Suitability of Newsprint and Kraft Papers as Materials for Cement Bonded Ceiling Board

The suitability of Newsprint and Kraft papers for the production of cement bonded ceiling board was investigated. Sample boards were produced from newsprint paper (100%), mixture of newsprint and Kraft paper (50:50) and Kraft paper (100%) at 1:1, 2:1 and 3:1 cement/paper mixing ratio respectively with 3% additive concentration of calcium chloride (CaCl2). Density, flexural and thickness swelling properties of the boards were investigated. The effects of paper type and mixing ratio on the physical and mechanical properties were also examined. The bending properties of the board which include Modulus of Elasticity (MOE) and Modulus of Rupture (MOR) increased linearly with increase in density. Modulus of rupture of boards increased as the density and mixing ratio increased. The thickness swelling property for the two paper types decreased as the board density and mixing ratio increased. Boards made from Kraft paper recorded higher strength values than the ones made from recycled newsprint paper while the mixture of kraft and newsprint papers had the best surface finish. The result of the study will help in managing the large quality of waste from paper converting/carton industry and that the ceiling boards produced could be installed with clout nails or used with suspended ceiling fittings.





References:
[1] O.P. Folorunso and B.U Anyata. Potential uses of waste paper/sludge as a ceiling material, Research Journal of Applied Sciences 2(25): 2007, pp584 -586.
[2] J. A. Fuwape and J. S. Fabiyi. Introduction to pulp and paper technology in Nigeria. Forestry and Wood Technology Department Lecture Series. 2010.
[3] W. Y. Ahn, and A. A. Moslemi. Sem examination of wood-Portland cements boards. Wood Science 13(2): 1980. Pp. 77-82.
[4] M. H. Simatupang, and R. L. Geimer. Inorganic binder for wood composites: feasibility and limitations. In Proceedings of the Wood Adhesive Symposium. 16-18 May. 1990. pp. 169-176.
[5] M. H. Simatupang, A. Kasim, N. Seddig, and M.Smid. Improving the bond between wood and gypsum. In Moslemi AA. (Ed). Proc. Second Int. Inorganic Bonded Wood and Fibre composite materials. For. Prod. Res. Sec. Madison Wis. 1991. pp. 61-69.
[6] A. O. Oyagade. Compatibility of some tropical hardwood species with Portland cement. Journal of Tropical Forest Science 6(4): 1994. pp. 387-396.
[7] B. Ajayi. Strength and dimensional stability of cement-bonded flake board produced from Gmelina arborea and Leucaena leucocephala. 2000. Ph.D. Thesis, Federal University of Technology, Akure.
[8] A. O. Oyagade. Thickness Swelling and Water Absorption of Cement-Bonded Particleboard as Influenced by Three Variables. The Nigeria Journal of Forestry. Vol. 18, 1988 pp. 1-7.
[9] S. O. Badejo. Influences of pretreatment temperature and additive concentration on the properties of cement-bonded particle board from plantation-grown tropical hardwoods. Tropical Science, Vol. 4, 1989. pp. 285-299.
[10] B. Ajayi. and J. A.Fuwape.Influence of additive concentration and wood species on dimensional stability of cement bonded flake board, Journal of Institute of Wood Science, UK, Vol. 17(1). 2005. pp. 34 – 40.
[11] J. A. Fuwape, J. S. Fabiyi and E. O. Osuntuyi. Technical assessment of three-layered cement-bonded boards produced from waste paper and sawdust. Waste Management 27(11).2007 pp1611-1616.
[12] Han – Seung Yang, Dae – Jun Kin, Young – Kyu Lee, Hyen – Joong Kim, Jm – Young Jeon and Clun–Won Kang. Possibility of using waste tyre composites reinforced with vice straw as construction materials.Bio-resource Technology 95 (2004) pp.61 – 65 Elsevier. www.sciencedirect.com.
[13] Eshmaiel Ganjian, Morteza Khorami and Homayoon Sadeghi Pouya, Application of Kraft and Acrylic Fibres to replace asbestos in composite cement sheets in 11th International Inorganic – Bonded Fibre composites conference, Madrid – Spain Nov 5 – 7 2008 pp. 52.