Abstract: Utilisation of biomass feedstock for biochar has received increasing attention because of their potential for carbon sequestration and soil amendment. The aim of this study is to investigate the characteristics of rubber wood as a biomass feedstock for biochar via slow pyrolysis process. This was achieved by using proximate, ultimate, and thermogravimetric analysis (TGA) as well as heating value, pH and lignocellulosic determination. Rubber wood contains 4.13 mf wt.% moisture, 86.30 mf wt.% volatile matter, 0.60 mf wt.% ash content, and 13.10 mf wt.% fixed carbon. The ultimate analysis shows that rubber wood consists of 44.33 mf wt.% carbon, 6.26 mf wt.% hydrogen, 19.31 mf wt.% nitrogen, 0.31 mf wt.% sulphur, and 29.79 mf wt.% oxygen. The higher heating value of rubber wood is 22.5 MJ/kg, and its lower heating value is 21.2 MJ/kg. At 27 °C, the pH value of rubber wood is 6.83 which is acidic. The lignocellulosic analysis revealed that rubber wood composition consists of 2.63 mf wt.% lignin, 20.13 mf wt.% cellulose, and 65.04 mf wt.% hemicellulose. The volatile matter to fixed carbon ratio is 6.58. This led to a biochar yield of 25.14 wt.% at 500 °C. Rubber wood is an environmental friendly feedstock due to its low sulphur content. Rubber wood therefore is a suitable and a potential feedstock for biochar production via slow pyrolysis.
Abstract: This study aims to determine the level of resistance of Hevea brasiliensis and Paraserianthes falcataria (synonym: Falcataria molucana) against wood rot fungi Pleurotus ostreatus based on Indonesian standard SNI 01.7207-2006 and Japanese standard JIS K 1571-2004. The variables measured were visual appearance and weight loss percentage of wood based on longitudinal and cross section fiber directions of rubber wood and sengon wood. Measurement of oven dry weight loss of wood samples performed after 12 weeks incubation. Replication performed was 10 times at each treatment combination. The results based on SNI 01.7207-2006, weight loss value of H. brasiliensis and P. falcataria wood with fiber direction longitudinal were 23,12 and 22,25% respectively and cross section were 20,77 and 18,76% respectively, and all were classified to resistance class IV (no resistance). The results based on JIS K 1571-2004, weight loss value of both woods with fiber direction cross section were 10,95 and 14,20% respectively.