaching and interaction with a specific region of interest. The most used magnetic nanoparticles for hyperthermia treatment are those based on iron oxides, mainly magnetite and maghemite, due to their biocompatibility, good magnetic properties and chemical stability. However, in order to fulfill more efficiently the requirements that demand the treatment of magnetic hyperthermia, there have been investigations using ferrites that incorporate different metallic ions, such as Mg, Mn, Co, Ca, Ni, Cu, Li, Gd, etc., in their structure. This paper reports the synthesis of nanosized MgxMn1-xFe2O4 (x = 0.3 and 0.4) ferrites by sol-gel method and their evaluation in terms of heating capability and in vitro hemolysis to determine the potential use of these nanoparticles as thermoseeds for the treatment of cancer by magnetic hyperthermia. It was possible to obtain ferrites with nanometric sizes, a single crystalline phase with an inverse spinel structure and a behavior near to that of superparamagnetic materials. Additionally, at concentrations of 10 mg of magnetic material per mL of water, it was possible to reach a temperature of approximately 45°C, which is within the range of temperatures used for the treatment of hyperthermia. The results of the in vitro hemolysis assay showed that, at the concentrations tested, these nanoparticles are non-hemolytic, as their percentage of hemolysis is close to zero. Therefore, these materials can be used as thermoseeds for the treatment of cancer by magnetic hyperthermia.
Abstract: Thermo-mechanical processing with various processing parameters was applied to 0.2%C-0.6%Mn-2S%i-0.8%Cr low alloyed high strength steel. The aim of the processing was to achieve the microstructures typical for transformation induced plasticity (TRIP) steels. Thermo-mechanical processing used in this work incorporated two or three deformation steps. The deformations were in all the cases carried out during the cooling from soaking temperatures to various bainite hold temperatures. In this way, 4-10% of retained austenite were retained in the final microstructures, consisting further of ferrite, bainite, martensite and pearlite. The complex character of TRIP steel microstructure is responsible for its good strength and ductility. The strengths achieved in this work were in the range of 740 MPa – 836 MPa with ductility A5mm of 31-41%.
Abstract: Corrosion problem which exists in every stage of oil and gas production has been a great challenge to the operators in the industry. The conventional carbon steel with all its inherent advantages has been adjudged susceptible to the aggressive corrosion environment of oilfield. This has aroused increased interest in the use of micro alloyed steels for oil and gas production and transportation. The corrosion behavior of three commercially supplied micro alloyed steels designated as A, B, and C have been investigated with API 5L X65 as reference samples. Electrochemical corrosion tests were conducted in an unbuffered 3.5 wt% NaCl solution saturated with CO2 at 30 0C for 24 hours. Pre-corrosion analyses revealed that samples A, B and X65 consist of ferrite-pearlite microstructures but with different grain sizes, shapes and distribution whereas sample C has bainitic microstructure with dispersed acicular ferrites. The results of the electrochemical corrosion tests showed that within the experimental conditions, the corrosion rate of the samples can be ranked as CR(A)< CR(X65)< CR(B)< CR(C). These results are attributed to difference in microstructures of the samples as depicted by ASTM grain size number in accordance with ASTM E112-12 Standard and ferrite-pearlite volume fractions determined by ImageJ Fiji grain size analysis software.
Abstract: Nanomaterials ferrites have applications in making permanent magnets, high density information devices, color imaging etc. In the present examination, lithium ferrite is synthesized by sol-gel process. The x-ray diffraction (XRD) result shows that the structure of lithium ferrite is monoclinic structure. The average particle size 22 nm is calculated by Scherer formula. The lattice parameters and dislocation density (δ) are calculated from XRD data. Strain (ε) values are evaluated from Williamson – hall plot. The FT-IR study reveals the formation of ferrites showing the significant absorption bands. The VU-VIS spectroscopic data is used to calculate direct and indirect optical band gap (Eg) of 1.57eV and 1.01eV respectively for lithium ferrite by using Tauc plot at the edge of the absorption band. The energy dispersive x-ray analysis spectra showed that the expected elements exist in the material. The magnetic behaviour of the materials studied using vibrating sample magnetometer (VSM).
