Abstract: Wind turbines are equipment of great importance for generating clean energy in countries and regions with abundant winds. However, complex loadings fluctuations to which they are subject can cause premature failure of these equipment due to the material fatigue process. This work evaluates fatigue failures in small AISI 304 stainless steel turbine shafts. Fractographic analysis techniques, chemical analyzes using energy dispersive spectrometry (EDS), and hardness tests were used to verify the origin of the failures, characterize the properties of the components and the material. The nucleation of cracks on the shafts' surface was observed due to a combined effect of variable stresses, geometric stress concentrating details, and surface wear, leading to the crack's propagation until the catastrophic failure. Beach marks were identified in the macrographic examination, characterizing the probable failure due to fatigue. The sensitization phenomenon was also observed.
Abstract: The tribological tests were performed on a new
tribometer, in order to measure the coefficient of friction of a gland
seal packing material on stainless steel shafts in presence of Cellulose
Nanocrystal (CNC) suspension as a sustainable, environmentally
friendly, water-based lubricant. To simulate the real situation from the
slurry pumps, silica sands were used as slurry particles. The surface
profiles after tests were measured by interferometer microscope to
characterize the surface wear. Moreover, the coefficient of friction
and surface wear were measured between stainless steel shaft and
chrome steel ball to investigate the tribological effects of CNC in
boundary lubrication region. Alignment of nanoparticles in the CNC suspensions are the
main reason for friction and wear reduction. The homogeneous
concentrated suspensions showed fingerprint patterns of a chiral
nematic liquid crystal. These properties made CNC a very good
lubricant additive in water.