Abstract: Acid leaching of flotation concentrate of oxide copper ore containing mainly of malachite was performed in a standard agitation tank with various parameters. The effects of solid to liquid ratio, sulfuric acid concentration, agitation speed, leaching temperature and time were examined to get proper conditions. The best conditions are 1:8 solid to liquid ratio, 10% concentration by weight, 250 rev/min, 30 oC and 5-min leaching time in respect. About 20% Cu grade assayed by atomic absorption technique with 98% copper recovery was obtained from these combined optimum conditions. Dissolution kinetics of the concentrate was approximated as a logarithmic function. As a result, the first-order reaction rate is suggested from this leaching study.
Abstract: The morphology, mineralogical and chemical
composition of a low-grade nickel ore from Mpumalanga, South
Africa, were studied by scanning electron microscope (SEM), X-ray
diffraction (XRD) and X-ray fluorescence (XRF), respectively. The
ore was subjected to atmospheric agitation leaching using sulphuric
acid to investigate the effects of acid concentration, leaching
temperature, leaching time and particle size on extraction of nickel
and cobalt. Analyses results indicated the ore to be a saprolitic nickel
laterite belonging to the serpentine group of minerals. Sulphuric acid
was found to be able to extract nickel from the ore. Increased acid
concentration and temperature only produced low amounts of nickel
but improved cobalt extraction. As high as 77.44% Ni was achieved
when leaching a -106+75μm fraction with 4.0M acid concentration at
25oC. The kinetics of nickel leaching from the saprolitic ore were
studied and the activation energy was determined to be 18.16kJ/mol.
This indicated that nickel leaching reaction was diffusion controlled.