Abstract: Various genes which control or affect heading time have been found in rice. Out of them, Se1 and E1 loci play important roles in determining heading time by controlling photosensitivity. An isogenic-line pair of late and early lines were developed from progenies of the F1 from Suweon 258 × 36U. A lateness gene tentatively designated as “Ex” was found to control the difference in heading time between the early and late lines mentioned above. The present study was conducted to examine the effect of Ex on yield and related traits. Indica-type variety Suweon 258 was crossed with 36U, which is an Ur1 (Undulate rachis-1) isogenic line of IR36. In the F2 population, comparatively early-heading, late-heading and intermediate-heading plants were segregated. Segregation similar to that by the three types of heading was observed in the F3 and later generations. A late-heading plant and an early-heading plant were selected in the F8 population from an intermediate-heading F7 plant, for developing L and E of the isogenic-line pair, respectively. Experiments for L and E were conducted by randomized block design with three replications. Transplanting was conducted on May 3 at a planting distance of 30 cm × 15 cm with two seedlings per hill to an experimental field of the Faculty of Agriculture, Kochi University. Chemical fertilizers containing N, P2O5 and K2O were applied at the nitrogen levels of 4 g/m2, 9 g/m2 and 18 g/m2 in total being denoted by "N4", "N9" and "N18", respectively. Yield, yield components and other traits were measured. Ex delayed 80%-heading by 17 or 18 days in L as compared with E. In total brown rice yield (g/m2), L was 635, 606 and 590, and E was 577, 548 and 501, respectively, at N18, N9 and N4, indicating that Ex increased this trait by 10% to 18%. Ex increased yield-1.5 mm sieve (g/m2) b 9% to 15% at the three fertilizer levels. Ex increased the spikelet number per panicle by 16% to 22%. As a result, the spikelet number per m2 was increased by 11% to 18% at the three fertilizer levels. Ex decreased 1000-grain weight (g) by 2 to 4%. L was not significantly different from E in ripened-grain percentage, fertilized-spikelet percentage and percentage of ripened grains to fertilized spikelets. Hence, it is inferred that Ex increased yield by increasing spikelet number per panicle. Hence, Ex could be utilized to develop high yielding varieties for warmer districts.
Abstract: Post growth annealing of solution grown ZnO
nanowire array is performed under controlled oxygen ambience. The
role of annealing over surface defects and their consequence on
dark/photo-conductivity and photosensitivity of nanowire array is
investigated. Surface defect properties are explored using various
measurement tools such as contact angle, photoluminescence, Raman
spectroscopy and XPS measurements. The contact angle of the NW
films reduces due to oxygen annealing and nanowire film surface
changes from hydrophobic (96°) to hydrophilic (16°). Raman and
XPS spectroscopy reveal that oxygen annealing improves the crystal
quality of the nanowire films. The defect band emission intensity
(relative to band edge emission, ID/IUV) reduces from 1.3 to 0.2 after
annealing at 600 °C at 10 SCCM flow of oxygen. An order
enhancement in dark conductivity is observed in O2 annealed
samples, while photoconductivity is found to be slightly reduced due
to lower concentration of surface related oxygen defects.