Abstract: In this paper, we proposed the effects of Mo thickness
on the properties of AZO/Mo/AZO multilayer thin films for
opto-electronics applications. The structural, optical and electrical
properties of AZO/Mo/AZO thin films were investigated.
Optimization of the thin films coatings resulted with low resistivity of
9.98 × 10-5 )-cm, mobility of 12.75 cm2/V-s, carrier concentration of
1.05 × 1022 cm-3, maximum transmittance of 79.13% over visible
spectrum of 380 – 780 nm and Haacke figure of merit (FOM) are 5.95
× 10-2 )-1 under Mo layer thickness of 15 nm. These results indicate an
alternative candidate for use as a transparent electrode in solar cells
and various displays applications.
Abstract: ZnO+Ga2O3 functionally graded thin films (FGTFs)
were examined for their potential use as Solar cell and organic light
emitting diodes (OLEDs). FGTF transparent conducting oxides (TCO)
were fabricated by combinatorial RF magnetron sputtering. The
composition gradient was controlled up to 10% by changing the
plasma power of the two sputter guns. A Ga2O3+ZnO graded region
was placed on the top layer of ZnO. The FGTFs showed up to 80%
transmittance. Their surface resistances were reduced to < 10% by
increasing the Ga2O3: pure ZnO ratio in the TCO. The FGTFs- work
functions could be controlled within a range of 0.18 eV. The
controlled work function is a very promising technology because it
reduces the contact resistance between the anode and Hall transport
layers of OLED and solar cell devices.
Abstract: Tungsten trioxide has been prepared by using P-PTA
as a precursor on alumina substrates by spin coating method.
Palladium introduced on WO3 film via electrolysis deposition by
using palladium chloride as catalytic precursor. The catalytic
precursor was introduced on the series of films with different
morphologies. X-ray diffractometry (XRD), Scanning electron
microscopy (SEM) and XPS were applied to analyze structure and
morphology of the fabricated thin films. Then we measured variation
of samples- electrical conductivity of pure and Pd added films in air
and diluted hydrogen. Addition of Pd resulted in a remarkable
improvement of the hydrogen sensing properties of WO3 by detection
of Hydrogen below 1% at room temperature. Also variation of the
electrical conductivity in the presence of diluted hydrogen revealed
that response of samples depends rather strongly on the palladium
configuration on the surface.
Abstract: The morphological parameter of a thin film surface
can be characterized by power spectral density (PSD) functions
which provides a better description to the topography than the RMS
roughness and imparts several useful information of the surface
including fractal and superstructure contributions. Through the
present study Nanoparticle copper/carbon composite films were
prepared by co-deposition of RF-Sputtering and RF-PECVD method
from acetylene gas and copper target. Surface morphology of thin
films is characterized by using atomic force microscopy (AFM). The
Carbon content of our films was obtained by Rutherford Back
Scattering (RBS) and it varied from .4% to 78%. The power values of
power spectral density (PSD) for the AFM data were determined by
the fast Fourier transform (FFT) algorithms. We investigate the effect
of carbon on the roughness of thin films surface. Using such
information, roughness contributions of the surface have been
successfully extracted.