Abstract: In this research, carrageenan extracted from seaweed Eucheuma cottonii was mixed with polyvinyl alcohol (PVA) and then crosslinked using glutaraldehyde (GA). The obtained hydrogel films were applied to control the drug release rate of paracetamol. The aim of this research was to develop a mathematical model that can be used to describe the mass transfer rate of paracetamol from the hydrogel film into buffer solution. The effect of weight ratio carrageenan-PVA (5: 0, 1: 0.5, 1: 1, 1: 2, 0: 5) on the parameters of the mathematical model was investigated also. Based on the experimental data, the proposed mathematical model could describe the mass transfer rate of paracetamol. The weight ratio of carrageenan-PVA greatly affected the amount of paracetamol absorbed in the hydrogel film and the mass transfer rate of paracetamol.
Abstract: Polyaniline (PANI) is one of the most extensively studied material among the conducting polymers due to its simple synthesis by chemical and electrochemical routes. PANIs have advantages of chemical stability and high conductivity making their commercial applications quite attractive. However, to our knowledge, very little work has been reported on the tensile strength properties of templated PANIs processed with polyvinyl alcohol and also, detailed study has not been carried out. We have investigated the effect of small molecule and polymers as templates on PANI. Stable aqueous colloidal suspensions of trisodium citrate (TSC), poly(ethylenedioxythiophene)-polystyrene sulfonate (PEDOT-PSS), and polyethylene glycol (PEG) templated PANIs were prepared through chemical synthesis, processed with polyvinyl alcohol (PVA) and were fabricated into films by solution casting. Absorption and infra-red spectra were studied to gain insight into the possible molecular interactions. Surface morphology was studied through scanning electron microscope and optical microscope. Interestingly, tensile testing studies revealed least strain for pure PVA when compared to the blends of templated PANI. Furthermore, among the blends, TSC templated PANI possessed maximum elasticity. The ultimate tensile strength for PVA processed, PEG-templated PANI was found to be five times more than other blends considered in this study. We establish structure–property correlation with morphology, spectral characterization and tensile testing studies.
Abstract: The present work reports an effect of surface- modification of indium tin oxide (ITO) particles with chemicals on their electronic conductivity properties. Examined chemicals were polyvinyl alcohol (nonionic polymer), poly(diallyl dimethyl ammonium chloride) (cationic polymer), poly(sodium 4-styrene-sulfonate) (anionic polymer), (2-aminopropyl) trimethoxy silane (APMS) (silane coupling agent with amino group), and (3-mercaptopropyl) trimethoxy silane (MPS) (silane coupling agent with thiol group). For all the examined chemicals, volume resistivities of surface-modified ITO particles did not increase much when they were aged in air at 80 oC, compared to a volume resistivity of un-surface-modified ITO particles. Increases in volume resistivities of ITO particles surface-modified with the silane coupling agents were smaller than those with the polymers, since hydrolysis of the silane coupling agents and condensation of generated silanol and OH groups on ITO particles took place to provide efficient immobilization of them on particles. The APMS gave an increase in volume resistivity smaller than the MPS, since a larger solubility in water of APMS providing a larger amount of APMS immobilized on particles.
Abstract: In this paper, MCM-41 mesoporous material nanofibers were synthesized by an electrospinning technique. The nanofibers were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), x-ray diffraction (XRD), and nitrogen adsorption–desorption measurement. Tetraethyl orthosilicate (TEOS) and polyvinyl alcohol (PVA) were used as a silica source and fiber forming source, respectively. TEM and SEM images showed synthesis of MCM-41 nanofibers with a diameter of 200 nm. The pore diameter and surface area of calcined MCM-41 nanofibers was 2.2 nm and 970 m2/g, respectively. The morphology of the MCM-41 nanofibers depended on spinning voltages.
Abstract: The rheological response of blends obtained from
quaternized polysulfone and polyvinyl alcohol in N-methyl-2-
pyrrolidone as against structural peculiarity of polymers from the
blend, composition of polymer mixtures, as well as the types of
interactions were investigated. Results show that the variation of
polyvinyl alcohol composition in the studied system determines
changes of the rheological properties, suggesting that the PVA acts as
a plasticizer. Consequently, rheological behavior of complex system,
described by the nonlinear flow curve, indicates the impact of
polyvinil alcohol content to polysulfone solution, in order to facilitate
the subsequently preparation of bioactive membranes.
