Abstract: Commercially available poly(acrylonitrile-co-vinyl acetate) P(AN-VA) or poly(acrylonitrile-co-methyl acrylate) P(AN-MA) are not satisfactory to meet the demand in flame and fire-resistance. In this work, vinylphosphonic acid is used during polymerization of acrylonitrile, vinyl acetate, methacrylic acid to produce fire-retardant polymers. These phosphorus containing polymers are successfully spun in the form of nanofibers. Properties such as water absorption of polymers are also determined and compared with commercial polymers.
Abstract: The effect of needle diameter on the morphological structure of electrospun n-Bi2O3/epoxy-PVA nanofibers has been investigated using three different types of needle diameters. The results were observed and investigated using two techniques of scanning electron microscope (SEM). The first technique is backscattered SEM while the second is secondary electron SEM. The results demonstrate that there is a correlation between the needle diameter and the morphology of electrospun nanofibers. As the internal needle diameter decreases, the average nanofiber diameter decreases and the fibers get thinner and smoother without agglomeration or beads formation. Moreover, with small needle diameter the nanofibrous porosity get larger compared with large needle diameter.
Abstract: Polysulfone (PSU) is a specialty engineering polymer
having various industrial applications. PSU is especially used in
waste water treatment membranes due to its good mechanical
properties, structural and chemical stability. But it is a hydrophobic
material and therefore its surface aim to pollute easily. In order to
resolve this problem and extend the properties of membrane, PSU
surface is rendered hydrophilic by addition of the sepiolite
nanofibers. Sepiolite is one of the natural clays, which is a hydrate
magnesium silicate fiber, also one of the well known layered clays of
the montmorillonites where has several unique channels and pores
within. It has also moisture durability, strength and low price.
Sepiolite channels give great capacity of absorption and good surface
properties. In this study, nanocomposites of commercial PSU and
Sepiolite were prepared by solvent mixing method. Different organic
solvents and their mixtures were used. Rheological characteristics of
PSU-Sepiolite solvent mixtures were analyzed, the solubility of
nanocomposite content in those mixtures were studied.
Abstract: A proton exchange membrane has been developed for
direct methanol fuel cell (DMFC). The nanofiber network composite
membranes were prepared by interconnected network of Nafion
(perfuorosulfonic acid) nanofibers that have been embedded in an
uncharged and inert polymer matrix, by electro-spinning. The
spinning solution of Nafion with a low concentration (1 wt%
compared to Nafion) of high molecular weight poly(ethylene oxide),
as a carrier polymer. The interconnected network of Nafion
nanofibers with average fiber diameter in the range of 160-700nm,
were used to make the membranes, with the nanofiber occupying up
to 85% of the membrane volume. The matrix polymer was
crosslinked with Norland Optical Adhesive 63 under UV. The
resulting membranes showed proton conductivity of 0.10 S/cm at
25°C and 80% RH; and methanol permeability of 3.6 x 10-6 cm2/s.
Abstract: Electrospinning is a broadly used technology to obtain
polymeric nanofibers ranging from several micrometers down to
several hundred nanometers for a wide range of applications. It offers
unique capabilities to produce nanofibers with controllable porous
structure. With smaller pores and higher surface area than regular
fibers, electrospun fibers have been successfully applied in various
fields, such as, nanocatalysis, tissue engineering scaffolds, protective
clothing, filtration, biomedical, pharmaceutical, optical electronics,
healthcare, biotechnology, defense and security, and environmental
engineering. In this study, polyurethane nanofibers were obtained
under different electrospinning parameters. Fiber morphology and
diameter distribution were investigated in order to understand them
as a function of process parameters.