Abstract: Al2(HPO4)3 was easily prepared and used as a solid
acid in acetalization of carbonyl compounds at room temperature and
under solvent-free conditions. The protection was done in short
reaction times and in good to high isolated yields. The cheapness and
availability of this reagent with easy procedure and work-up make
this method attractive for the organic synthesis.
Abstract: This article presents summary on preparation and
characterization of zinc, copper, cadmium and cobalt chromite
nanocrystals, embedded in an amorphous silica matrix. The
ZnCr2O4/SiO2, CuCr2O4/SiO2, CdCr2O4/SiO2 and CoCr2O4/SiO2
nanocomposites were prepared by a conventional sol-gel method
under acid catalysis. Final heat treatment of the samples was carried
out at temperatures in the range of 900−1200 ◦C to adjust the
phase composition and the crystallite size, respectively. The resulting
samples were characterized by Powder X-ray diffraction (PXRD),
High Resolution Transmission Electron Microscopy (HRTEM),
Raman/FTIR spectroscopy and magnetic measurements. Formation
of the spinel phase was confirmed in all samples. The average size of
the nanocrystals was determined from the PXRD data and by direct
particle size observation on HRTEM; both results were correlated.
The mean particle size (reviewed by HRTEM) was in the range from
∼4 to 46 nm. The results showed that the sol-gel method can be
effectively used for preparation of the spinel chromite nanoparticles
embedded in the silica matrix and the particle size is driven by the
type of the cation A2+ in the spinel structure and the temperature
of the final heat treatment. Magnetic properties of the nanocrystals
were found to be just moderately modified in comparison to the bulk
phases.