Abstract: The present work is dealing with 2% Si-steel alloy. The alloy contains 0.05% C as well as 0.85% Al. The alloy under investigation would be used for electrical transformation purposes. A heating (expansion) - cooling (contraction) dilation investigation was executed to detect the a, a+g, and g transformation temperatures at the inflection points of the dilation curve. On heating, primary a was detected at a temperature range between room temperature and 687 oC. The domain of a+g was detected in the range between 687 oC and 746 oC. g phase exists in the closed g region at the range between 746 oC and 1043 oC. The domain of a phase appears again at a temperature range between 1043 and 1105 oC, and followed by secondary a at temperature higher than 1105 oC. A physical simulation of thermo-mechanical processing on the as-cast alloy was carried out. The simulation process took into consideration the hot flat rolling pilot plant parameters. The process was executed on the thermo-mechanical simulator (Gleeble 3500). The process was designed to include seven consecutive passes. The 1st pass represents the roughing stage, while the remaining six passes represent finish rolling stage. The whole process was executed at the temperature range from 1100 oC to 900 oC. The amount of strain starts with 23.5% at the roughing pass and decreases continuously to reach 7.5 % at the last finishing pass. The flow curve of the alloy can be abstracted from the stress-strain curves representing simulated passes. It shows alloy hardening from a pass to the other up to pass no. 6, as a result of decreasing the deformation temperature and increasing of cumulative strain. After pass no. 6, the deformation process enhances the dynamic recrystallization phenomena to appear, where the z-parameter would be high.
Abstract: Electron back-scattered diffraction was used to follow the evolution of microstructure from the base metal to the stir zone (SZ) in a duplex stainless steel subjected to friction stir welding. In the stir zone (SZ), a continuous dynamic recrystallization (CDRX) was evidenced for ferrite, while it was suggested that a static recrystallization together with CDRX may occur for austenite. It was found that ferrite and austenite grains in the SZ take a typical shear texture of bcc and fcc materials respectively.
Abstract: Superplastic deformation and high temperature load
relaxation behavior of coarse-grained iron aluminides with the
composition of Fe-28 at.% Al have been investigated. A series of load
relaxation and tensile tests were conducted at temperatures ranging
from 600 to 850oC. The flow curves obtained from load relaxation
tests were found to have a sigmoidal shape and to exhibit stress vs.
strain rate data in a very wide strain rate range from 10-7/s to 10-2/s.
Tensile tests have been conducted at various initial strain rates ranging
from 3×10-5/s to 1×10-2/s. Maximum elongation of ~500 % was
obtained at the initial strain rate of 3×10-5/s and the maximum strain
rate sensitivity was found to be 0.68 at 850oC in binary Fe-28Al alloy.
Microstructure observation through the optical microscopy (OM) and
the electron back-scattered diffraction (EBSD) technique has been
carried out on the deformed specimens and it has revealed the
evidences for grain boundary migration and grain refinement to occur
during superplastic deformation, suggesting the dynamic
recrystallization mechanism. The addition of Cr by the amount of 5
at.% appeared to deteriorate the superplasticity of the binary iron
aluminide. By applying the internal variable theory of structural
superplasticity, the addition of Cr has been revealed to lower the
contribution of the frictional resistance to dislocation glide during high
temperature deformation of the Fe3Al alloy.