Abstract: A systematic study was conducted to explore the photocatalytic reduction of carbon dioxide (CO2) into methanol on TiO2 loaded copper ferrite (CuFe2O4) photocatalyst under visible light irradiation. The phases and crystallite size of the photocatalysts were characterized by X-ray diffraction (XRD) and it indicates CuFe2O4 as tetragonal phase incorporation with anatase TiO2 in CuFe2O4/TiO2 hetero-structure. The XRD results confirmed the formation of spinel type tetragonal CuFe2O4 phases along with predominantly anatase phase of TiO2 in the CuFe2O4/TiO2 hetero-structure. UV-Vis absorption spectrum suggested the formation of the hetero-junction with relatively lower band gap than that of TiO2. Photoluminescence (PL) technique was used to study the electron–hole (e−/h+) recombination process. PL spectra analysis confirmed the slow-down of the recombination of electron–hole (e−/h+) pairs in the CuFe2O4/TiO2 hetero-structure. The photocatalytic performance of CuFe2O4/TiO2 was evaluated based on the methanol yield with varying amount of TiO2 over CuFe2O4 (0.5:1, 1:1, and 2:1) and changing light intensity. The mechanism of the photocatalysis was proposed based on the fact that the predominant species of CO2 in aqueous phase were dissolved CO2 and HCO3- at pH ~5.9. It was evident that the CuFe2O4 could harvest the electrons under visible light irradiation, which could further be injected to the conduction band of TiO2 to increase the life time of the electron and facilitating the reactions of CO2 to methanol. The developed catalyst showed good recycle ability up to four cycles where the loss of activity was ~25%. Methanol was observed as the main product over CuFe2O4, but loading with TiO2 remarkably increased the methanol yield. Methanol yield over CuFe2O4/TiO2 was found to be about three times higher (651 μmol/gcat L) than that of CuFe2O4 photocatalyst. This occurs because the energy of the band excited electrons lies above the redox potentials of the reaction products CO2/CH3OH.
Abstract: It has been shown that BaFe12O19 is a perspective room-temperature multiferroic material. A large spontaneous polarization was observed for the BaFe12O19 ceramics revealing a clear ferroelectric hysteresis loop. The maximum polarization was estimated to be approximately 11.8 μC/cm2. The FeO6 octahedron in its perovskite-like hexagonal unit cell and the shift of Fe3+ off the center of octahedron are suggested to be the origin of the polarization in BaFe12O19. The magnetic field induced electric polarization has been also observed in the doped BaFe12-x-δScxMδO19 (δ=0.05) at 10 K and in the BaScxFe12−xO19 and SrScxFe12−xO19 (x = 1.3–1.7) M-type hexaferrites. The investigated BaFe12-xDxO19 (x=0.1, D-Al3+, In3+) samples have been obtained by two-step “topotactic” reactions. The powder neutron investigations of the samples were performed by neutron time of flight method at High Resolution Fourier Diffractometer.
Abstract: Fenton oxidation technology is the general strategy for the treatment of organic compounds-contained wastewater. However, a considerable amount of ferric sludge was produced during the Fenton process as secondary wastes, which were needed to be further removed from the effluent and treated. In this study, heterogeneous catalysts based on ferrite oxide (Cu-Fe-Ce-O) were synthesized and characterized, and their application for Fenton-like oxidation of simulated and actual radioactive organic wastewater was investigated. The results of TOC decomposition efficiency around 54% ~ 99% were obtained when the catalyst loading, H2O2 loading, pH, temperature, and reaction time were controlled. In this case, no secondary wastes formed and the given catalysts were able to be separated by magnetic devices and reused again.
