Abstract: Perovskite manganite La0.7Ca0.3MnO3 was synthesized by Sol-gel method. Polymerization of pyrrole was carried by in-situ polymerization method. The composite of pyrrole (Py)/La0.7Ca0.3MnO3 composite in the presence of oxidizing agent ammonium per sulphate to synthesize polypyrrole (PPy)/La0.7Ca0.3MnO3 (LCM) composite was carried out by the same in-situ polymerization method. The PPy/LCM composites were synthesized with varying compositions like 10, 20, 30, 40, and 50 wt.% of LCM in Py. The surface morphologies of these composites were analyzed by using scanning electron microscope (SEM). The images show that LCM particles are embedded in PPy chain. The impedance measurement of PPy/LCM at different temperature ranges from 30 to 180 °C was studied using impedance analyzer. The study shows that impedance is frequency and temperature dependent and it is found to decrease with increase in frequency and temperature.
Abstract: Zinc oxide particles were synthesized using the sol-gel method and dip coated on polyester fabric. X-ray diffraction (XRD) analysis revealed a single crystal phase of ZnO particles. Chemical characteristics of the polyester fabric surface were investigated using attenuated total reflection-Fourier transform infrared (ATR-FTIR) measurements. Morphology of ZnO coated fabric was analyzed using field emission scanning electron microscopy (FESEM). After particle analysis, the aqueous ZnO solution resulted in a narrow size distribution at submicron levels. The deposit of ZnO on polyester fabrics yielded a homogeneous spread of spherical particles. Energy dispersive X-ray spectroscopy (EDX) results also affirmed the presence of ZnO particles on the polyester fabrics.
Abstract: Microbial fuel cells (MFCs) represent a promising
technology for simultaneous bioelectricity generation and wastewater
treatment. Catalysts are significant portions of the cost of microbial
fuel cell cathodes. Many materials have been tested as aqueous
cathodes, but air-cathodes are needed to avoid energy demands for
water aeration. The sluggish oxygen reduction reaction (ORR) rate at
air cathode necessitates efficient electrocatalyst such as carbon
supported platinum catalyst (Pt/C) which is very costly. Manganese
oxide (MnO2) was a representative metal oxide which has been
studied as a promising alternative electrocatalyst for ORR and has
been tested in air-cathode MFCs. However the single MnO2 has poor
electric conductivity and low stability. In the present work, the MnO2
catalyst has been modified by doping Pt nanoparticle. The goal of the
work was to improve the performance of the MFC with minimum Pt
loading. MnO2 and Pt nanoparticles were prepared by hydrothermal
and sol gel methods, respectively. Wet impregnation method was
used to synthesize Pt/MnO2 catalyst. The catalysts were further used
as cathode catalysts in air-cathode cubic MFCs, in which anaerobic
sludge was inoculated as biocatalysts and palm oil mill effluent
(POME) was used as the substrate in the anode chamber. The asprepared
Pt/MnO2 was characterized comprehensively through field
emission scanning electron microscope (FESEM), X-Ray diffraction
(XRD), X-ray photoelectron spectroscopy (XPS), and cyclic
voltammetry (CV) where its surface morphology, crystallinity,
oxidation state and electrochemical activity were examined,
respectively. XPS revealed Mn (IV) oxidation state and Pt (0)
nanoparticle metal, indicating the presence of MnO2 and Pt.
Morphology of Pt/MnO2 observed from FESEM shows that the
doping of Pt did not cause change in needle-like shape of MnO2
which provides large contacting surface area. The electrochemical
active area of the Pt/MnO2 catalysts has been increased from 276 to
617 m2/g with the increase in Pt loading from 0.2 to 0.8 wt%. The
CV results in O2 saturated neutral Na2SO4 solution showed that
MnO2 and Pt/MnO2 catalysts could catalyze ORR with different
catalytic activities. MFC with Pt/MnO2 (0.4 wt% Pt) as air cathode
catalyst generates a maximum power density of 165 mW/m3, which
is higher than that of MFC with MnO2 catalyst (95 mW/m3). The
open circuit voltage (OCV) of the MFC operated with MnO2 cathode
gradually decreased during 14 days of operation, whereas the MFC
with Pt/MnO2 cathode remained almost constant throughout the
operation suggesting the higher stability of the Pt/MnO2 catalyst.
Therefore, Pt/MnO2 with 0.4 wt% Pt successfully demonstrated as an
efficient and low cost electrocatalyst for ORR in air cathode MFC with higher electrochemical activity, stability and hence enhanced
performance.
Abstract: The contact resistance between source/drain electrodes
and semiconductor layer is an important parameter affecting electron
transporting performance in the thin film transistor (TFT). In this
work, we introduced a transparent and the solution prossable
single-walled carbon nanotube (SWCNT)/Al-doped ZnO nano particle
(AZO NP) bilayer electrodes showing low contact resistance with
indium-oxide (In2O3) sol gel thin film. By inserting low work function
AZO NPs into the interface between the SWCNTs and the In2O3 which
has a high energy barrier, we could obtain an electrical Ohmic contact
between them. Finally, with the SWCNT-AZO NP bilayer electrodes,
we successfully fabricated a TFT showing a field effect mobility of
5.38 cm2/V·s at 250°C.
