Abstract: In this investigation, a hypoeutectic AlSi11Cu alloy was printed. This alloy was obtained in powder form with an average particle size of 40 µm. Bars 20 mm in diameter and 100 mm in length were printed with the building direction parallel to the bars' longitudinal direction. The microstructural characterization demonstrated an Al matrix surrounded by a Si network forming a coral-like pattern. The microstructure of the alloy showed a heterogeneous behavior with a mixture of columnar and equiaxed grains. Likewise, the texture indicated that the columnar grains were preferentially oriented towards the building direction, while the equiaxed followed a texture dominated by the cube component. On the other hand, the as-printed material strength showed higher values than those obtained in the same alloy using conventional processes such as casting. In addition, strength and ductility differences were found in the printed material, depending on the measurement direction. The highest values were obtained in the radial direction (565 MPa maximum strength and 4.8% elongation to failure). The lowest values corresponded to the transverse direction (508 MPa maximum strength and 3.2 elongation to failure), which corroborate the material anisotropy.
Abstract: Electrical resistivity investigation was conducted in vicinity of Tarbela Ghazi, in order to study the subsurface layer with a view of determining the depth to the aquifer and thickness of groundwater potential zones. Vertical Electrical Sounding (VES) using Schlumberger array was carried out at 16 VES stations. Well logging data at four tube wells have been used to mark the super saturated zones with great discharge rate. The present paper shows a geoelectrical identification of the lithology and an estimate of the relationship between the resistivity and Dar Zarrouk parameters (transverse unit resistance and longitudinal unit conductance). The VES results revealed both homogeneous and heterogeneous nature of the subsurface strata. Aquifer is unconfined to confine in nature, and at few locations though perched aquifer has been identified, groundwater potential zones are developed in unconsolidated deposits layers and more than seven geo-electric layers are observed at some VES locations. Saturated zones thickness ranges from 5 m to 150 m, whereas at few area aquifer is beyond 150 m thick. The average anisotropy, transvers resistance and longitudinal conductance values are 0.86 %, 35750.9821 Ω.m2, 0.729 Siemens, respectively. The transverse unit resistance values fluctuate all over the aquifer system, whereas below at particular depth high values are observed, that significantly associated with the high transmissivity zones. The groundwater quality in all analyzed samples is below permissible limit according to World Health Standard (WHO).
Abstract: The crystal orientation is a factor that affects the microscopic material properties. Crystal orientation determines the anisotropy of the polycrystalline material. And it is closely related to the mechanical properties of the material. In this paper, for pure copper polycrystalline material, two different methods; X-Ray Diffraction (XRD) and Electron Backscatter Diffraction (EBSD); and the crystal orientation were analyzed. In the latter method, it is possible that the X-ray beam diameter is thicker as compared to the former, to measure the crystal orientation macroscopically relatively. By measurement of the above, we investigated the change in crystal orientation and internal tissues of pure copper.
Abstract: This paper is a continuation of the work carried out by various turbulence modelers in Oceanography on the topic of oceanic turbulent mixing. It evaluates the evolution of ocean water temperature and salinity by the appropriate modeling of turbulent mixing utilizing proper prescription of eddy viscosity. Many modelers in past have suggested including terms like shear, buoyancy and vorticity to be the parameters that decide the slow pressure strain correlation. We add to it the fact that dissipation anisotropy also modifies the correlation through eddy viscosity parameterization. This recalibrates the established correlation constants slightly and gives improved results. This anisotropization of dissipation implies that the critical Richardson’s number increases much beyond unity (to 1.66) to accommodate enhanced mixing, as is seen in reality. The model is run for a couple of test cases in the General Ocean Turbulence Model (GOTM) and the results are presented here.
Abstract: Eddy viscosity models in turbulence modeling can be mainly classified as linear and nonlinear models. Linear formulations are simple and require less computational resources but have the disadvantage that they cannot predict actual flow pattern in complex geophysical flows where streamline curvature and swirling motion are predominant. A constitutive equation of Reynolds stress anisotropy is adopted for the formulation of eddy viscosity including all the possible higher order terms quadratic in the mean velocity gradients, and a simplified model is developed for actual oceanic flows where only the vertical velocity gradients are important. The new model is incorporated into the one dimensional General Ocean Turbulence Model (GOTM). Two realistic oceanic test cases (OWS Papa and FLEX' 76) have been investigated. The new model predictions match well with the observational data and are better in comparison to the predictions of the two equation k-epsilon model. The proposed model can be easily incorporated in the three dimensional Princeton Ocean Model (POM) to simulate a wide range of oceanic processes. Practically, this model can be implemented in the coastal regions where trasverse shear induces higher vorticity, and for prediction of flow in estuaries and lakes, where depth is comparatively less. The model predictions of marine turbulence and other related data (e.g. Sea surface temperature, Surface heat flux and vertical temperature profile) can be utilized in short term ocean and climate forecasting and warning systems.