Abstract: Partially lubricated sliding wear behaviour of a zinc-based alloy reinforced with 10wt% SiC particles has been studied as a function of applied load and solid lubricant particle size and has been compared with that of matrix alloy and conventionally used grey cast iron. The wear tests were conducted at the sliding velocities of 2.1m/sec in various partial lubricated conditions using pin on disc machine as per ASTM G-99-05. Base oil (SAE 20W-40) or mixture of the base oil with 5wt% graphite of particle sizes (7-10 µm) and (100 µm) were used for creating lubricated conditions. The matrix alloy revealed primary dendrites of a and eutectoid a + h and Î phases in the Inter dendritic regions. Similar microstructure has been depicted by the composite with an additional presence of the dispersoid SiC particles. In the case of cast iron, flakes of graphite were observed in the matrix; the latter comprised of (majority of) pearlite and (limited quantity of) ferrite. Results show a large improvement in wear resistance of the zinc-based alloy after reinforcement with SiC particles. The cast iron shows intermediate response between the matrix alloy and composite. The solid lubrication improved the wear resistance and friction behaviour of both the reinforced and base alloy. Moreover, minimum wear rate is obtained in oil+ 5wt % graphite (7-10 µm) lubricated environment for the matrix alloy and composite while for cast iron addition of solid lubricant increases the wear rate and minimum wear rate is obtained in case of oil lubricated environment. The cast iron experienced higher frictional heating than the matrix alloy and composite in all the cases especially at higher load condition. As far as friction coefficient is concerned, a mixed trend of behaviour was noted. The wear rate and frictional heating increased with load while friction coefficient was affected in an opposite manner. Test duration influenced the frictional heating and friction coefficient of the samples in a mixed manner.
Abstract: Low density polyethylene (LDPE) nanocomposites
with 3, 5 and 7 wt. % cobalt ferrite (CoFe2O4) nanopowder fabricated
with extrusion mixing and followed up by hot press to reach compact
samples. The transmission/reflection measurements were carried out
with a network analyzer in the frequency range of 8-12 GHz. By
increasing the percent of CoFe2O4 nanopowder, reflection loss (S11)
increases, while transferring loss (S21) decreases. Reflectivity (R)
calculations made using S11 and S21. Increase in percent of CoFe2O4
nanopowder up to 7 wt. % in composite leaded to higher reflectivity
amount, and revealed that increasing the percent of CoFe2O4
nanopowder up to 7 wt. % leads to further microwave absorption in
8-12 GHz range.
Abstract: NiFe2O4 (nickel ferrite), ZnFe2O4 (zinc ferrite) and
Ni0.5Zn0.5Fe2O4 (nickel-zinc ferrite) were prepared by
mechanochemical route in a planetary ball mill starting from mixture
of the appropriate quantities of the Ni(OH)2/Fe(OH)3,
Zn(OH)2/Fe(OH)3 and Ni(OH)2/Zn(OH)2/Fe(OH)3 hydroxide
powders. In order to monitor the progress of chemical reaction and
confirm phase formation, powder samples obtained after 25 h, 18 h
and 10 h of milling were characterized by X-ray diffraction (XRD),
transmission electron microscopy (TEM), IR, Raman and Mössbauer
spectroscopy. It is shown that the soft mechanochemical method, i.e.
mechanochemical activation of hydroxides, produces high quality
single phase ferrite samples in much more efficient way. From the IR
spectroscopy of single phase samples it is obvious that energy of
modes depends on the ratio of cations. It is obvious that all samples
have more than 5 Raman active modes predicted by group theory in
the normal spinel structure. Deconvolution of measured spectra
allows one to conclude that all complex bands in the spectra are made
of individual peaks with the intensities that vary from spectrum to
spectrum. The deconvolution of Raman spectra allows to separate
contributions of different cations to a particular type of vibration and
to estimate the degree of inversion.