Abstract: In this work, we have synthesized BaTiO3 via sol gel method by sintering at different temperatures (600, 700, 800, 900, 10000C) and studied their structural, optical and ferroelectric properties through X-ray diffraction (XRD), UV-Vis spectrophotometer and PE Loop Tracer. X-ray diffraction patterns of barium titanate samples show that the peaks of the diffractogram are successfully indexed with the tetragonal and cubic structure of BaTiO3. The Optical band gap calculated through UV Visible spectrophotometer varies from 4.37 to 3.80 eV for the samples sintered at 600 to 10000C, respectively. The particle size calculated through transmission electron microscopy varies from 20 to 40 nm for the samples sintered at 600 to 10000C, respectively. Moreover, it has been observed that the ferroelectricity increases as we increase the sintering temperature.
Abstract: Nanocrystalline thin film of Na0.1V2O5.nH2O xerogel
obtained by sol gel synthesis was used as gas sensor. Gas sensing
properties of different gases such as hydrogen, petroleum and
humidity were investigated. Applying XRD and TEM the size of the
nanocrystals is found to be 7.5 nm. SEM shows a highly porous
structure with submicron meter-sized voids present throughout the
sample. FTIR measurement shows different chemical groups
identifying the obtained series of gels. The sample was n-type
semiconductor according to the thermoelectric power and electrical
conductivity. It can be seen that the sensor response curves from
130oC to 150oC show a rapid increase in sensitivity for all types of
gas injection, low response values for heating period and the rapid
high response values for cooling period. This result may suggest that
this material is able to act as gas sensor during the heating and
cooling process.
Abstract: In this study, Li4SiO4 powder was successfully
synthesized via sol gel method followed by drying at 150oC. Lithium
oxide, Li2O and silicon oxide, SiO2 were used as the starting
materials with citric acid as the chelating agent. The obtained powder
was then sintered at various temperatures. Crystallographic phase
analysis, morphology and ionic conductivity were investigated
systematically employing X-ray diffraction, Fourier Transform
Infrared, Scanning Electron Microscopy and AC impedance
spectroscopy. XRD result showed the formation of pure monoclinic
Li4SiO4 crystal structure with lattice parameters a = 5.140 Å, b =
6.094 Å, c = 5.293 Å, β = 90o in the sample sintered at 750oC. This
observation was confirmed by FTIR analysis. The bulk conductivity
of this sample at room temperature was 3.35 × 10-6 S cm-1 and the
highest bulk conductivity of 1.16 × 10-4 S cm-1 was obtained at
100°C. The results indicated that, the Li4SiO4 compound has
potential to be used as host for LISICON structured solid electrolyte
for low temperature application.
Abstract: n-CdO/p-Si heterojunction diode was fabricated using
sol-gel spin coating technique which is a low cost and easily scalable
method for preparing of semiconductor films. The structural and
morphological properties of CdO film were investigated. The X-ray
diffraction (XRD) spectra indicated that the film was of
polycrystalline nature. The scanning electron microscopy (SEM)
images indicate that the surface morphology CdO film consists of the
clusters formed with the coming together of the nanoparticles. The
electrical characterization of Au/n-CdO/p–Si/Al heterojunction diode
was investigated by current-voltage. The ideality factor of the diode
was found to be 3.02 for room temperature. The reverse current of
the diode strongly increased with illumination intensity of 100
mWcm-2 and the diode gave a maximum open circuit voltage Voc of
0.04 V and short-circuits current Isc of 9.92×10-9 A.
Abstract: Recently, nanomaterials are developed in the form of nano-films, nano-crystals and nano-pores. Lanthanide phosphates as a material find extensive application as laser, ceramic, sensor, phosphor, and also in optoelectronics, medical and biological labels, solar cells and light sources. Among the different kinds of rare-earth orthophosphates, yttrium orthophosphate has been shown to be an efficient host lattice for rare earth activator ions, which have become a research focus because of their important role in the field of light display systems, lasers, and optoelectronic devices. It is in this context that the 4fn- « 4fn-1 5d transitions of rare earth in insulating materials, lying in the UV and VUV, are the aim of large number of studies .Though there has been a few reports on Eu3+, Nd3+, Pr3+,Er3+, Ce3+, Tm3+ doped YPO4. The 4fn- « 4fn-1 5d transitions of the rare earth dependent to the host-matrix, several matrices ions were used to study these transitions, in this work we are suggesting to study on a very specific class of inorganic material that are orthophosphate doped with rare earth ions. This study focused on the effect of Ce3+ concentration on the structural and optical properties of Ce3+ doped YPO4 yttrium orthophosphate with powder form prepared by the Sol Gel method.