Abstract: Alternative electrode materials for optoelectronic devices have been widely investigated in recent years. Since indium tin oxide (ITO) is the most preferred transparent conductive electrode, producing ITO films by simple and cost-effective solution-based techniques with enhanced optical and electrical properties has great importance. In this study, single- and multi-walled carbon nanotubes (SWCNT and MWCNT) incorporated into the ITO structure to increase electrical conductivity, mechanical strength, and chemical stability. Carbon nanotubes (CNTs) were firstly functionalized by acid treatment (HNO3:H2SO4), and the thermal resistance of CNTs after functionalization was determined by thermogravimetric analysis (TGA). Thin films were then prepared by spin coating technique and characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), four-point probe measurement system and UV-Vis spectrophotometer. The effects of process parameters were compared for ITO, MWCNT-ITO, and SWCNT-ITO films. Two factors including CNT concentration and annealing temperature were considered. The UV-Vis measurements demonstrated that the transmittance of ITO films was 83.58% at 550 nm, which was decreased depending on the concentration of CNT dopant. On the other hand, both CNT dopants provided an enhancement in the crystalline structure and electrical conductivity. Due to compatible diameter and better dispersibility of SWCNTs in the ITO solution, the best result in terms of electrical conductivity was obtained by SWCNT-ITO films with the 0.1 g/L SWCNT dopant concentration and heat-treatment at 550 °C for 1 hour.
Abstract: Zinc sulphide (ZnS) quantum dots (QDs) were synthesized successfully via simple sonochemical method. X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM) analysis revealed the average size of QDs of the order of 3.7 nm. The band gap of the QDs was tuned to 5.2 eV by optimizing the synthesis parameters. UV-Vis absorption spectra of ZnS QD confirm the quantum confinement effect. Fourier transform infrared (FTIR) analysis confirmed the formation of single phase ZnS QDs. To fabricate the diode, blend of ZnS QDs and P3HT was prepared and the heterojunction of PEDOT:PSS and the blend was formed by spin coating on indium tin oxide (ITO) coated glass substrate. The diode behaviour of the heterojunction was analysed, wherein the ideality factor was found to be 2.53 with turn on voltage 0.75 V and the barrier height was found to be 1.429 eV. ZnS-Graphene QDs nanocomposite was characterised for the surface morphological study. It was found that the synthesized ZnS QDs appear as quasi spherical particles on the graphene sheets. The average particle size of ZnS-graphene nanocomposite QDs was found to be 8.4 nm. From voltage-current characteristics of ZnS-graphene nanocomposites, it is observed that the conductivity of the composite increases by 104 times the conductivity of ZnS QDs. Thus the addition of graphene QDs in ZnS QDs enhances the mobility of the charge carriers in the composite material. Thus, the graphene QDs, with high specific area for a large interface, high mobility and tunable band gap, show a great potential as an electron-acceptors in photovoltaic devices.
Abstract: Water contamination by toxic compound is one of the serious environmental problems today. These toxic compounds mostly originated from industrial effluents, agriculture, natural sources and human waste. These studies focus on modification of multiwalled carbon nanotube (MWCNTs) with nanoparticle of calixarene and explore the possibility of using this modification for the remediation of cadmium in water. The nanocomposites were prepared by dissolving calixarene in chloroform solution as solvent, followed by additional multiwalled carbon nanotube (MWCNTs) then sonication process for 3 hour and fabricated the nanocomposites on substrate by spin coating method. Finally, the nanocomposites were tested on cadmium ion (10 mg/ml). The morphology of nanocomposites was investigated by FESEM showing the formation of calixarene on the outer walls of carbon nanotube and cadmium ion also clearly seen from the micrograph. This formation was supported by using energy dispersive x-ray (EDX). The presence of cadmium ions in the films, leads to some changes in the surface potential and Fourier Transform Infrared spectroscopy (FTIR).The nanocomposites MWCNTs-calixarene have potential for development of sensor for pollutant monitoring and nanoelectronics devices applications.
Abstract: A biosensor based on glucose oxidase (GOx) immobilized onto nanoparticles zirconium oxide with polyethylene nanocomposite for glucose monitoring has been designed. The CTAB/PEG/ZrO2/GOx nanocomposite was deposited onto screen printed carbon paste (SPCE) electrode via spin coating technique. The properties of CTAB/PEG/ZrO2/GOx were study using scanning electron microscopy (SEM). The SPE modified with the CTAB/PEG/ZrO2/GOx showed electrocatalytical response to the oxidation of glucose when ferrocene carboxaldehyde was used as an artificial redox mediator, which was studied by cyclic voltammetry (CV). Several parameters such as working potential, effect of pH and effect of ZrO2/PEG layers that governed the analytical performance of the biosensor, have been studied. The biosensor was applied to detect glucose with a linear range of 0.4 to 2.0 mmol L−1 with good repetability and reproducibility.
Abstract: This paper presents a spectroscopic study on doping
of Vanadyl pathalocyanine (VOPc) by [6,6]-phenyl C61 butyric acid
methyl ester (PCBM). The films are characterized by UV/Vis/NIR
spectroscopy. A drastic increase in the absorption coefficient has
been observed with increasing dopant concentration. Optical
properties of VOPc:PCBM films deposited by spin coating technique
were studied in detail. Optical band gap decreased with the PCBM
incorporation in the VOPc film. Optical band gap calculated from the
absorption spectra decreased from 3.32 eV to 3.26 eV with a
variation of 0–75 % of PCBM concentration in the VOPC films.