Abstract: The ferrites ZnFe2O4, CdFe2O4 and CuFe2O4 are
synthesized in laboratory conditions using ceramic technology. Their
homogeneity and structure are proven by X-Ray diffraction analysis
and Mössbauer spectroscopy. The synthesized ferrites are subjected
to strong acid and high temperature leaching with solutions of H2SO4,
HCl and HNO3. The results indicate that the highest degree of
leaching of Zn, Cd and Cu from the ferrites is achieved by use of
HCl. The charging of five zinc sulfide concentrates was optimized using
the criterion of minimal amount of zinc ferrite produced when
roasting the concentrates in a fluidized bed. The results obtained are
interpreted in terms of the hydrometallurgical zinc production and
maximum recovery of zinc, copper and cadmium from initial zinc
concentrates after their roasting.
Abstract: The conventional ceramic route was utilized to
prepare a hard magnetic powder (M-type strontium ferrite,
SrFe12O19). The stoichiometric mixture of iron oxide and strontium
carbonate were calcined at 1000oC and then fired at various
temperatures. The influence of various reaction parameters such as
mixing ratio, calcination temperature, firing temperature and firing
time on the magnetic behaviors of the synthesized magnetic powder
were investigated. The magnetic properties including Coercivity
(Hc), Magnetic saturation (Ms), and Magnetic remnance (Mr) were
measured by vibrating sample magnetometer. Morphologically the
produced magnetic powder has a dense hexagonal grain shape
structure.
Abstract: The synthesis of CuFe2O4 spinel powders by an
optimized combustion-like process followed by calcination is
described herein. The samples were characterized using X-ray
diffraction (XRD), differential thermal analysis (TG/DTA), scanning
electron microscopy (SEM), dilatometry and 4-probe DC methods.
Different glycine to nitrate (G/N) ratios of 1 (fuel-deficient), 1.48
(stoichiometric) and 2 (fuel-rich) were employed. Calcining the asprepared
powders at 800 and 1000°C for 5 hours showed that the G/N
ratio of 2 results in the formation of the desired copper spinel single
phase at both calcination temperatures. For G/N=1, formation of
CuFe2O4 takes place in three steps. First, iron and copper nitrates
decompose to iron oxide and pure copper. Then, copper transforms to
copper oxide and finally, copper and iron oxides react with each other
to form a copper ferrite spinel phase. The electrical conductivity and
the coefficient of thermal expansion of the sintered pelletized
samples were 2 S.cm-1 (800°C) and 11×10-6 °C-1 (25-800°C),
respectively.
Abstract: Many industrial materials like magnets need to be
tested for the radiation environment expected at linear colliders (LC)
where the accelerator and detectors will be subjected to large
influences of beta, neutron and gamma’s over their life Gamma
irradiation of the permanent sample magnets using a 60Co source was
investigated up to an absorbed dose of 700Mrad shows a negligible
effect on some magnetic properties of Nd-Fe-B. In this work it has
been tried to investigate the change of some important properties of
Barium hexa ferrite. Results showed little decreases of magnetic
properties at doses rang of 0.5 to 2.5 Mrad. But at the gamma
irradiation dose up to 10 Mrad it is showed a few increase of
properties. Also study of gamma irradiation of Nd-Fe-B showed
considerably increase of magnetic properties.
Abstract: It is well known that in recent years magnetic
materials have received increased attention due to their properties.
For this reason a significant number of patents that were published
during the last decade are oriented towards synthesis and study of
such materials. The aim of this work is to create and study ferrite
nanocrystalline materials with spinel structure, using sol-gel
technology with participation of auto-combustion. This method is
perspective in that it is a cheap and low-temperature technique that
allows for the fine control on the product’s chemical composition.
