Abstract: Bisphenol A (BPA) is an organic synthetic compound that has many applications in various industries and is known as persistent pollutant. The aim of this research was to evaluate the efficiency of bone ash and banana peel as adsorbents for BPA adsorption from aqueous solution by using Response Surface Methodology. The effects of some variables such as sorbent dose, detention time, solution pH, and BPA concentration on the sorption efficiency was examined. All analyses were carried out according to Standard Methods. The sample size was performed using Box-Benken design and also optimization of BPA removal was done using response surface methodology (RSM). The results showed that the BPA adsorption increases with increasing of contact time and BPA concentration. However, it decreases with higher pH. More adsorption efficiency of a banana peel is very smaller than a bone ash so that BPA removal for bone ash and banana peel is 62 and 28 percent, respectively. It is concluded that a bone ash has a good ability for the BPA adsorption.
Abstract: Most failures of soil have been attributed to poor shear strength. Consequently, the present paper investigated the suitability of cattle bone ash as a possible additive to improve the shear strength of soils. Four soil samples were collected and stabilized with prepared bone ash in proportions of 3%, 5%, 7%, 10%, 15% and 20% by dry weight. Chemical analyses of the bone ash; followed by classification, compaction, and triaxial shear tests of the treated soil samples were conducted. Results obtained showed that bone ash contained high proportion of calcium oxide and phosphate. Addition of bone ash to soil samples led to increase in soil shear strengths within the range of 22.40% to 105.18% over the strengths of the respective control tests. Conversely, all samples attained maximum shear strengths at 7% bone ash stabilization. The use of bone ash as an additive will therefore improve the shear strength of soils; however, using bone ash quantities in excess of 7% may not yield ample results.
Abstract: Heavy metals have bad effects on environment and
soils and it can uptake by natural HAP .natural Hap is an inexpensive
material that uptake large amounts of various heavy metals like Zn
(II) .Natural HAP (N-HAP), extracted from bovine cortical bone ash,
is a good choice for substitution of commercial HAP. Several
experiments were done to investigate the sorption capacity of Zn (II)
to N-HAP in various particles sizes, temperatures, initial
concentrations, pH and reaction times. In this study, the sorption of
Zinc ions from a Zn solution onto HAP particles with sizes of 1537.6
nm and 47.6 nm at three initial pH values of 4.50, 6.00 and 7.50 was
studied. The results showed that better performance was obtained
through a 47.6 nm particle size and higher pH values. The
experimental data were analyzed using Langmuir, Freundlich, and
Arrhenius equations for equilibrium, kinetic and thermodynamic
studies. The analysis showed a maximum adsorption capacity of NHAP
as being 1.562 mmol/g at a pH of 7.5 and small particle size.
Kinetically, the prepared N-HAP is a feasible sorbent that retains Zn
(II) ions through a favorable and spontaneous sorption process.