Abstract: Nanofibers are defined as fibers with diameters less
than 100 nanometers. In this study, behaviours of activated carbon
nanofiber (ACNF), carbon nanofiber (CNF), polyacrylonitrile/ carbon
nanotube (PAN/CNT), polyvinyl alcohol/nanosilver (PVA/Ag) in
proton exchange membrane (PEM) fuel cells are investigated
experimentally. This material was used as gas diffusion layer (GDL)
in PEM fuel cells. In this study, the electrical conductivities of
nanofiber and nanofiber/nanoparticles have been studied to
understand their effects on PEM fuel cell performance. According to
the experimental results, the maximum electrical conductivity
performance of the fuel cell with nanofiber was found to be at
PVA/Ag (at UConn condition). The electrical conductivities of CNF,
ACNF, PAN/CNT are lower for PEM. The resistance of cell with
PVA/Ag is lower than the resistance of cell with PAN/CNT, ACNF,
CNF.
Abstract: Graphene was dispersed using a tip sonicator and the
effect of surfactants were analysed. Sodium Dodecyl Sulphate (SDS)
and Polyvinyl Alcohol (PVA) were compared to observe whether or
not they had any effect on any de-wrinkling, and secondly whether
they aided to achieve better dispersions. There is a huge demand for
wrinkle free graphene as this will greatly increase its usefulness in
various engineering applications. A comprehensive literature on dewrinkling
graphene has been discussed. Low magnification Scanning
Electronic Microscopy (SEM) was conducted to assess the quality of
graphene de-wrinkling. The utilization of the PVA has significant
effect on de-wrinkling whereas SDS had minimal effect on the dewrinkling
of graphene.
Abstract: In recent years a new method of combination
treatment for cancer has been developed and studied that has led to
significant advancements in the field of cancer therapy. Hyperthermia
is a traditional therapy that, along with a creation of a medically
approved level of heat with the help of an alternating magnetic AC
current, results in the destruction of cancer cells by heat. This paper
gives details regarding the production of the spherical nanocomposite
PVA/γ-Fe2O3 in order to be used for medical purposes such as tumor
treatment by hyperthermia. To reach a suitable and evenly distributed
temperature, the nanocomposite with core-shell morphology and
spherical form within a 100 to 200 nanometer size was created using
phase separation emulsion, in which the magnetic nano-particles γ-
Fe2O3 with an average particle size of 20 nano-meters and with
different percentages of 0.2, 0.4, 0.5 and 0.6 were covered by
polyvinyl alcohol. The main concern in hyperthermia and heat
treatment is achieving desirable specific absorption rate (SAR) and
one of the most critical factors in SAR is particle size. In this project
all attempts has been done to reach minimal size and consequently
maximum SAR. The morphological analysis of the spherical
structure of the nanocomposite PVA/γ-Fe2O3 was achieved by SEM
analyses and the study of the chemical bonds created was made
possible by FTIR analysis. To investigate the manner of magnetic
nanocomposite particle size distribution a DLS experiment was
conducted. Moreover, to determine the magnetic behavior of the γ-
Fe2O3 particle and the nanocomposite PVA/γ-Fe2O3 in different
concentrations a VSM test was conducted. To sum up, creating
magnetic nanocomposites with a spherical morphology that would be
employed for drug loading opens doors to new approaches in
developing nanocomposites that provide efficient heat and a
controlled release of drug simultaneously inside the magnetic field,
which are among their positive characteristics that could significantly
improve the recovery process in patients.
Abstract: In this paper, the effects of fiber types and elevated
temperatures on compressive strength, modulus of rapture and the
bond characteristics of fiber reinforced concretes (FRC) are
presented. By using the three different types of fibers (steel fiber-SF,
polypropylene-PPF and polyvinyl alcohol-PVA), FRC specimens
were produced and exposed to elevated temperatures up to 800 ºC for
1.5 hours. In addition, a plain concrete (without fiber) was produced
and used as a control. Test results obtained showed that the steel fiber
reinforced concrete (SFRC) had the highest compressive strength,
modulus of rapture and bond stress values at room temperatures, the
residual bond, flexural and compressive strengths of both FRC and
plain concrete dropped sharply after exposure to high temperatures.