Abstract: Micro-alloyed steel components are used in
automotive industry for the necessity to make the manufacturing
process cycles shorter when compared to conventional steel by
eliminating heat treatment cycles, so an important saving of costs and
energy can be reached by reducing the number of operations. Microalloying
elements like vanadium, niobium or titanium have been
added to medium carbon steels to achieve grain refinement with or
without precipitation strengthening along with uniform
microstructure throughout the matrix. Present study reports the
applicability of medium carbon vanadium micro-alloyed steel in hot
forging. Forgeability has been determined with respect to different
cooling rates, after forging in a hydraulic press at 50% diameter
reduction in temperature range of 900-11000C. Final microstructures,
hardness, tensile strength, and impact strength have been evaluated.
The friction coefficients of different lubricating conditions, viz.,
graphite in hydraulic oil, graphite in furnace oil, DF 150 (Graphite,
Water-Based) die lubricant and dry or without any lubrication were
obtained from the ring compression test for the above micro-alloyed
steel. Results of ring compression tests indicate that graphite in
hydraulic oil lubricant is preferred for free forging and dry lubricant
is preferred for die forging operation. Exceptionally good forgeability
and high resistance to fracture, especially for faster cooling rate has
been observed for fine equiaxed ferrite-pearlite grains, some amount
of bainite and fine precipitates of vanadium carbides and
carbonitrides. The results indicated that the cooling rate has a
remarkable effect on the microstructure and mechanical properties at
room temperature.
Abstract: Composite material based on Fe3Si micro-particles
and Mn-Zn nano-ferrite was prepared using powder metallurgy
technology. The sol-gel followed by autocombustion process was
used for synthesis of Mn0.8Zn0.2Fe2O4 ferrite. 3 wt.% of mechanically
milled ferrite was mixed with Fe3Si powder alloy. Mixed micro-nano
powder system was homogenized by the Resonant Acoustic Mixing
using ResodynLabRAM Mixer. This non-invasive homogenization
technique was used to preserve spherical morphology of Fe3Si
powder particles. Uniaxial cold pressing in the closed die at pressure
600 MPa was applied to obtain a compact sample. Microwave
sintering of green compact was realized at 800°C, 20 minutes, in air.
Density of the powders and composite was measured by
Hepycnometry. Impulse excitation method was used to measure
elastic properties of sintered composite. Mechanical properties were
evaluated by measurement of transverse rupture strength (TRS) and
Vickers hardness (HV). Resistivity was measured by 4 point probe
method. Ferrite phase distribution in volume of the composite was
documented by metallographic analysis.
It has been found that nano-ferrite particle distributed among
micro- particles of Fe3Si powder alloy led to high relative density
(~93%) and suitable mechanical properties (TRS >100 MPa, HV
~1GPa, E-modulus ~140 GPa) of the composite. High electric
resistivity (R~6.7 ohm.cm) of prepared composite indicate their
potential application as soft magnetic material at medium and high
frequencies.
Abstract: Magnetic powder of Sr-ferrite was prepared by
conventional and sol-gel auto-combustion methods. In conventional
method, strontium carbonate and ferric oxide powders were mixed
together and then mixture was calcined. In sol-gel auto-combustion
method, a solution containing strontium nitrate, ferric nitrate and
citric acid was heated until the combustion took place automatically;
then, as-burnt powder was calcined. Thermal behavior, phase
identification, morphology and magnetic properties of powders
obtained by these two methods were compared by DTA, XRD, SEM
and VSM techniques. According to the results of DTA analysis,
formation temperature of Sr-ferrite obtained by conventional and solgel
auto-combustion methods were 1300°C and 1000°C, respectively.
XRD results confirmed the formation of pure Sr-ferrite at the
mentioned temperatures. Plate and hexagonal-shape particles of Srferrite
were observed using SEM. The Sr-ferrite powder obtained by
sol-gel auto-combustion method had saturation magnetization of
66.03 emu/g and coercivity of 5731 Oe in comparison with values of
58.20 emu/g and 4378 Oe obtained by conventional method.