Abstract: Conditions corresponding to the unconditional stability
of convection in a mechanically anisotropic fluid saturated porous
medium of infinite horizontal extent are determined. The medium
is heated from below and its bounding surfaces are subjected to
temperature modulation which consists of a steady part and a
time periodic oscillating part. The Brinkman model is employed
in the momentum equation with the Bousinessq approximation.
The stability region is found for arbitrary values of modulational
frequency and amplitude using the energy method. Higher order
numerical computations are carried out to find critical boundaries
and subcritical instability regions more accurately.
Abstract: The paper presents the results of a detailed assessment of several modern Reynolds Averaged Navier-Stokes (RANS) turbulence models for prediction of C3X vane film cooling at various injection regimes. Three models are considered, namely the Shear Stress Transport (SST) model, the modification of the SST model accounting for the streamlines curvature (SST-CC), and the Explicit Algebraic Reynolds Stress Model (EARSM). It is shown that all the considered models face with a problem in prediction of the adiabatic effectiveness in the vicinity of the cooling holes; however, accounting for the Reynolds stress anisotropy within the EARSM model noticeably increases the solution accuracy. On the other hand, further downstream all the models provide a reasonable agreement with the experimental data for the adiabatic effectiveness and among the considered models the most accurate results are obtained with the use EARMS.
Abstract: Anisotropy is one of the major aspects that affect soil behavior, and extensive efforts have investigated its effect on the mechanical properties of soil. However, very little attention has been given to the combined effect of anisotropy and fine contents. Therefore, in this paper, the anisotropic strength of sand containing different fine content (F) of 5%, 10%, 15%, and 20%, was investigated using hollow cylinder tests under different principal stress directions of α = 0° and α = 90°. For a given principal stress direction (α), it was found that increasing fine content resulted in decreasing deviator stress (q). Moreover, results revealed that all fine contents showed anisotropic strength where there is a clear difference between the strength under 0° and the strength under 90°. This anisotropy was greatest under F = 5% while it decreased with increasing fine contents, particularly at F = 10%. Mixtures with low fine content show low contractive behavior and tended to show more dilation. Moreover, all sand-clay mixtures exhibited less dilation and more compression at α = 90° compared with that at α = 0°.
Abstract: Earing defect in drawing process is highly undesirable not only because it adds on an additional trimming operation but also because the uneven material flow demands extra care. The objective of this work is to study the earing problem in the Deep Drawing of circular cup and to optimize the blank shape to reduce the earing. A finite element model is developed for 3-D numerical simulation of cup forming process in ABAQUS. Extra-deep-drawing (EDD) steel sheet has been used for simulation. Properties and tool design parameters were used as input for simulation. Earing was observed in the simulated cup and it was measured at various angles with respect to rolling direction. To reduce the earing defect initial blank shape was modified with the help of anisotropy coefficient. Modified blanks showed notable reduction in earing.
Abstract: The morphotropic phase boundary (MPB) recently has attracted constant interest in ferromagnetic systems for obtaining enhanced large magnetoelastic response. In the present study, structural and magnetoelastic properties of MPB involved ferromagnetic Tb1-xGdxFe2 (0≤x≤1) system has been investigated. The change of easy magnetic direction from to with increasing x up MPB composition of x=0.9 is detected by step-scanned [440] synchrotron X-ray diffraction reflections. The Gd substitution for Tb changes the composition for the anisotropy compensation near MPB composition of x=0.9, which was confirmed by the analysis of detailed scanned XRD, magnetization curves and the calculation of the first anisotropy constant K1. The spin configuration diagram accompanied with different crystal structures for Tb1-xGdxFe2 was designed. The calculated first anisotropy constant K1 shows a minimum value at MPB composition of x=0.9. In addition, the large ratio between magnetostriction, and the absolute values of the first anisotropy constant │λS∕K1│ appears at MPB composition, which makes it a potential material for magnetostrictive application. Based on experimental results, a theoretically approach was also proposed to signify that the facilitated magnetization rotation and enhanced magnetoelastic effect near MPB composition are a consequence of the anisotropic flattening of free energy of ferromagnetic crystal. Our work specifies the universal existence of MPB in ferromagnetic materials which is important for substantial improvement of magnetic and magnetostrictive properties and may provide a new route to develop advanced functional materials.
