Abstract: In this work new macroporous Ni electrodes modified
with Au nanoparticles for hydrogen production have been developed.
The supporting macroporous Ni electrodes have been obtained by
means of the electrodeposition at high current densities. Then, the Au
nanoparticles were synthesized and added to the electrode surface.
The electrocatalytic behaviour of the developed electrocatalysts was
studied by means of pseudo-steady-state polarization curves,
electrochemical impedance spectroscopy (EIS) and hydrogen
discharge curves. The size of the Au synthetized nanoparticles shows
a monomodal distribution, with a very sharp band between 10 and 50
nm. The characteristic parameters d10, d50 and d90 were 14, 20 and
31 nm respectively. From Tafel polarization data has been concluded
that the Au nanoparticles improve the catalytic activity of the
developed electrodes towards the HER respect to the macroporous Ni
electrodes. EIS permits to obtain the electrochemically active area by
means of the roughness factor value. All the developed electrodes
show roughness factor values in the same order of magnitude. From
the activation energy results it can be concluded that the Au
nanoparticles improve the intrinsic catalytic activity of the
macroporous Ni electrodes.
Abstract: Chitosan functionalized Fe3O4-Au core shell
nanoparticles have been prepared using a two-step wet chemical
approach using NaBH4 as reducing agent for formation of Au in
ethylene glycol. X-ray diffraction studies shows individual phases of
Fe3O4 and Au in the as prepared samples with crystallite size of 5.9
and 11.4 nm respectively. The functionalization of the core-shell
nanostructure with Chitosan has been confirmed using Fourier
transform infrared spectroscopy along with signatures of octahedral
and tetrahedral sites of Fe3O4 below 600cm-1. Mössbauer
spectroscopy shows decrease in particle-particle interaction in
presence of Au shell (72% sextet) than pure oleic coated Fe3O4
nanoparticles (88% sextet) at room temperature. At 80K, oleic acid
coated Fe3O4 shows only sextets whereas the Chitosan functionalized
Fe3O4 and Chitosan functionalized Fe3O4@Au core shell show
presence of 5 and 11% doublet, respectively.
Abstract: The use of magnetic and magnetic/gold core/shell
nanoparticles in biotechnology or medicine has shown good promise
due to their hybrid nature which possesses superior magnetic and
optical properties. Some of these potential applications include
hyperthermia treatment, bio-separations, diagnostics, drug delivery
and toxin removal. Synthesis refinement to control geometric and
magnetic/optical properties, and finding functional surfactants for
biomolecular attachment, are requirements to meet application
specifics.
Various high-temperature preparative methods were used for the
synthesis of iron oxide and gold-coated iron oxide nanoparticles.
Different surface functionalities, such as 11-aminoundecanoic and
11-mercaptoundecanoic acid, were introduced on the surface of the
particles to facilitate further attachment of biomolecular functionality
and drug-like molecules. Nanoparticle thermal stability, composition,
state of aggregation, size and morphology were investigated and the
results from techniques such as Fourier Transform-Infra Red
spectroscopy (FT-IR), Ultraviolet visible spectroscopy (UV-vis),
Transmission Electron Microscopy (TEM) and thermal analysis are
discussed.
Abstract: Mercury is a natural occurring element and present in
various concentrations in the environment. Due to its toxic effects, it
is desirable to research mercury sensitive materials to adsorb
mercury. This paper describes the preparation of Au nanoparticles for
mercury adsorption by using a microwave (MW)-polyol method in
the presence of three different Sodium Chloride (NaCl)
concentrations (10, 20 and 30 mM). Mixtures of spherical, triangular,
octahedral, decahedral particles and 1-D product were obtained using
this rapid method. Sizes and shapes was found strongly depend on the
concentrations of NaCl. Without NaCl concentration, spherical,
triangular plates, octahedral, decahedral nanoparticles and 1D
product were produced. At the lower NaCl concentration (10 mM),
spherical, octahedral and decahedral nanoparticles were present,
while spherical and decahedral nanoparticles were preferentially form
by using 20 mM of NaCl concentration. Spherical, triangular plates,
octahedral and decahedral nanoparticles were obtained at the highest
NaCl concentration (30 mM). The amount of mercury adsorbed using
20 ppm mercury solution is the highest (67.5 %) for NaCl
concentration of 30 mM. The high yield of polygonal particles will
increase the mercury adsorption. In addition, the adsorption of
mercury is also due to the sizes of the particles. The sizes of particles
become smaller with increasing NaCl concentrations (size ranges, 5-
16 nm) than those synthesized without addition of NaCl (size ranges
11-32 nm). It is concluded that NaCl concentrations affects the
formation of sizes and shapes of Au nanoparticles thus affects the
mercury adsorption.
Abstract: Particle detection in very noisy and low contrast images
is an active field of research in image processing. In this article, a
method is proposed for the efficient detection and sizing of subsurface
spherical particles, which is used for the processing of softly fused
Au nanoparticles. Transmission Electron Microscopy is used for
imaging the nanoparticles, and the proposed algorithm has been
tested with the two-dimensional projected TEM images obtained.
Results are compared with the data obtained by transmission optical
spectroscopy, as well as with conventional circular object detection
algorithms.