Abstract: This paper presents the experimental results of salt fog ageing test of silicone rubber housing material for outdoor polymer insulator based on IEC 61109. Four types of HTV silicone rubber sheet with different amount of ATH were tested continuously 1000
Abstract: This paper presents the experimental results of silicone rubber housing material for 24kV lightning arrester under artificial accelerated ageing test based on IEC 61109 specifications. Specimens having inclined and alternated shed made of HTV silicone rubber with ATH content and having leakage distance 625 mm were tested continuously 1000 hrs in artificial salt fog chamber. After 1000 hrs of salt fog ageing test, obviously surface erosion was observed on trunk between the upper large shed and the lower small shed near the energized end. Decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Chemical analysis by ATR-FTIR confirmed the observation results.
Abstract: This paper presents the comparison ageing deterioration of silicone rubber housing material for outdoor polymer insulators by using salt fog ageing test based on IEC 61109 and outdoor exposure test.Four types of high temperature silicone vulcanized silicone rubber sheet with different amount of ATH were used as testing specimen. For salt fog ageing test, the specimens were tested continuously 1000 hours with energized in test chamber. For outdoor exposure test, the specimens were hung continuously 18 months without energized. Physical and chemical analyses were conducted to evaluate degree of ageing deterioration of tested specimens. Slightly surface erosion was observed on specimen surface after salt fog ageing test and no erosion was observed on surface of outdoor exposure specimen. However, comparable degree of ageing deterioration can be seen from surface analysis results.
Abstract: This paper presents the experimental results on
artificial ageing test of 22 kV XLPE cable for distribution system
application in Thailand. XLPE insulating material of 22 kV cable
was sliced to 60-70 μm in thick and was subjected to ac high voltage
at 23
Ôùª
C, 60
Ôùª
C and 75
Ôùª
C. Testing voltage was constantly applied to
the specimen until breakdown. Breakdown voltage and time to
breakdown were used to evaluate life time of insulating material.
Furthermore, the physical model by J. P. Crine for predicts life time
of XLPE insulating material was adopted as life time model and was
calculated in order to compare the experimental results. Acceptable
life time results were obtained from Crine-s model comparing with
the experimental result. In addition, fourier transform infrared
spectroscopy (FTIR) for chemical analysis and scanning electron
microscope (SEM) for physical analysis were conducted on tested
specimens.