Abstract: The objective of the present investigation was to
evaluate the morphology of Escherchia coli bacteria in interaction
with SiO2 nanoparticles.
This study was made by atomic force microscopy and quartz
crystal microbalance using SiO2 nanoparticles with 10nm, 50nm and
100nm diameter and bacteria immobilized on polyelectrolyte
multilayer films obtained by spin coating or by “layer by layer”
(LbL) method.
Abstract: In this paper, Zinc Oxide (ZnO) thin films are deposited on glass substrate by sol-gel method. The ZnO thin films with well defined orientation were acquired by spin coating of zinc acetate dehydrate monoethanolamine (MEA), de-ionized water and isopropanol alcohol. These films were pre-heated at 275°C for 10 min and then annealed at 350°C, 450°C and 550°C for 80 min. The effect of annealing temperature and different thickness on structure and surface morphology of the thin films were verified by Atomic Force Microscopy (AFM). It was found that there was a significant effect of annealing temperature on the structural parameters of the films such as roughness exponent, fractal dimension and interface width. Thin films also were characterizied by X-ray Diffractometery (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure and show the c-axis grain orientation. Increasing annealing temperature increased the crystallite size and the c-axis orientation of the film after 450°C. Also In this study, ZnO thin films in different thickness have been prepared by sol-gel method on the glass substrate at room temperature. The thicknesses of films are 100, 150 and 250 nm. Using fractal analysis, morphological characteristics of surface films thickness in amorphous state were investigated. The results show that with increasing thickness, surface roughness (RMS) and lateral correlation length (ξ) are decreased. Also, the roughness exponent (α) and growth exponent (β) were determined to be 0.74±0.02 and 0.11±0.02, respectively.
Abstract: n-CdO/p-Si heterojunction diode was fabricated using
sol-gel spin coating technique which is a low cost and easily scalable
method for preparing of semiconductor films. The structural and
morphological properties of CdO film were investigated. The X-ray
diffraction (XRD) spectra indicated that the film was of
polycrystalline nature. The scanning electron microscopy (SEM)
images indicate that the surface morphology CdO film consists of the
clusters formed with the coming together of the nanoparticles. The
electrical characterization of Au/n-CdO/p–Si/Al heterojunction diode
was investigated by current-voltage. The ideality factor of the diode
was found to be 3.02 for room temperature. The reverse current of
the diode strongly increased with illumination intensity of 100
mWcm-2 and the diode gave a maximum open circuit voltage Voc of
0.04 V and short-circuits current Isc of 9.92×10-9 A.
Abstract: An organic bulk heterojunction (BHJ) was fabricated using a blended film containing Copper (II) tetrakis(4-acumylphenoxy) phthalocyanine (Tc-CuPc) along with [6,6]-Phenyl C61 butyric acid methyl ester (PCBM). Weight ratio between Tc-CuPc and PCBM was 1:1. The electrical properties of Tc-CuPc: PCBM BHJ were examined. Rectifying nature of the BHJ was displayed by current-voltage (I-V) curves, recorded in dark and at various temperatures. At low voltages, conduction was ohmic succeeded by space-charge limiting current (SCLC) conduction at higher voltages in which exponential trap distribution was dominant. Series resistance, shunt resistance, ideality factor, effective barrier height and mobility at room temperature were found to be 526 4, 482 k4, 3.7, 0.17 eV and 2×10-7 cm2V-1s-1 respectively. Temperature effect towards different BHJ parameters was observed under dark condition.
Abstract: This paper presents a comparative study on
Vanadyl Phthalocyanine (VOPc) thin films deposited by thermal
evaporation and spin coating techniques. The samples
were prepared on cleaned glass substrates and annealed at
various temperatures ranging form 95oC to 155oC. To obtain
the morphological and structural properties of VOPc thin
films, X-ray diffraction (XRD) technique and atomic force
microscopy (AFM) have been implied. The AFM topographic
images show a very slight difference in the thermally grown
films, before and after annealing, however best results are
achieved for the spin-cast film annealed at 125oC. The XRD
spectra show no existence of the sharp peaks, suggesting the
material to be amorphous. The humps in the XRD patterns
indicate the presence of some crystallites.
Abstract: Tungsten trioxide has been prepared by using P-PTA
as a precursor on alumina substrates by spin coating method.
Palladium introduced on WO3 film via electrolysis deposition by
using palladium chloride as catalytic precursor. The catalytic
precursor was introduced on the series of films with different
morphologies. X-ray diffractometry (XRD), Scanning electron
microscopy (SEM) and XPS were applied to analyze structure and
morphology of the fabricated thin films. Then we measured variation
of samples- electrical conductivity of pure and Pd added films in air
and diluted hydrogen. Addition of Pd resulted in a remarkable
improvement of the hydrogen sensing properties of WO3 by detection
of Hydrogen below 1% at room temperature. Also variation of the
electrical conductivity in the presence of diluted hydrogen revealed
that response of samples depends rather strongly on the palladium
configuration on the surface.
Abstract: PDMS (Polydimethylsiloxane) polymer is a suitable material for biological and MEMS (Microelectromechanical systems) designers, because of its biocompatibility, transparency and high resistance under plasma treatment. PDMS round channel is always been of great interest due to its ability to confine the liquid with membrane type micro valves. In this paper we are presenting a very simple way to form round shapemicrofluidic channel, which is based on reflow of positive photoresist AZ® 40 XT. With this method, it is possible to obtain channel of different height simply by varying the spin coating parameters of photoresist.