Abstract: The corrosion behaviour of 316L stainless steel coatings obtained by cold spray method was investigated in this study. 316L powders were deposited onto Al5052 aluminum substrates. The coatings were produced using nitrogen (N2) process gas. In order to further improve the corrosion and mechanical properties of the coatings, heat treatment was applied at 250 and 750 °C. The corrosion performances of the coatings were compared using the potentiodynamic scanning (PDS) technique under in-vitro conditions (in Ringer’s solution at 37 °C). In addition, the hardness and porosity tests were carried out on the coatings. Microstructural characterization of the coatings was carried out by using scanning electron microscopy attached with energy dispersive spectrometer (SEM-EDS) and X-ray diffraction (XRD) technique. It was found that clean surfaces and a good adhesion were achieved for particle/substrate bonding. The heat treatment process provided both elimination of the anisotropy in the coating and resulting in healing-up of the incomplete interfaces between the deposited particles. It was found that the corrosion potential of the annealed coatings at 750 °C was higher than that of commercially 316 L stainless steel. Moreover, the microstructural investigations after the corrosion tests revealed that corrosion preferentially starts at inter-splat boundaries.
Abstract: This paper presents an experimental characterization of the anisotropic mechanical behavior of 4 textile woven fabrics with different weaves (Twill 3, Plain, Twill4 and Satin 4) by off-axis tensile testing. These tests are applied according seven directions oriented by 15° increment with respect to the warp direction. Fixed and articulated jaws are used. Analysis of experimental results is done through global (Effort/Elongation curves) and local scales. Global anisotropy was studied from the Effort/Elongation curves: shape, breaking load (Frup), tensile elongation (EMT), tensile energy (WT) and linearity index (LT). Local anisotropy was studied from the measurement of strain tensor components in the central area of the specimen as a function of testing orientation and effort: longitudinal strain ɛL, transverse strain ɛT and shearing ɛLT. The effect of used jaws is also analyzed.
Abstract: In the present work, forming limit diagrams and strain
distribution profile diagrams for extra deep drawing steel at room and
elevated temperatures have been determined experimentally by
conducting stretch forming experiments by using designed and
fabricated warm stretchforming tooling setup. With the help of
forming Limit Diagrams (FLDs) and strain, distribution profile
diagrams the formability of Extra Deep Drawing steel has been
analyzed and co-related with mechanical properties like strain
hardening COEFFICIENT (n) and normal anisotropy (r−). Mechanical
properties of EDD steel from room temperature to 4500C were
determined and discussed the impact of temperature on the properties
like work hardening exponent (n) anisotropy (r-) and strength
coefficient of the material. In addition, the fractured surfaces after
stretching have undergone the some metallurgical investigations and
attempt has been made to co-relate with the formability of EDD steel
sheets. They are co-related and good agreement with FLDs at various
temperatures.
Abstract: Evaluation of the excavation-induced ground
movements is an important design aspect of support systems in urban
areas. Geological and geotechnical conditions of an excavation area
have significant effects on excavation-induced ground movements and
the related damage. This paper is aimed at studying the performance of
excavation walls supported by nails in jointed rock medium. The
performance of nailed walls is investigated based on evaluating the
excavation-induced ground movements. For this purpose, a set of
calibrated 2D finite element models are developed by taking into
account the nail-rock-structure interactions, the anisotropic properties
of jointed rock, and the staged construction process. The results of this
paper highlight effects of different parameters such as joint
inclinations, anisotropy of rocks and nail inclinations on deformation
parameters of excavation wall supported by nails.
Abstract: Radiative heat transfer in participating medium was
carried out using the finite volume method. The radiative transfer
equations are formulated for absorbing and anisotropically scattering
and emitting medium. The solution strategy is discussed and the
conditions for computational stability are conferred. The equations
have been solved for transient radiative medium and transient
radiation incorporated with transient conduction. Results have been
obtained for irradiation and corresponding heat fluxes for both the
cases. The solutions can be used to conclude incident energy and
surface heat flux. Transient solutions were obtained for a slab of heat
conducting in slab and by thermal radiation. The effect of heat
conduction during the transient phase is to partially equalize the
internal temperature distribution. The solution procedure provides
accurate temperature distributions in these regions. A finite volume
procedure with variable space and time increments is used to solve
the transient radiation equation. The medium in the enclosure
absorbs, emits, and anisotropically scatters radiative energy. The
incident radiations and the radiative heat fluxes are presented in
graphical forms. The phase function anisotropy plays a significant
role in the radiation heat transfer when the boundary condition is
non-symmetric.
Abstract: In this work, the plastic behaviour of cold-rolled zinc
coated dual-phase steel sheets DP600 and DP800 grades is firstly
investigated with the help of uniaxial, hydraulic bulge and Forming
Limit Curve (FLC) tests. The uniaxial tensile tests were performed in
three angular orientations with respect to the rolling direction to
evaluate the strain-hardening and plastic anisotropy. True stressstrain
curves at large strains were determined from hydraulic bulge
testing and fitted to a work-hardening equation. The limit strains are
defined at both localized necking and fracture conditions according to
Nakajima’s hemispherical punch procedure. Also, an elasto-plastic
localization model is proposed in order to predict strain and stress
based forming limit curves. The investigated dual-phase sheets
showed a good formability in the biaxial stretching and drawing FLC
regions. For both DP600 and DP800 sheets, the corresponding
numerical predictions overestimated and underestimated the
experimental limit strains in the biaxial stretching and drawing FLC
regions, respectively. This can be attributed to the restricted failure
necking condition adopted in the numerical model, which is not
suitable to describe the tensile and shear fracture mechanisms in
advanced high strength steels under equibiaxial and biaxial stretching
conditions.