The results also indicated that the reduction of bond, flexural and
compressive strengths with increasing the exposed temperature was
relatively less for SFRC than for plain, and FRC with PPF and PVA.
Abstract: Poly bag and mulch films for agricultural field caused
pose environmental problem due to the non-degradable plastics
wastes upon disposal. Thus, a degradable poly bag was designed with
hybrid sago starch (SS) and polyvinyl alcohol (PVA). Two Different
blended compositions of SS and PVA hybrid have been compounded.
Then, the hybrids blended are mixed with linear line density
polyethylene (LLDPE) resin to fabricate poly bag film through
conventional film blowing process. Samples of LLDPE, SS and PVA
hybrid film were exposed to UV light and soil burial. The weight
losses were determined during degradation process. Hybrid film by
degradation of starch was found to hydrolyze and hydroxyl groups
decrease on esterification upon exposure to soil burial and uv
radiation. It was found out that, the hybrid film for 60% of SS
composition showed greatest degradation in soil and UV radiation.
Abstract: Surface modification and functionalization has been
an important tool for scientists in order to open new frontiers in
nanoscience and nanotechnology. Desired surface characteristics for
the intended applications can be achieved with surface
functionalization.
In this work, the effect of water soluble ligands on the adsorption
capabilities of silver nanoparticles onto AC which was synthesized
from German beech wood was investigated. Sodium borohydride
(NaBH4) and polyvinyl alcohol (PVA) were used as the ligands.
Silver nanoparticles with different surface coatings have average
sizes range from 10 to 13 nm. They were synthesized in aqueous
media by reducing Ag (I) ion in the presence of ligands. These
particles displayed adsorption tendencies towards AC when they
were mixed together and shaken in distilled water.
Silver nanoparticles (NaBH4-AgNPs) reduced and stabilized by
NaBH4 adsorbed onto AC with a homogenous dispersion of
aggregates with sizes in the range of 100-400 nm. Beside, silver
nanoparticles, which were prepared in the presence of both NaBH4
and PVA (NaBH4/PVA-Ag NPs), demonstrated that NaBH4/PVA-Ag
NPs adsorbed and dispersed homogenously but, they aggregated with
larger sizes on the AC surface (range from 300 to 600 nm). In
addition, desorption resistance of Ag nanoparticles were investigated
in distilled water. According to the results AgNPs were not desorbed
on the AC surface in distilled water.
Abstract: A simple multi-wavelength passively Q-switched
Erbium-doped fiber laser (EDFL) is demonstrated using low cost
multi-walled carbon nanotubes (MWCNTs) based saturable absorber
(SA), which is prepared using polyvinyl alcohol (PVA) as a host
polymer. The multi-wavelength operation is achieved based on
nonlinear polarization rotation (NPR) effect by incorporating 50 m
long photonic crystal fiber (PCF) in the ring cavity. The EDFL
produces a stable multi-wavelength comb spectrum for more than 14
lines with a fixed spacing of 0.48 nm. The laser also demonstrates a
stable pulse train with the repetition rate increases from 14.9 kHz to
25.4 kHz as the pump power increases from the threshold power of
69.0 mW to the maximum pump power of 133.8 mW. The minimum
pulse width of 4.4 μs was obtained at the maximum pump power of
133.8 mW while the highest energy of 0.74 nJ was obtained at pump
power of 69.0 mW.
Abstract: Polybag and mulch film in agricultural field are used plastics which caused environmental problems after transplantation and planting processes due to the discarded wastes. Thus a degradable polybag was designed in this study to replace non degradable polybag with natural biodegradable resin that is widely available, namely sago starch (SS) and polyvinyl alcohol (PVA). Hybrid blend consists of SS, PVA and linear low density polyethylene (LLDPE) was compounded at different ratios. The thermal and mechanical properties of the blends were investigated. Hybrid films underwent landfill degradation tests for up to 2 months. The films showed gelation and melting transition existed for all three systems with significant melting peaks by LLDPE and PVA. All hybrid blends loses its LLDPE semi crystalline characteristics as PVA and SS systems had disrupted crystallinity and enhanced the amorphosity of the hybrid system. Generally, blending SS with PVA improves the mechanical properties of the SS based materials. Tensile strength of each film was also decreased with the increase of SS contents while its modulus had increased with SS content.
