Investigation on Toxicity of Manufactured Nanoparticles to Bioluminescence Bacteria Vibrio fischeri

Acute toxicity of nano SiO2, ZnO, MCM-41 (Meso pore silica), Cu, Multi Wall Carbon Nano Tube (MWCNT), Single Wall Carbon Nano Tube (SWCNT) , Fe (Coated) to bacteria Vibrio fischeri using a homemade luminometer , was evaluated. The values of the nominal effective concentrations (EC), causing 20% and 50% inhibition of biouminescence, using two mathematical models at two times of 5 and 30 minutes were calculated. Luminometer was designed with Photomultiplier (PMT) detector. Luminol chemiluminescence reaction was carried out for the calibration graph. In the linear calibration range, the correlation coefficients and coefficient of Variation (CV) were 0.988 and 3.21% respectively which demonstrate the accuracy and reproducibility of the instrument that are suitable. The important part of this research depends on how to optimize the best condition for maximum bioluminescence. The culture of Vibrio fischeri with optimal conditions in liquid media, were stirring at 120 rpm at a temperature of 150C to 180C and were incubated for 24 to 72 hours while solid medium was held at 180C and for 48 hours. Suspension of nanoparticles ZnO, after 30 min contact time to bacteria Vibrio fischeri, showed the highest toxicity while SiO2 nanoparticles showed the lowest toxicity. After 5 min exposure time, the toxicity of ZnO was the strongest and MCM-41 was the weakest toxicant component.

Toxicity Study of Two Different Synthesized Silver Nanoparticles on Bacteria Vibrio Fischeri

A comparative evaluation of acute toxicity of synthesized nano silvers using two different procedures (biological and chemical reduction methods) and silver ions on bacteria Vibrio fischeri was investigated. The bacterial light inhibition test as a toxicological endpoint was used by applying of a homemade luminometer. To compare the toxicity effects as a quantitative parameter, a nominal effective concentrations (EC) of chemicals and a susceptibility constant (Z-value) of bacteria, after 5 min and 30 min exposure times, were calculated. After 5 and 30 min contact times, the EC50 values of two silver nanoparticles and the EC20 values were about similar. It demonstrates that toxicity of silvers was independent of their procedure. The EC values of nanoparticles were larger than those of the silver ions. The susceptibilities(Z- Values) of V.fischeri (L/mg) to the silver ions were greater than those of the nano silvers. According to the EC and Z values, the toxicity of silvers decreased in the following order: Silver ions >> silver nanoparticles from chemical reduction method ~ silver nanoparticles from biological method.