Abstract: In this paper, we investigated the athermal pressure
behavior of the structural and elastic properties of scheelite BaWO4
phase up to 7 GPa using the ab initio pseudo-potential method. The
calculated lattice parameters pressure relation have been compared
with the experimental values and found to be in good agreement with
these results. Moreover, we present for the first time the investigation
of the elastic properties of this compound using the density functional
perturbation theory (DFPT). It is shown that this phase is
mechanically stable up to 7 GPa after analyzing the calculated elastic
constants. Other relevant quantities such as bulk modulus, pressure
derivative of bulk modulus, shear modulus; Young’s modulus,
Poisson’s ratio, anisotropy factors, Debye temperature and sound
velocity have been calculated. The obtained results, which are
reported for the first time to the best of the author’s knowledge, can
facilitate assessment of possible applications of the title material.
Abstract: A new method for determining the distribution of
birefringence and linear dichroism in optical polymer materials is
presented. The method is based on the use of polarizationholographic
diffraction grating that forms an orthogonal circular basis
in the process of diffraction of probing laser beam on the grating. The
intensities ratio of the orders of diffraction on this grating enables the
value of birefringence and linear dichroism in the sample to be
determined. The distribution of birefringence in the sample is
determined by scanning with a circularly polarized beam with a
wavelength far from the absorption band of the material. If the
scanning is carried out by probing beam with the wavelength near to
a maximum of the absorption band of the chromophore then the
distribution of linear dichroism can be determined. An appropriate
theoretical model of this method is presented. A laboratory setup was
created for the proposed method. An optical scheme of the laboratory
setup is presented. The results of measurement in polymer films with
two-dimensional gradient distribution of birefringence and linear
dichroism are discussed.
Abstract: The calcarenites carbonate rocks of the Quaternary ridges, which extend along the northwestern Mediterranean coastal plain of Egypt, represent an excellent model for the transformation of loose sediments to real sedimentary rocks by the different stages of meteoric diagenesis. The depositional and diagenetic fabrics of the rocks, in addition to the strata orientation, highly affect their ultimate compressive strength and other geotechnical properties.
There is a marked increase in the compressive strength (UCS) from the first to the fourth ridge rock samples. The lowest values are related to the loose packing, weakly cemented aragonitic ooid sediments with high porosity, besides the irregularly distributed of cement, which result in decreasing the ability of these rocks to withstand crushing under direct pressure. The high (UCS) values are attributed to the low porosity, the presence of micritic cement, the reduction in grain size and the occurrence of micritization and calcretization processes.
The strata orientation has a notable effect on the measured (UCS). The lowest values have been recorded for the samples cored in the inclined direction; whereas the highest values have been noticed in most samples cored in the vertical and parallel directions to bedding plane. In case of the inclined direction, the bedding planes were oriented close to the plane of maximum shear stress. The lowest and highest anisotropy values have been recorded for the first and the third ridges rock samples, respectively, which may attributed to the relatively homogeneity and well sorted grainstone of the first ridge rock samples, and relatively heterogeneity in grain and pore size distribution and degree of cementation of the third ridge rock samples, besides, the abundance of shell fragments with intraparticle pore spaces, which may produce lines of weakness within the rock.
Abstract: This article is concerned with the determination of the static interaction of a vertically loaded rigid circular disc embedded at the interface of a horizontal layer sandwiched in between two different transversely isotropic half-spaces called as tri-material full-space. The axes of symmetry of different regions are assumed to be normal to the horizontal interfaces and parallel to the movement direction. With the use of a potential function method, and by implementing Hankel integral transforms in the radial direction, the government partial differential equation for the solely scalar potential function is transformed to an ordinary 4th order differential equation, and the mixed boundary conditions are transformed into a pair of integral equations called dual integral equations, which can be reduced to a Fredholm integral equation of the second kind, which is solved analytically. Then, the displacements and stresses are given in the form of improper line integrals, which is due to inverse Hankel integral transforms. It is shown that the present solutions are in exact agreement with the existing solutions for a homogeneous full-space with transversely isotropic material. To confirm the accuracy of the numerical evaluation of the integrals involved, the numerical results are compared with the solutions exists for the homogeneous full-space. Then, some different cases with different degrees of material anisotropy are compared to portray the effect of degree of anisotropy.