Abstract: In this study, hydrogels consisted of polyvinyl alcohol,
propylene glycol and β-glucan were developed by radiation technique
for wound dressing. The prepared hydrogels were characterized by
examining of physical properties such as gel fraction and absorption
ratio. The gel fraction and absorption ratio were dependent on the
crosslinking density. On observing the wound healing of rat skin, the
resulting hydrogels accelerated the wound healing comparing to cotton
gauze. Therefore, the PVA/propylene glycol/β-glucan blended
hydrogels can greatly accelerate the healing without causing irritation.
Abstract: In modern agriculture, polymeric hydrogels are
known as a component able to hold an amount of water due to their
3-dimensional network structure and their tendency to absorb water
in humid environments. In addition, these hydrogels are able to
controllably release the fertilisers and pesticides loaded in them.
Therefore, they deliver these materials to the plants' roots and help
them with growing. These hydrogels also reduce the pollution of
underground water sources by preventing the active components
from leaching. In this study, sIPN acrylamide based hydrogels are
synthesised by using acrylamide free radical, potassium acrylate, and
linear polyvinyl alcohol. Ammonium nitrate is loaded in the hydrogel
as the fertiliser. The effect of various amounts of monomers and
linear polymer, measured in molar ratio, on the swelling rate,
equilibrium swelling, and release of ammonium nitrate is studied.
Abstract: The hybrid membranes containing inorganic materials in polymer matrix are identified as a remarkable family of proton conducting hybrid electrolytes. In this work, the proton conducting inorganic/organic hybrid membranes for proton exchange membrane fuel cells (PEMFCs) were prepared using polyvinyl alcohol (PVA), tetraethoxyorthosilane (TEOS) and heteropolyacid (HPA). The synthesized hybrid membranes were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction spectroscopy (XRD), Scanning electron microscopy (SEM) and Thermogravimetry analysis (TGA). The effects of heteropolyacid incorporation on membrane properties, including morphology and thermal stability were extensively investigated.
Abstract: Highly ordered TiO2 nanotube (TNT) arrays were
fabricated onto a pre-treated titanium foil by anodic oxidation with a
voltage of 20V in phosphoric acid/sodium fluoride electrolyte. A pretreatment
of titanium foil involved washing with acetone,
isopropanol, ethanol and deionized water. Carbon doped TiO2
nanotubes (C-TNT) was fabricated 'in-situ' with the same method in
the presence of polyvinyl alcohol and urea as carbon sources. The
affects of polyvinyl alcohol concentration and oxidation time on the
composition, morphology and structure of the C-TN were studied by
FE-SEM, EDX and XRD techniques. FESEM images of the
nanotubes showed uniform arrays of C-TNTs. The density and
microstructures of the nanotubes were greatly affected by the content
of PVA. The introduction of the polyvinyl alcohol into the electrolyte
increases the amount of C content inside TiO2 nanotube arrays
uniformly. The influence of carbon content on the photo-current of
C-TNT was investigated and the I-V profiles of the nanotubes were
established. The preliminary results indicated that the 'in-situ'
doping technique produced a superior quality nanotubes compared to
post doping techniques.
Abstract: A scaffold is necessary for tooth regeneration because of its three-dimensional geometry. For restoration of defect, it is necessary for the scaffold to be prepared in the shape of the defect. Sponges made from polyvinyl alcohol with formalin cross-linking (PVF sponge) have been used for scaffolds for bone formation in vivo. To induce osteogenesis within the sponge, methods of growing rat bone marrow cells (rBMCs) among the fiber structures in the sponge might be considered. Storage of rBMCs among the fibers in the sponge coated with dextran (10 kDa) was tried. After seeding of rBMCs to PVF sponge immersed in dextran solution at 2 g/dl concentration, osteogenesis was recognized in subcutaneously implanted PVF sponge as a scaffold in vivo. The level of osteocalcin was 25.28±5.71 ng/scaffold and that of Ca was 129.20±19.69 µg/scaffold. These values were significantly higher than those in sponges without dextran coating (p