Abstract: Catalytic wet air oxidation (CWAO) is normally carried out at elevated temperature and pressure. This work investigates the potential of NiO-CeO2 nano-catalyst in CWAO of paper industry wastewater under milder operating conditions of 90 °C and 1 atm. The NiO-CeO2 nano-catalysts were synthesized by a simple co-precipitation method and characterized by X-ray diffraction (XRD), before and after use, in order to study any crystallographic change during experiment. The extent of metal-leaching from the catalyst was determined using the inductively coupled plasma optical emission spectrometry (ICP-OES). The catalytic activity of nano-catalysts was studied in terms of total organic carbon (TOC), adsorbable organic halides (AOX) and chlorophenolics (CHPs) removal. Interestingly, mixed oxide catalysts exhibited higher activity than the corresponding single-metal oxides. The maximum removal efficiency was achieved with Ce40Ni60 catalyst. The results indicate that the CWAO process is efficient in removing the priority organic pollutants from wastewater, as it exhibited up to 59% TOC, 55% AOX, and 54 % CHPs removal.
Abstract: Preparation of nanoparticles of cerium oxide and
adsorption of bovine serum albumin on them were studied. Particle
size distribution and influence of pH on zeta potential of prepared
CeO2 were determined. Average size of prepared cerium oxide
nanoparticles was 9 nm. The simultaneous measurements of the
bovine serum albumin adsorption and zeta potential determination of
the (adsorption) suspensions were carried out. The adsorption
isotherms were found to be of typical Langmuir type; values of the
bovine serum albumin adsorption capacities were calculated.
Increasing of pH led to decrease of zeta potential and decrease of
adsorption capacity of cerium oxide nanoparticles. The maximum
adsorption capacity was found for strongly acid suspension (am =
118 mg/g). The samples of nanoceria with positive zeta potential
adsorbed more bovine serum albumin on the other hand, the samples
with negative zeta potential showed little or no protein adsorption.
Surface charge or better say zeta potential of CeO2 nanoparticles
plays the key role in adsorption of proteins on such type of materials.
Abstract: The value of emission factor was calculated in the
older type of Diesel engine operating on an engine testing bench and
then compared with the parameters monitored under similar
conditions when the EnviroxTM additive was applied. It has been
found out that the additive based on CeO2 nanoparticles reduces
emission of NOx. The dependencies of NOx emissions on reduced
torque, engine power and revolutions have been observed as well.
Abstract: Cerium oxide is to be recovered from monazite,
which contains about 27.35% CeO2. The principal objective
of this study is to be able to extract cerium oxide from
monazite of Moemeik Myitsone Area. The treatment of
monazite in this study involves three main steps; extraction
of cerium hydroxide from monazite, solvent extraction of
cerium hydroxide, and precipitation with oxalic acid and
calcination of cerium oxalate.
Abstract: In this study, oxidative steam reforming of methanol (OSRM) over a Au/CeO2–Fe2O3 catalyst prepared by a depositionprecipitation (DP) method was studied to produce hydrogen in order to feed a Proton Exchange Membrane Fuel Cell (PEMFC). The support (CeO2, Fe2O3, and CeO2–Fe2O3) were prepared by precipitation and co-precipitation methods. The impact of the support composition on the catalytic performance was studied by varying the Ce/(Ce+Fe) atomic ratio, it was found that the 1%Au/CF(0.25) calcined at 300 °C exhibited the highest catalytic activity in the whole temperature studied. In addition, the effect of Au content was investigated and 3%Au/CF(0.25) exhibited the highest activity under the optimum condition in the temperature range of 200 °C to 400 °C. The catalysts were characterized by various techniques: XRD, TPR, XRF, and UV-vis.
Abstract: The leaching behavior and structure of Li2O-CeO2- Fe2O3-P2O5 glasses incorporated with simulated high level nuclear wastes (HLW) were studied. The leach rates of gross and each constituent element were determined from the total weight loss of the specimen and the leachate analyses by inductively coupled argon plasma spectroscopy (ICP). The gross leach rate of the 4.5Li2O- 9.7CeO2-34.7Fe2O3-51.5P2O5 glass waste form containing 45 mass% simulated HLW is of the order of 10