Abstract: The destruction effect of hydrocarbon solutions on concrete besides its high permeability have led researchers to try to improve the performance of concrete exposed to these solutions, hence improving the durability and usability of oil concrete structures. Recently, polymer concrete is considered one of the most important types of concrete, and its behavior after exposure to oil products is still unknown. In the present work, an experimental study has been carried out, in which the prepared epoxy polymer concrete immersed in different types of hydrocarbon exposure solutions (gasoline, kerosene, and gas oil) for 120 days and compared with the reference concrete left in the air. The results for outdoor specimens indicate that the mechanical properties are increased after 120 days, but the specimens that were immersed in gasoline, kerosene, and gas oil for the same period show a reduction in compressive strength by -21%, -27% and -23%, whereas in splitting tensile strength by -19%, -24% and -20%, respectively. The reductions in ultrasonic pulse velocity for cubic specimens are -17%, -22% and -19% and in cylindrical specimens are -20%, -25% and -22%, respectively.
Abstract: This paper presents the results of an experimental
study on the effects of elevated temperature on compressive and
flexural strength of Normal Strength Concrete (NSC), High Strength
Concrete (HSC) and High Performance Concrete (HPC). In addition,
the specimen mass and volume were measured before and after
heating in order to determine the loss of mass and volume during the
test. In terms of non-destructive measurement, ultrasonic pulse
velocity test was proposed as a promising initial inspection method
for fire damaged concrete structure. 100 Cube specimens for three
grades of concrete were prepared and heated at a rate of 3°C/min up
to different temperatures (150, 250, 400, 600, and 900°C). The results
show a loss of compressive and flexural strength for all the concretes
heated to temperature exceeding 400°C. The results also revealed that
mass and density of the specimen significantly reduced with an
increase in temperature.