Abstract: The influence of SiC powder addition on densification of Al-SiC compacts during sintering in different atmospheres was investigated. It was performed in a dilatometer in flowing nitrogen, nitrogen/hydrogen (95/5 by volume) and argon. Fine, F500 grade of SiC powder was used. Mixtures containing 10 and 30 vol.% of SiC reinforcement were prepared in a Turbula mixer. Green compacts of about 82% of theoretical density were made of each mixture. For comparison, compacts made of pure aluminum powder were also investigated. It was shown that nitrogen is the best sintering atmosphere because only in this atmosphere did shrinkage take place. Its amount is lowered by ceramic powder addition, i.e. the more SiC the less densification occurs. Additionally, the formation of clusters, enhanced in compacts containing 30 vol.% SiC, is also responsible for limiting the shrinkage. Microstructural examinations of sintered composites revealed that sintering of compacts occurs in the presence of the liquid phase exclusively in nitrogen.
Abstract: Particulate reinforced metal matrix composites
(MMCs) are potential materials for various applications due to their
advantageous of physical and mechanical properties. This paper
presents a study on the performance of stir cast Al2O3 SiC reinforced
metal matrix composite materials. The results indicate that the
composite materials exhibit improved physical and mechanical
properties, such as, low coefficient of thermal expansion, high
ultimate tensile strength, high impact strength, and hardness. It has
been found that with the increase of weight percentage of
reinforcement particles in the aluminium metal matrix, the new
material exhibits lower wear rate against abrasive wearing. Being
extremely lighter than the conventional gray cast iron material, the
Al-Al2O3 and Al-SiC composites could be potential green materials
for applications in the automobile industry, for instance, in making
car disc brake rotors.